A kind of anti-corrosion and anti-rust concrete and its application

A technology for concrete and concrete preservatives, which is applied in infrastructure engineering, sheet pile walls, protection devices, etc., can solve problems such as structural damage, affect the normal use of concrete structures, and lose structural durability, and achieve the effect of improving rust resistance.

Active Publication Date: 2022-02-25
深圳市利建新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The concrete foundation has been in such an environment with high chloride ions and sulfate ions for a long time, and the chloride ions will corrode the concrete, causing corrosion of the steel bars, causing early damage to the structure, losing the durability of the structure, and causing cracks, damage, and falling off of the concrete structure It seriously affects the normal use of concrete structures and reduces the actual service life of the project.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-corrosion and anti-rust concrete and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An anti-corrosion and anti-rust concrete, including the following raw material components in parts by weight: 300kg of P.O42.5 ordinary Portland cement, 680kg of medium sand, 980kg of gravel, 35kg of I-level wind separation fly ash, 50kg of S95 mineral powder, ZQ -3 8kg of waterproof pumping agent, 8kg of FSS-7A anti-sulfate preservative, 8kg of FS-7B high-efficiency rust inhibitor and 150kg of water, of which the sand rate is 41.0%, and the water-binder ratio is 0.41.

Embodiment 2

[0032] An anti-corrosion and anti-rust concrete, including the following raw material components in parts by weight: 300kg of P.O42.5 ordinary Portland cement, 680kg of medium sand, 980kg of gravel, 50kg of I-level wind separation fly ash, 35kg of S95 mineral powder, ZQ -3 8kg of waterproof pumping agent, 8kg of FSS-7A anti-sulfate preservative, 8kg of FS-7B high-efficiency rust inhibitor and 150kg of water, of which the sand rate is 41.0%, and the water-binder ratio is 0.41.

Embodiment 3

[0034] An anti-corrosion and anti-rust concrete, including the following raw material components in parts by weight: 300kg of P.O42.5 ordinary Portland cement, 680kg of medium sand, 980kg of gravel, 35kg of I-level winnowing fly ash, 35kg of S95 mineral powder, ZQ -3 8kg of waterproof pumping agent, 8kg of FSS-7A anti-sulfate preservative, 8kg of FS-7B high-efficiency rust inhibitor and 150kg of water, of which the sand rate is 41.0%, and the water-binder ratio is 0.41.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of concrete, in particular to a kind of anti-corrosion and anti-rust concrete, comprising the following components in parts by weight: 300-420 parts of cement, 680-730 parts of sand, 980-1200 parts of stones, and 35-50 parts of fly ash , 35-50 parts of mineral powder, 8-15 parts of pumping agent, 8-15 parts of concrete preservative, 8-15 parts of rust inhibitor and 150-200 parts of water; Anti-rust performance; the invention also provides the application of the anti-corrosion and anti-rust concrete in cast-in-place piles.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to an anti-corrosion and anti-rust concrete and its application. Background technique [0002] For marine buildings, sea sand buildings and buildings in saline-alkali areas, coastal areas or surrounding environments contain a large amount of chloride ions and sulfate ions, which are easy to cause corrosion effects on steel bars and concrete, reduce the alkalinity of concrete, and destroy the passivation film on the surface of steel bars , causing corrosion and expansion of steel bars, further leading to cracking and spalling of the concrete protective layer, and the continuous deterioration of the structural function and mechanical properties. For this reason, experts at home and abroad have proposed various measures to improve the anti-corrosion ability of concrete structures, among which adding anti-corrosion agents to concrete is an effective measure that is economical, practica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04E02D5/34E02D31/06C04B111/20
Inventor 王小杰
Owner 深圳市利建新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap