Aluminum alloy checkered plate in state of 4017-H2X and preparation method thereof

A 4017-H2X, aluminum alloy technology, applied in the field of metal manufacturing, can solve the problems of poor anodic oxidation effect, no 4017-H2X state aluminum alloy related products, and no 4017-H2X state aluminum alloy material preparation process, etc. The effect of fast heating speed, fine grain size and qualitative product performance

Active Publication Date: 2019-04-16
河南明晟新材料科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the corrosion resistance of the 5-series aluminum alloy plate is better, the anodic oxidation effect is slightly worse than that of the 6-series aluminum alloy
[0003] At present, there is no mature preparation process for aluminum alloy materials in the 4017-H2X state, and there are no related products for the 4017-H2X state aluminum alloy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy checkered plate in state of 4017-H2X and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation of a 4017-H22 state aluminum alloy checkered plate comprises the following steps:

[0038] Step 1: Ingredients:

[0039] Raw materials are formulated according to the following weight percentages: Si 0.6%, Fe≤0.7%, Cu 0.1%, Mn 0.6%, Mg0.1%, Zn≤0.2%, other individual impurities <0.05%, total impurities <0.15%, the rest The amount is Al.

[0040] Melting and casting:

[0041] Smelting the mixed metal at 700°C-750°C for 5-8 hours, standing and refining according to the routine, degassing, adding grain refiner, filtering, and measuring the hydrogen content in the launder ≤ 0.1mL / 100gAL; then at 690 The semi-continuous casting method is used for casting between ℃~730℃, the casting speed is 50~65mm / min, and the ingot size is determined according to the actual width of the product.

[0042] Step 2: Homogenizing heat treatment:

[0043] The ingot is subjected to a homogenization heat treatment at a temperature of 590°C to 610°C for a holding time of 8 to 12 ...

Embodiment 2

[0055] The preparation of a 4017-H24 state aluminum alloy checkered plate comprises the following steps:

[0056] Step 1: Ingredients:

[0057] Raw materials are formulated according to the following weight percentages: Si 1.6%, Fe≤0.7%, Cu 0.5%, Mn 1.2%, Mg0.5%, Zn≤0.2%, other individual impurities <0.05%, total impurities <0.15%, and the rest The amount is Al.

[0058] Melting and casting:

[0059] Melt the mixed metal at 700°C to 750°C for 5 to 8 hours, carry out static refining according to the routine, degas, add grain refiner, filter, and measure the hydrogen content in the launder to be ≤0.1mL / 100gAL; then at 690 The semi-continuous casting method is used for casting between ℃~730℃, the casting speed is 50~65mm / min, and the ingot size is determined according to the actual width of the product.

[0060] Step 2: Homogenizing heat treatment:

[0061] The ingot is subjected to a homogenization heat treatment at 590°C to 610°C for a holding time of 8 to 12 hours, and aft...

Embodiment 3

[0073] The preparation of a 4017-H22 state aluminum alloy checkered plate comprises the following steps:

[0074] Step 1: Ingredients:

[0075] Raw materials are formulated according to the following weight percentages: Si 1.1%, Fe0.7%, Cu 0.4%, Mn 0.9%, Mg0.4%, Zn 0.2%, other individual impurities <0.05%, total impurities <0.15%, and the balance for Al.

[0076] Melting and casting:

[0077] Melt the mixed metal at 700°C to 750°C for 5 to 8 hours, carry out static refining according to the routine, degas, add grain refiner, filter, and measure the hydrogen content in the launder to be ≤0.1mL / 100gAL; then at 690 The semi-continuous casting method is used for casting between ℃~730℃, the casting speed is 50~65mm / min, and the ingot size is determined according to the actual width of the product.

[0078] Step 2: Homogenizing heat treatment:

[0079] The ingot is subjected to a homogenization heat treatment at 590°C to 610°C for a holding time of 8 to 12 hours, and after it is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an aluminum alloy checkered plate in the state of 4017-H2X and a preparation method thereof. The checkered plate comprises the following raw materials in percentage by weight:0.6-1.6% of Si, less than or equal to 0.7% of Fe, 0.1-0.5% of Cu, 0.6-1.2% of Mn, 0.1-0.5% of Mg, less than or equal to 0.2% of Zn, less than 0.05% of other single impurities, less than 0.15% of total impurities and the balance of Al. The preparation method comprises the following steps of material preparing, smelting and casting; ingot soaking, machining and milling surface; hot rolling; cold rolling and cogging; cold rolling embossing; continuous annealing; and tension correction or crosscutting. The checkered plate in the state of 4017-H22 or 4017-H24 prepared by the preparation method hasno naked eye crack, no orange peel lines and fine surface after being bent at 90 degrees. The checkered plate prepared by the preparation method can be painted and is suitable for being used as building materials and manufacturing decorative parts.

Description

technical field [0001] The invention relates to the field of metal manufacturing, in particular to a 4017-H2X state aluminum alloy checkered plate and a manufacturing method thereof. Background technique [0002] Ordinary checkered plates are mostly processed with 1060, 3003, and 5052 aluminum alloys in series 1, 3, and 5 as the base, and rarely use 4-series aluminum alloys as the base. In comparison, the 1-series and 3-series aluminum alloy checkered plates have lower hardness and slightly poorer wear resistance, and are mostly used for rust prevention in ordinary environments and application requirements that are not strict. Although the corrosion resistance of the 5-series aluminum alloy plate is better, the anodic oxidation effect is slightly worse than that of the 6-series aluminum alloy. The 4-series tread plate has particularly good wear resistance and good anti-slip ability. It is usually used as building materials and manufacturing decorative parts, such as transpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C1/02C22C1/06C22C21/00C22F1/04C22F1/043
CPCC22C1/026C22C1/06C22C21/00C22C21/02C22F1/04C22F1/043
Inventor 宋喜波李克振李坤朋柴明科
Owner 河南明晟新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap