Welding wire for submerged arc welding of high-manganese low-temperature steel and welding method

A technology of submerged arc welding and welding method, applied in welding/welding/cutting items, welding medium, welding equipment, etc., can solve the problems of toxic manganese, difficult use, volatilization, etc., to improve low-temperature impact performance, reduce alloy cost, the effect of improving stability

Active Publication Date: 2019-04-16
NANJING IRON & STEEL CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These high-manganese welding consumables have the obvious advantage of low alloy cost, but due to the high-content manganese element is easy to form toxic manganese volatilization during the welding process, special welding equipment is required, and it is difficult to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A welding wire for submerged arc welding of high manganese and low temperature steel provided in this example, its chemical composition and mass percentage are as follows: C: 0.29%, Mn: 14.1%, Ni: 17%, Cr: 3.1%, P≤0.004 %, S≤0.002%, the balance is Fe and unavoidable impurities.

[0024] The welding method is as follows: the diameter of the welding wire used is 2.4mm, the submerged arc welding method is adopted, and the high-manganese low-temperature steel plate with a thickness of 21mm and a Mn content of 23.8% is welded. The groove of the high-manganese low-temperature steel plate is V-shaped, the groove angle on one side is 30°C, the flux is INCOFLUX9 (SMC), the welding current is 410A, the arc voltage is 27V, the welding speed is 34cm / min, and the welding heat input is 18kJ / cm.

[0025] Charpy Pendulum Impact Test (National Standard GB / T229--2007) Impact Absorption Energy KV of V-shaped Sample of Weld Metal Formed by Welding Wire 2 It is 69J, and the microstructur...

Embodiment 2

[0027]A welding wire for submerged arc welding of high manganese and low temperature steel provided in this example, its chemical composition and mass percentage are as follows: C: 0.2%, Mn: 15%, Ni: 16%, Cr: 5%, P≤0.004 %, S≤0.002%, the balance is Fe and unavoidable impurities.

[0028] The welding method is as follows: the diameter of the welding wire used is 4 mm, and the submerged arc welding method is used to weld high-manganese low-temperature steel plates with a thickness of 18 mm and a Mn content of 24% by mass. The groove of the high-manganese low-temperature steel plate is V-shaped, the groove angle on one side is 30°C, the flux is INCOFLUX9 (SMC), the welding current is 550A, the arc voltage is 30V, the welding speed is 51cm / min, and the welding heat input is 19kJ / cm.

[0029] Charpy Pendulum Impact Test (National Standard GB / T229--2007) Impact Absorption Energy KV of V-shaped Sample of Weld Metal Formed by Welding Wire 2 It is 46J, and the microstructure of the ...

Embodiment 3

[0031] A welding wire for submerged arc welding of high manganese and low temperature steel provided in this example, its chemical composition and mass percentage are as follows: C: 0.4%, Mn: 12%, Ni: 20%, Cr: 2%, P≤0.004 %, S≤0.002%, the balance is Fe and unavoidable impurities.

[0032] The welding method is as follows: the diameter of the welding wire used is 2.4mm, and the submerged arc welding method is used to weld high-manganese low-temperature steel plates with a thickness of 25mm and a Mn content of 22.5%. The groove of the high-manganese low-temperature steel plate is V-shaped, the angle of the groove on one side is 30°C, the flux is INCOFLUX9 (SMC), the welding current is 430A, the arc voltage is 30V, the welding speed is 37cm / min, and the welding heat input is 21kJ / cm .

[0033] Charpy pendulum impact test (national standard GB / T229--2007) impact absorption energy KV of V-shaped sample formed by welding wire -196°C 2 It is 77J, the microstructure of the weld meta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Impact absorption energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding wire for submerged arc welding of high-manganese low-temperature steel and a welding method, and relates to the technical field of welding. The welding wire is prepared from the following chemical components according to mass percent: 0.2% to 0.4% of C, 12% to 15% of Mn, 16% to 20% of Ni, 2% to 5% of Cr, less than or equal to 0.004% of P, less than or equal to 0.002% of S and the balance of Fe and inevitable impurities. The manganese-nickel composition design adopted by the welding wire has good compatibility with high-manganese low-temperature steel base metal and is suitable for a conventional welding wire manufacturing method, the composition is simple, weld metal formed by the welding wire has good impact toughness at low temperature of -196 DEG C, andthe welding requirement of the high-manganese low-temperature steel for constructing equipment like a liquefied natural gas storage tank is preferably met.

Description

technical field [0001] The invention relates to the field of welding technology, in particular to a welding wire for submerged arc welding of high manganese and low temperature steel and a welding method. Background technique [0002] The storage and transportation of liquefied natural gas (boiling point -162°C), liquid oxygen (boiling point -183°C) and liquid nitrogen (boiling point -196°C) require structural materials that serve under low temperature conditions. The main mechanical property requirements are low temperature Has sufficient impact toughness. As commonly used low-temperature steel, materials such as 9% Ni steel and Cr-Ni austenitic stainless steel need to add a large amount of expensive nickel element, so the cost is high. In recent years, high-manganese low-temperature steel has received widespread attention as a cutting-edge new low-temperature material, and the development of its special matching welding consumables is also extremely important. [0003] T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/30B23K9/18B23K103/04
CPCB23K9/186B23K35/0261B23K35/3066B23K35/30C22C38/58C22C38/44C22C38/50C22C38/48C22C38/001
Inventor 孙超李东晖尹雨群
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com