Nitriding equipment and process based on high valve stability

A high stability, valve technology, applied in the direction of metal material coating process, coating, solid diffusion coating, etc., can solve the problems such as difficult to remove, affect the cleanliness of valve finished products, poor valve nitriding effect, etc., to improve The effect of stability

Active Publication Date: 2020-07-28
重庆恒蕾工贸有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Nitriding treatment refers to the chemical heat treatment process that makes nitrogen atoms penetrate into the surface layer of the workpiece. When nitriding the valve, the valve is usually placed in the nitriding equipment to contact with nitrogen gas, so that nitrogen atoms can penetrate into the surface layer of the valve. After nitriding The valve has a certain stability in terms of wear resistance, fatigue resistance, corrosion resistance and high temperature resistance, but it is found that the nitriding effect of the valve is not good during the inspection process, and the stability performance has not reached the best level
Moreover, after the valve is nitrided, a large amount of black scale will adhere to the surface of the valve, which is difficult to remove and directly affects the cleanliness of the finished valve.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitriding equipment and process based on high valve stability
  • Nitriding equipment and process based on high valve stability
  • Nitriding equipment and process based on high valve stability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The following is further described in detail through specific implementation methods:

[0025] The reference signs in the drawings of the description include: the first conveyor belt 1, the gas storage tank 2, the drying furnace 3, the reactor 4, the annular cavity 5, the hole 6, the blocking plate 7, the sealing plate 8, the baffle plate 9, the pressing plate 10. Valve stem 11, support plate 12, blocking block 13, through hole 14, through groove 15, collection box 16, blanking hole 17, second conveyor belt 18, material storage tank 19, hot gas pipe 20, support block 21, Grinding sheet 22, circular cavity 23, rotating rod 24, fan blade 25, jet hole 26, air valve 27, air pipe 28.

[0026] The embodiment is basically as attached Figure 1-3 Shown: as figure 1 The shown nitriding equipment based on the high stability of valve 27 includes a first conveyor belt 1, a grinding mechanism, and a gas storage tank 2, a drying furnace 3 and a reactor 4 fixedly installed on the fr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of valve nitridation, in particular to a nitridation device and process based on valve high stability. The nitridation device based on the valve high stability comprises a first conveyor belt, a polishing mechanism, a machine frame, a gas storage tank, a drying stove and a reactor, wherein the gas storage tank, the drying stove and the reactor are sequentially arranged on the machine frame. The nitridation process based on the valve high stability includes the following steps that firstly, a valve is sent into the drying stove through the first conveyor beltto be baked, and nitrogen is heated at the same time; secondly, when the valve is baked to 290 DEG C to 310 DEG C and the nitrogen is heated to 390 DEG C to 410 DEG C, the valve and the nitrogen are sent into the reactor to be subjected to nitridation treatment; thirdly, after nitridation treatment is conducted for 35 min to 45 min, the valve is sent onto a second conveyor belt; and fourthly, thevalve is polished through the polishing mechanism. When the technical scheme is adopted, dark dirt on the surface of the valve can be removed while the stability of the valve is improved.

Description

technical field [0001] The invention relates to the field of valve nitriding, in particular to nitriding equipment based on high valve stability and a process thereof. Background technique [0002] The function of the valve is to input air into the engine and discharge the exhaust gas after combustion. The valve includes the valve stem and the valve head; due to the high temperature in the engine, the valve must have certain wear resistance, fatigue resistance and corrosion resistance. performance and high temperature resistance. [0003] Nitriding treatment refers to the chemical heat treatment process that makes nitrogen atoms penetrate into the surface layer of the workpiece. When nitriding the valve, the valve is usually placed in the nitriding equipment to contact with nitrogen gas, so that nitrogen atoms can penetrate into the surface layer of the valve. After nitriding The valve has a certain stability in terms of wear resistance, fatigue resistance, corrosion resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C8/24
CPCC23C8/24
Inventor 向勇
Owner 重庆恒蕾工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products