Water-based coating for trash can and preparation method thereof

A water-based paint and trash can technology, applied in the field of paint, can solve the problems of trash trash can odor, breeding mosquitoes, mildew, etc., and achieve the effect of eliminating odor, eliminating odor and mildew, and improving the density.

Inactive Publication Date: 2019-03-22
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Trash cans are containers of dirt and dirt in people's lives. Most of the trash cans have problems of odor, mildew, and breeding of mosquitoes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based coating for trash can and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]A water-based paint for a trash can, which comprises the following raw material components in parts by mass: 30 parts of high-temperature silicone resin, 0.01 part of pyrethrin, 0.5 part of hydrotalcite, 0.1 part of nano-silver, 0.1 part of nano-zinc oxide, 1 part of flame retardant, 2 parts of shell powder, 0.1 part of PH regulator, 2 parts of film-forming aid, 0.3 part of dispersant, 0.3 part of substrate wetting agent, 5 parts of deionized water, and 0.5 part of thickener.

[0037] In this example, the high-temperature silicone resin is 767 high-temperature silicone resin from Qingdao Jinwanli Fine Chemical Co., Ltd.; the pyrethrins are from Hangzhou Guoyou Agricultural Production Materials Co., Ltd.; Flame-retardant hydrotalcite from the plastic material factory; nano-silver adopts nano-silver antibacterial agent 300-AG-2000 from Guangzhou Bofeng Chemical Technology Co., Ltd.; nano-zinc oxide adopts TZP-50 nano-zinc oxide produced by Nanjing Tianxing New Material Co.,...

Embodiment 2

[0042] A water-based paint for a trash can, which comprises the following raw material components in parts by mass: 45 parts of high-temperature silicone resin, 0.1 part of pyrethrin, 0.1 part of antiseptic and bactericide, 1.2 parts of hydrotalcite, 0.3 part of nano-silver, 0.3 parts of nano-zinc oxide, 5 parts of flame retardant, 5 parts of pigment, 4 parts of shell powder, 0.15 parts of pH regulator, 4 parts of film-forming aid, 0.4 part of dispersant, 0.4 part of substrate wetting agent, deionized water 8 parts, thickener 0.8 parts.

[0043] In this embodiment, the antiseptic and bactericide adopts the isothiazolone of Qingdao Xingguo Paint Co., Ltd.; the PH regulator adopts the multifunctional additive AMP-95 of American Dow Chemical; the dispersant adopts the water-based paint and water-based pigment of BYK Company The wetting and dispersing additive BYK194 is used for the concentrated slurry; the substrate wetting agent is AFCONA-3031 from Efcona AFCONA Company. The se...

Embodiment 3

[0048] A water-based coating for a trash can, which comprises the following raw material components in parts by mass: 60 parts of high-temperature silicone resin, 0.2 part of pyrethrin, 0.2 part of antiseptic and bactericide, 2 parts of hydrotalcite, 0.5 part of nano-silver, 0.5 parts of nano-zinc oxide, 8 parts of flame retardant, 8 parts of pigment, 5 parts of shell powder, 0.2 parts of pH regulator, 5 parts of film-forming aid, 0.5 part of dispersant, 0.5 part of substrate wetting agent, deionized water 10 parts, thickener 1 part.

[0049] In this embodiment, the antiseptic and bactericide adopts the isothiazolone of Qingdao Xingguo Coatings Co., Ltd.; the pH regulator adopts the dimethylethanolamine of German BASF company and the multifunctional additive AMP-95 of U.S. Dow Chemical Industry, two types of The PH regulator is mixed with a ratio of 1:1; the dispersant is BYK’s water-based paint and water-based pigment concentrate, wetting and dispersing additives BYK190 and B...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based coating for a trash can and a preparation method thereof. The water-based coating for the trash can comprises the following components in parts by mass: 30-60 parts of high temperature silicone resin, 0.01-0.2 part of pyrethrin, 0-0.2 part of antiseptic and sterilizing agents, 0.5-2 parts of hydrotalcite, 0.1-0.5 part of nanosilver, 0.1-0.5 part of nano zinc oxide, 1-8 parts of a flame retardant, 2-5 parts of shell powder, 0.1-0.2 part of a PH regulator, 2-5 parts of a coalescing agent, 0.3-0.5 part of a dispersing agent, 0.3-0.5 part of a substrate wettingagent, 5-10 parts of deionized water, and 0.5-1 part of a thickener. The water-based coating prepared by the method has good water resistance, flame resistance and antibacterial property, has properfilm hardness, and has the characteristics of preventing insects, preventing mould, removing peculiar smell, and sterilizing.

Description

technical field [0001] The application belongs to the technical field of coatings, and in particular relates to a water-based coating for trash cans and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, more and more garbage is produced by human beings. The trash can is a container for storing dirt and dirt in people's lives, and there are problems of peculiar smell, mildew, and breeding of mosquitoes in most trash cans. In addition, most of the trash cans are made of metal or plastic, and some trash cans are made of wood and pulp. There are flammable characteristics for trash cans made of flammable materials such as plastic, wood, and pulp. How to solve the problems of peculiar smell, mildew, breeding of mosquitoes and flammability in garbage bins has become a direction that industry technicians need to study hard. Contents of the invention [0003] In order to overcome the problems in the related art at leas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/16C09D5/14C09D5/18
CPCC09D183/04C09D5/14C09D5/16C09D5/18C08L2201/08C08L2201/02C08K2201/011C08K2201/014C08K2003/2296C08K2003/0806C08K13/02C08K3/26C08K3/08C08K3/22C08K5/47
Inventor 湛冬冬祁艳东王科端胡中源董立志
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com