Environment-friendly heat-insulating building energy-saving heat-preserving material
A technology for building energy-saving and thermal insulation materials, applied in epoxy resin coatings, reflective/signal coatings, coatings, etc., can solve problems such as unsatisfactory coatings and poor thermal insulation performance, and achieve environmental protection, good thermal insulation effects, less toxic effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] The raw materials of the following components and the mass percentages of each component are selected to produce coatings:
[0012] Elastic acrylic modified emulsion (water-based) 35wt%, epoxy resin (water-based) 6wt%, n-butanol 4wt%, hollow glass microspheres 11wt%, functional filler (asbestos powder 4 wt%, alumina 6 wt%), kaolin 18wt%, talcum powder 1wt%, dispersant 0.6wt%, wetting agent 0.4wt%, defoamer 0.5%, antibacterial agent 0.3wt%, antifungal agent 0.3wt%, leveling agent 2wt%, thickener 1wt% %, water 10wt%.
[0013] During the production process, when the hollow glass microspheres are added, the stirring speed of the motor is set to 800 rpm until the stirring process is completed. Paint the paint produced according to the above raw materials and methods on the wall, and the heat insulation effect is: when the outdoor temperature is 38-42°C, the indoor temperature is 26-31°C; the heat preservation effect is: the outdoor temperature is about 0°C At that time, th...
Embodiment 2
[0015] The raw materials of the following components and the mass percentages of each component are selected to produce coatings:
[0016] Elastic acrylic modified emulsion (water-based) 30wt%, epoxy resin (water-based) 7wt%, n-butanol 5wt%, hollow glass microspheres 15wt%, functional filler (asbestos powder 5 wt%, alumina 7 wt%), kaolin 15wt%, talcum powder 1.2wt%, dispersant 0.7wt%, wetting agent 0.5wt%, defoamer 0.6%, antibacterial agent 0.3wt%, antifungal agent 0.4wt%, leveling agent 2.5wt%, thickener 1.2wt%, water 8.6wt%.
[0017] During the production process, when the hollow glass microspheres are added, the stirring speed of the motor is set to 800 rpm until the stirring process is completed. Paint the paint produced by the above raw materials on the wall, and its heat insulation effect is: when the outdoor temperature is 38-42°C, the indoor temperature is 28-33°C; the heat preservation effect is: when the outdoor temperature is about 0°C, The temperature in the room...
Embodiment 3
[0019] The raw materials of the following components and the mass percentages of each component are selected to produce coatings:
[0020] Elastic acrylic modified emulsion (water-based) 38wt%, epoxy resin (water-based) 5wt%, n-butanol 3wt%, hollow glass microspheres 10wt%, functional filler (asbestos powder 3 wt%, alumina 5 wt%), kaolin 20wt%, talc powder 0.8wt%, dispersant 0.5wt%, wetting agent 0.3wt%, defoamer 0.4%, antibacterial agent 0.1wt%, antifungal agent 0.2wt%, leveling agent 1.5wt%, thickener 0.8wt%, water 11.4wt%.
[0021] During the production process, when the hollow glass microspheres are added, the stirring speed of the motor is set to 800 rpm until the stirring process is completed. Paint the paint produced by the above raw materials on the wall, and its heat insulation effect is: when the outdoor temperature is 38-42°C, the indoor temperature is 29-34°C; the heat preservation effect is: when the outdoor temperature is about 0°C, The temperature in the room ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com