Method for recovering black carbon powder to be modified into colored carbon powder

A technology for black toner and toner, which is applied in the field of recycling black toner and improving it into color toner, can solve the problems of toner being easily affected by the environment, cannot be used directly, and damage to the respiratory system, and achieves high uniformity, high toner The effect of quality improvement and good electrical conductivity

Inactive Publication Date: 2019-03-01
北海市天硌打印耗材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to improper installation, transportation or storage of toner cartridges and toner cartridges, the residual toner is easily affected by the environment, with moisture, impurities, etc., and cannot be used directly. It is a great waste to discard this part of toner. Therefore, How to reproduce the recovered toner so that it can be used is a difficult problem currently being explored
[0003] At the same time, those skilled in the art know that when the printer works for a long time, if the environment where the printer is located is not ventilated in time, there will be a certain smell when printing, which is harmful to the human body, or there is more toner in the air. It will cause damage to the user's respiratory system, therefore, how to remind the user to ventilate the environment where the printer is located is an urgent matter to be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The invention provides a method for reclaiming black carbon powder and improving it into colored carbon powder, comprising the steps of:

[0053] Step 1, taking the coloring agent, external additives and modifying agent and performing ultrafine pulverization treatment respectively, so that the particle diameters of the coloring agent and modifying agent are all below 5 microns, wherein, in parts by weight, the modifying agent Including 5 parts of chromium salicylate complex, 5 parts of polyethylene wax, 5 parts of acicular conductive titanium dioxide, 5 parts of silicon dioxide, 3 parts of calcium chloride, 5 parts of fragrance indicator and 1 part of polydimethylsiloxane The method for obtaining the aroma indicator is as follows: first soak the tea leaves in cold water for 1 min, then remove the tea leaves and soak the tea leaves in water at a temperature of 80°C, and then add ethylene glycol Alcohol, and kept at a temperature of 90°C for 20 minutes under airtight cond...

Embodiment 2

[0061] The invention provides a method for reclaiming black carbon powder and improving it into colored carbon powder, comprising the steps of:

[0062] Step 1, taking the coloring agent, external additives and modifying agent and performing ultrafine pulverization treatment respectively, so that the particle diameters of the coloring agent and modifying agent are all below 5 microns, wherein, in parts by weight, the modifying agent Including 15 parts of chromium salicylate complex, 15 parts of polyethylene wax, 15 parts of acicular conductive titanium dioxide, 15 parts of silicon dioxide, 5 parts of calcium chloride, 5-15 parts of fragrance indicator and polydimethylsiloxane 2 parts of alkanes, the aroma indicator comes from tea leaves. The method for obtaining the aroma indicator is: first soak the tea leaves in cold water for 2 minutes, then remove the tea leaves and soak the tea leaves in water with a temperature of 90°C, and then add ethylene glycol, and kept at a tempera...

Embodiment 3

[0070] The invention provides a method for reclaiming black carbon powder and improving it into colored carbon powder, comprising the steps of:

[0071]Step 1, taking the coloring agent, external additives and modifying agent and performing ultrafine pulverization treatment respectively, so that the particle diameters of the coloring agent and modifying agent are all below 5 microns, wherein, in parts by weight, the modifying agent Including 10 parts of chromium salicylate complex, 10 parts of polyethylene wax, 10 parts of acicular conductive titanium dioxide, 10 parts of silicon dioxide, 4 parts of calcium chloride, 4 parts of fragrance indicator 5-15 parts and polydimethyl 1.5 parts of siloxane, the aroma indicator comes from tea leaves. The method for obtaining the aroma indicator is: first soak the tea leaves in cold water for 1 min, then remove the tea leaves and soak the tea leaves in water at a temperature of 85°C, Then add ethylene glycol and keep it at a temperature o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for recovering black carbon powder to be modified into colored carbon powder. The method comprises the following steps: step one, a coloring agent, an external additive and a modifier are taken to be subjected to ultramicro-pulverization treatment; step two, impurities in the black carbon powder are filtered and removed, the black carbon powder and the coloring agent are dissolved in water, and first-time ultrasound treatment is conducted; step three, the modifier is added, and second-time ultrasound treatment is conducted; step four, the carbon powder is dried; step five, the modified carbon powder is extruded; and step six, the modified carbon powder is vibrated by ultrasonic vibrating equipment and then also subjected to ultramicro-pulverization, carbonpowder with the particle size being 5 microns or below is obtained, the external additive is added, and thus the colored carbon powder is obtained, wherein the external additive is any one or more offerroferric oxide, nickel powder, iron powder and calcium iron oxide. According to the colored carbon powder, printing pages are all normal during printing, dirty edges are avoided, printing is smooth, inkjet is uniform, pattern colors are consistent, and the damage influence on a printer is avoided.

Description

technical field [0001] The invention belongs to the technical field of printer consumables, and relates to a method for recycling black carbon powder and improving it into colored carbon powder. Background technique [0002] Printer (Printer) is one of the output devices of computer, with the quickening of life and the widespread use of electronic products. Printers are becoming an essential item in consumers' work and life. With the use of printers, the demand for printing consumables is also increasing. Most of the toner is composed of resin and carbon black, charging agent, magnetic powder and so on. The toner is melted into the paper fiber by high temperature, so that the output content can be displayed. Toner is one of the important consumables. In the recycling of printer consumables, in order to protect the environment and avoid material waste, toner must be classified according to color and category. However, due to improper installation, transportation or stora...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G03G21/10
CPCG03G21/10
Inventor 王和平
Owner 北海市天硌打印耗材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap