Fireproof coating and preparation method thereof

A technology for fire-resistant coatings and raw materials, applied in the field of coatings, can solve the problems of low fire resistance and shortened service life, and achieve the effects of reducing temperature, good compatibility, and good fire-retardant and flame-retardant properties.

Inactive Publication Date: 2019-02-19
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the fireproof performance of the fireproof coatings on the market is not high, which leads to the reduction of its service life, and it is difficult to meet the needs of the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof coating and preparation method thereof
  • Fireproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of fireproof coating, its raw material comprises by weight: 33 parts of fluorocarbon resin, 16 parts of vinyl acetate resin, 6 parts of aluminum oxide powder, 9.5 parts of ammonium polyphosphate, 3 parts of iron silicon nitride powder, 17 parts of expanded graphite, fiber 1.2 parts of plain ether, 9 parts of linalool, 5.5 parts of film-forming agent, 6.9 parts of talcum powder, 3.3 parts of curing agent, and 2.5 parts of defoamer.

[0018] The preparation method of described fireproof coating, described method comprises the steps:

[0019] S1. Take ferrosilicon nitride powder and add deionized water, ultrasonically disperse to obtain a ferrosilicon nitride dispersion; add expanded graphite to the ferrosilicon nitride dispersion, mechanically stir, filter, and dry to obtain modified expanded graphite;

[0020] S2. Put fluorocarbon resin, vinyl acetate resin, alumina powder, ammonium polyphosphate, cellulose ether and linalool into the mixer in turn, stir once, the...

Embodiment 2

[0022] A kind of fireproof coating, its raw material comprises by weight: 48 parts of fluorocarbon resin, 11 parts of vinyl acetate resin, 12 parts of aluminum oxide powder, 5.5 parts of ammonium polyphosphate, 6 parts of ferrosilicon nitride powder, 9 parts of expanded graphite, fiber 5.6 parts of plain ether, 6.8 parts of linalool, 12 parts of film-forming agent, 2.3 parts of talcum powder, 5.5 parts of curing agent, and 0.5 parts of defoamer;

[0023] Wherein, the expanded graphite is composed of expanded graphite with a small particle size and expanded graphite with a large particle size in a mass ratio of 1.4:3.7.

[0024] The preparation method of described fireproof coating, described method comprises the steps:

[0025] S1. Take ferrosilicon nitride powder and add deionized water, ultrasonically disperse to obtain a ferrosilicon nitride dispersion; add expanded graphite to the ferrosilicon nitride dispersion, mechanically stir, filter, and dry to obtain modified expand...

Embodiment 3

[0028] A kind of fireproof coating, its raw material comprises by weight: 40 parts of fluorocarbon resin, 13 parts of vinyl acetate resin, 9 parts of aluminum oxide powder, 7 parts of ammonium polyphosphate, 4.5 parts of ferrosilicon nitride powder, 12 parts of expanded graphite, fiber 3 parts of plain ether, 8 parts of linalool, 9 parts of film-forming agent, 4 parts of talcum powder, 4.5 parts of curing agent, 1.5 parts of defoamer;

[0029] Wherein, the expanded graphite is composed of small particle size expanded graphite and large particle size expanded graphite according to the mass ratio of 1.5:3.5;

[0030] The expanded graphite with small particle size is 240 mesh; the expanded graphite with large particle size is 70 mesh.

[0031] The preparation method of described fireproof coating, described method comprises the steps:

[0032] S1. Take ferrosilicon nitride powder and add deionized water, ultrasonically disperse to obtain a ferrosilicon nitride dispersion; add ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of coatings, in particular to a fireproof coating. The fireproof coating comprises the following raw materials in parts by weight: 33-48 parts of fluorocarbon resin, 11-16 parts of vinyl acetate resin, 6-12 parts of alumina powder, 5.5-9.5 parts of ammonium polyphosphate, 3-6 parts of silicon nitride iron powder, 9-17 parts of expanded graphite, 1.2-5.6parts of cellulose ether, 6.8-9 parts of linalool, 5.5-12 parts of a film forming agent, 2.3-6.9 parts of talcum powder, 3.3-5.5 parts of a curing agent and 0.5-2.5 parts of a defoaming agent. The invention further provides a preparation method of the fireproof coating. The fireproof coating has excellent fireproof performance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a fireproof coating and a preparation method thereof. Background technique [0002] Fire retardant coating is to brush the paint on the surface of those flammable materials, which can improve the fire resistance of the material, slow down the speed of flame spread, or prevent burning within a certain period of time. This type of coating is called fire retardant coating, or flame retardant coating. At present, the fireproof performance of fireproof coatings on the market is not high, resulting in reduced service life, and it is difficult to meet the needs of the market. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a fireproof coating and a preparation method thereof. The invention has excellent fireproof performance. [0004] A kind of fireproof coating proposed by the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D131/04C09D5/18
CPCC08K2003/2227C08K2003/323C08L2201/02C08L2205/03C09D5/18C09D127/12C08L31/04C08L1/26C08K3/22C08K3/32C08K3/34C08K7/24C08K13/04
Inventor 李子荣王和山王厚国王和东殷东楼殷芳荣曹文强张万霞张萍
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap