3D-effect laser paste pigment and preparation method thereof

A technology of 3D effect and manufacturing method, which is applied in the direction of pigment slurry, ink, household utensils, etc., can solve the problems of application limitation, high production cost, frequent replacement of nickel plates, etc., and achieve enhanced application adaptability, improved service life, Clear effect of laser information

Inactive Publication Date: 2019-01-25
深圳市崯彩特殊金属颜料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the ink formulated with laser aluminum paste can only be used on the surface of smooth and transparent materials, and cannot be used on non-transparent materials, because only the transparent side can see the side that is arranged in parallel
In addition, because aluminum is not resistant to water and corrosion, laser aluminum paste cannot be used in water-based systems, and the acid value of ink resin is also very strict, which greatly limits the application occasions.
In addition, the disadvantage of the preparation method of the laser aluminum paste is that it is first coated with aluminum, and then laser molded on the aluminum film. Due to the hardness of the metal aluminum film, the molded nickel plate is greatly worn, and frequent production is required. Replace nickel plate, high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The 3D laser paste pigment has a gray solid paste appearance and is composed of alloy nano flake particles, solvents and additives, and its weight percentage composition is:

[0041] Alloy nanosheet 25% solvent 74.5% additive 0.5%.

[0042] In this embodiment, the alloy nanosheet particles have a thickness of 10 nm and a particle size (d50) of 6-7 μm; the alloy nanosheets are made of alloy sputtering targets in the following weight percentages:

[0043] Iron 68.9%, chromium 16.3%, nickel 11.5%, manganese 1.2%, molybdenum 2.1%.

[0044] In this embodiment, the solvent is propylene glycol methyl ether acetate with a purity greater than 99.5%; the auxiliary agent is an anti-sedimentation agent.

[0045]The manufacturing method of the 3D effect laser paste pigment comprises:

[0046] A transparent resin layer with a thickness of 2 μm was coated on a PET film with a thickness of 16 μm on a coating machine.

[0047] The resin layer on the PET film is in contact with the gl...

Embodiment 2

[0052] The 3D laser paste pigment has a gray solid paste appearance and is composed of alloy nano flake particles, solvents and additives, and its weight percentage composition is:

[0053] Alloy nanosheet 20% solvent 79.5% additive 0.5%.

[0054] In this embodiment, the alloy nanosheet particles have a thickness of 20 nm and a particle size (d50) of 9 to 10 μm; the alloy nanosheets are made of alloy sputtering targets in the following weight percentages:

[0055] Iron 79.0%, chromium 18.0%, nickel 2.1%, manganese 0.9%.

[0056] In this embodiment, the solvent is propylene glycol methyl ether with a purity greater than 99.5%; the auxiliary agent is an anti-sedimentation agent.

[0057] The manufacturing method of this 3D effect laser paste pigment comprises:

[0058] (1) Coat a PET film with a thickness of 12 μm on a coating machine with a transparent resin layer with a thickness of 2 μm;

[0059] ⑵Contact the resin layer on the PET film with the optical column laser moldin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to laser paste pigment with a 3D-effect and a preparation method thereof. The pigment is prepared from 15-35% of an alloy material, 65-85% of a dispersing agent, and 0-1.5% of anassistant. The preparation method comprises the following steps: (1) coating a resin layer with 1.5-2 mum of a thickness on a plastic film base material, preparing a laser information layer on resinby using a laser film pressure technology, and enabling the resin layer to form optical refraction points of different heights and sizes to obtain an information layer with a laser dream color effect;(2) enabling a multi-element alloy material to be deposited on the surface of the laser information layer by using a continuous winding magnetron sputtering method so as to form an alloy film with amagnetic conductance function in a nano thickness; (3) dissolving the resin by using a solvent, and enabling the alloy film to be separated from the base material; and (4) smashing and filtering mixedliquor prepared from the solvent, the resin and the alloy material, adding the assistant, and adjusting solid content, to obtain 3D-effect laser paste prepared from the solvent, the assistant and nano sheet-like alloy particles.

Description

technical field [0001] The invention relates to the technical field of ink, in particular to a 3D effect laser paste pigment and a manufacturing method thereof. Background technique [0002] Laser paste is a high-grade decorative and anti-counterfeit pigment that can produce different colors and laser colorful effects. It is a one-dimensional nano-sheet made of aluminum by using PVD technology, laser film pressure technology and other physical and chemical processes. After the particle slurry is printed with the laser ink prepared by it, the sheet-like particles are arranged on the printing substrate in a plane, relying on the special nanostructure on the surface of the particles to produce colorful discoloration effects through the refraction and reflection of light. [0003] CN201210105500.2 discloses a preparation method of laser aluminum paste. Its purpose is to provide a kind of plastic film as raw material, through vacuum aluminum plating, laser molding to produce lase...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/50C09D17/00
CPCC09D11/50C09D17/002C09D17/006
Inventor 瞿晓岳雷庆昌瞿祥慧
Owner 深圳市崯彩特殊金属颜料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com