Method for extracting coconut fiber

A technology of coconut husk fiber and extraction method, applied in the field of extraction of coconut husk fiber, can solve problems such as unevenness, thick fiber, limited use, etc., and achieve the effects of uniform length, thickness of fiber, and reduction of residual fat rate.

Active Publication Date: 2019-01-08
安徽九天印务有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional process of extracting and processing coconut husk fibers makes the fibers thick, heavy, and uneven, resulting in very limited end uses. A large number of coconut husks are directly treated as garbage every year.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The extraction method of coir fiber described in the present embodiment may further comprise the steps:

[0027] (1) Coconut shell is broken, obtain coconut shell fragment, the length of coconut shell fragment is 5cm, set aside;

[0028] (2) Add deionized water and lipase in the tank, the amount of lipase added is 0.6% of the quality of deionized water, after mixing evenly, heat to 45°C to keep the constant temperature, put the coconut shell fragments into the tank and soak for 2 hours post filter;

[0029] (3) adding concentration is 0.5% sodium hydroxide solution in cooking tank, puts into the coconut shell after step (2) filtration, heats and pressurizes, and heating temperature is controlled between 105 ℃, and pressurized pressure is controlled at 14.7 MPa, cook for 1 hour, take out and rinse with water for 10 minutes after cooking;

[0030] (4) the coconut husk after step (3) is rinsed is analyzed into thick fibers with a silk forming machine, and then rinsed wit...

Embodiment 2

[0034] The extraction method of coir fiber described in the present embodiment may further comprise the steps:

[0035] (1) Coconut shell is broken, obtain coconut shell fragment, the length of coconut shell fragment is 6m, for subsequent use;

[0036] (2) Add deionized water and lipase in the tank, the amount of lipase added is 0.7% of the quality of deionized water, after mixing evenly, heat to 45°C to keep a constant temperature, put the coconut shell fragments into the tank and soak for 2.5 filter after h;

[0037] (3) adding concentration is 0.7% sodium hydroxide solution in cooking pot, puts into the coconut shell after step (2) filtration, carries out heating and pressurization, and heating temperature is controlled between 112 ℃, and pressurization pressure is controlled at 16.8 MPa, cook for 1.2h, take out after cooking and rinse with water for 13min;

[0038] (4) the coconut husk after step (3) is rinsed is analyzed into thick fibers with a silk forming machine, an...

Embodiment 3

[0042] The extraction method of coir fiber described in the present embodiment may further comprise the steps:

[0043] (1) Coconut shell is broken, obtain coconut shell fragment, the length of coconut shell fragment is 7cm, set aside;

[0044] (2) Add deionized water and lipase in the tank, the amount of lipase added is 0.8% of the quality of deionized water, after mixing evenly, heat to 45°C to keep the constant temperature, put the coconut shell fragments into the tank and soak for 3 hours post filter;

[0045] (3) adding concentration is 1% sodium hydroxide solution in cooking tank, puts into the coconut shell after step (2) filtration, carries out heating and pressurization, and heating temperature is controlled between 120 ℃, and pressurization pressure is controlled at 18.3 MPa, cook for 1.5h, take out after cooking and rinse with water for 15min;

[0046] (4) the coconut husk after step (3) is rinsed is analyzed into thick fibers with a wire forming machine, and then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for extracting coconut fiber. The method comprises the following steps: crushing coconut shell; adding deionized water and lipase into a cylinder, conducting uniform mixing, heating the mixture to 45 DEG C, and soaking the coconut shell into a cylinder for 2-3 h after soaking; adding sodium hydroxide solution in a cooking tank, putting the filtered coconut shell into the cooking tank, heating and pressurizing the mixture, cooking the mixture for 1-1.5 h, taking out the cooked coconut shell, and rinsing off the cooked coconut shell with water for 10-15 min; dissecting the rinsed coconut shell in the step (3) into crude fiber by a filament forming machine, and then rinsing the fiber with water for 10-15 minutes; mixing the deionized water with chlorine dioxide and sodium carbonate uniformly, and then the rinsed crude fiber in the step (4); conducting soaking for 30 to 40 minutes, taking out the fiber, and rinsing the fiber with hot water for 15 to 20 minutes; and dehydrating the dried fiber in the step (5), and then loosening the fiber with a carding machine to obtain the coconut fiber. The coconut shell fiber extracted by the method for extracting the coconut fiber of the invention has uniformity, less impurities, low residual fat ratio, and guaranteed quality.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a method for extracting coconut shell fibers. Background technique [0002] Coconut shell is the endocarp of palm plant coconut, and coconut shell contains ash 0.61%, lignin 36.51%, cellulose 53.06%, pentosan 29.27% ​​(total amount). It can cure wind, cold, heat and so on. For plant morphology, see Coconut Strips. Carve some patterns and characters on the coconut shell, and even make doll heads, all kinds of bird rain folk art. Coconut husk contains a lot of fiber, and coconut husk fiber can be used to produce rugs, mats, ropes and filter cloths, etc.; secondly, because coconut husk fiber is degradable and will not cause harm to the ecological environment, it can be used in Processing of nonwoven fabrics for soil control; in addition, coir fiber has strong toughness and can be used as a reinforcing base for composite materials instead of synthetic fibers. However, the traditional proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21B1/06D21B1/12D21C5/00
CPCD21B1/06D21B1/12D21C5/005
Inventor 胡长青
Owner 安徽九天印务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap