Method for preparing environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather

A car seat, bio-based technology, applied in the direction of motor vehicles, road vehicles, transportation and packaging, etc., can solve the problems of poor seat covering performance, poor hand feeling and flexibility of non-woven fabrics, etc., and achieve improved flame retardancy Difficult, good surface skin-friendly performance, soft and full-feeling effect

Inactive Publication Date: 2018-12-21
ANHUI ANLI MATERIAL TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Non-woven fabrics have the characteristics of good physical properties and high strength, but the hand feeling and flexibility of commonly used non-woven fabrics are poor, and the covering performance of seats is not good. At the same time, there are many difficulties in improving the flame retardancy of non-woven fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather
  • Method for preparing environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather
  • Method for preparing environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] Such as figure 1 Shown, a kind of preparation method of environmental protection, flame-retardant bio-based car seat polyurethane synthetic leather, comprises the following steps:

[0030] (1) Co-spin bio-based raw materials and nylon to obtain a bio-based cloth base, then impregnate the bio-based cloth base with water-based polyurethane / halogen-free water-based flame retardant impregnating material, then squeeze and dry in sequence to obtain a Combustible bio-based substrates;

[0031] (2) Through the release paper film transfer method, the halogen-free flame-retardant high-solid polyurethane material is laminated to obtain a halogen-free flame-retardant high-solid polyurethane film, and then the release paper is peeled off to obtain a high-solid film with flame-retardant properties;

[0032] (3) Composite the flame-retardant bio-based substrate obtained in step (1) with the flame-retardant high-solid film obtained in step (2), and then perform surface treatment and m...

Embodiment 1

[0045] 1. Co-spinning bio-based raw materials and nylon to form a bio-based high-strength, high-elastic bio-based cloth base, which is impregnated with water-based polyurethane / halogen-free water-based flame retardant impregnation material, extruded, and dried to obtain a bio-based fabric with flame-retardant properties. Substrate, standby; wherein the preferred formula of water-based polyurethane / halogen-free water-based flame retardant impregnating material is as follows:

[0046]

[0047] 2. Through the release paper film transfer method, the halogen-free flame-retardant high-solid polyurethane material is laminated to obtain a halogen-free flame-retardant high-solid polyurethane film, and then the release paper is peeled off to obtain a high-solid film with flame-retardant properties; among them, the halogen-free flame-retardant The preferred formula of burning high solid polyurethane material is as follows:

[0048]

[0049] 3. Composite the bio-based base material wi...

Embodiment 2

[0051] 1. Co-spinning bio-based raw materials and nylon to form a bio-based high-strength, high-elastic bio-based cloth base, which is impregnated with water-based polyurethane / halogen-free water-based flame retardant impregnation material, extruded, and dried to obtain a bio-based fabric with flame-retardant properties. Substrate. Among them, the preferred formula of water-based polyurethane / halogen-free water-based flame retardant impregnation material is as follows:

[0052]

[0053] 2. Through the release paper film transfer method, the halogen-free flame-retardant high-solid polyurethane material is laminated to obtain a halogen-free flame-retardant high-solid polyurethane film, and then the release paper is peeled off to obtain a high-solid film with flame-retardant properties; among them, the halogen-free flame-retardant The preferred formula of burning high solid polyurethane material is as follows:

[0054]

[0055] 3. Composite the bio-based base material with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather. The method comprises the following steps: firstly, cospinning a bio-based raw material and chinlon to obtain bio-based base cloth, and carrying out dipping, extrusion and drying to obtain a bio-based basic material with flame retardancy; preparing a halogen-free flame-retardant high-solid polyurethane membrane in a release paper membrane transferring mode, and peeling off the release paper membrane to obtain a high-solid membrane with flame retardancy; finally compounding the bio-based basic material with the high-solid membrane, thereby obtaining a finished product. The environmentally-friendly flame-retardant bio-based automobile chair polyurethane synthetic leather prepared with the method has flame retardancy which meets requirements of grade B provided by 'GB 8410-2006 combustion property of automotive trim material'. Meanwhile, the leather has the advantages of low VOC (volatile organic compound), good environment protection, flexible and full hand feelings, good surface skin friendliness, high physical strength, oil resistance, aging resistance, and the like.

Description

technical field [0001] The invention relates to the field of preparation methods of polyurethane synthetic leather, in particular to a preparation method of an environment-friendly and flame-retardant bio-based polyurethane synthetic leather for automobile seats. Background technique [0002] At present, automotive interior materials mainly include synthetic leather, leather, thermoplastic polymers and textile materials. With the improvement of people's life and the increasing awareness of health and environmental protection, the hazards of using ordinary leather for car seat cushions are gradually discovered, especially the environmental protection and flame retardancy. [0003] Commonly used flame retardants generally use halogen-based flame-retardant materials, which have good flame-retardant properties and relatively low prices, but they generate a large amount of smoke during combustion and release a large amount of hydrogen halide gas, which has strong corrosion proper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/14
CPCD06N3/0015D06N3/0034D06N3/0059D06N3/0061D06N3/0063D06N3/0097D06N3/145D06N2201/04D06N2201/045D06N2209/067D06N2209/145D06N2209/16D06N2209/1664D06N2209/1692D06N2211/263D06N2211/28
Inventor 赵伟栋邢高瞻张启超杜东旭钟元成王开俊程艳西
Owner ANHUI ANLI MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com