Flame-retardant, high-viscosity and environmental-protection sealant

A sealant and environmental protection technology, applied in the direction of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problems of poor flame retardancy and applicability, and achieve good temperature resistance and long service life Long, good effect

Inactive Publication Date: 2018-12-18
HEFEI LONGYANG AGRI TECH CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of sealant uses antioxidants and anti-ultraviolet agents to improve the weather resistance of the sealant, and has good stability and reproducibility, but its flame retardancy is poor, and its applicability is affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant, high-viscosity and environmental-protection sealant
  • Flame-retardant, high-viscosity and environmental-protection sealant
  • Flame-retardant, high-viscosity and environmental-protection sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] This embodiment relates to a flame-retardant high-viscosity environment-friendly sealant and a preparation method thereof. The sealant is composed of the following raw materials in parts by weight:

[0042] 46 parts of vinyl chloride-acrylate copolymers;

[0043] 30 parts of tert-butylphenol-formaldehyde tackifying resin;

[0044] 8 parts of illite powder with a particle size of 20 μm;

[0045] 3 parts of methylisothiazolinone;

[0046] 7 parts of fluff powder with a particle size of 15 μm;

[0047] 5.5 parts of triphenylmethane triisocyanate;

[0048] 3 parts flaxseed gum;

[0049] 4 parts of tris (butoxyethyl) phosphate;

[0050] Dispersant FT-780.8 parts;

[0051] 3 parts of cross-linking agent;

[0052] Accelerator 1 part;

[0053] 1.5 parts of antioxidant;

[0054] 0.4 parts of coupling agent.

[0055] The selection of crosslinking agent, coupling agent, accelerator and antioxidant in the above raw materials is shown in Table 1 below:

[0056] Table 1

...

Embodiment 2

[0063]This embodiment relates to a flame-retardant high-viscosity environment-friendly sealant and a preparation method thereof. The sealant is composed of the following raw materials in parts by weight:

[0064] 48 parts of vinyl chloride-acrylate copolymers;

[0065] 34 parts of tert-butylphenolic tackifying resins;

[0066] 10 parts of illite powder with a particle size of 20 μm;

[0067] 3.5 parts of methylisothiazolinone;

[0068] 8 parts of fluff powder with a particle size of 15 μm;

[0069] 6.5 parts of triphenylmethane triisocyanate;

[0070] 3.5 parts of linseed gum;

[0071] 4.5 parts of tris (butoxyethyl) phosphate;

[0072] Dispersant FT-780.9 parts;

[0073] 3.5 parts of crosslinking agent;

[0074] Accelerator 1.2 parts;

[0075] 1.8 parts of antioxidant;

[0076] 0.45 parts of coupling agent.

[0077] The selection of crosslinking agent, coupling agent, accelerator and antioxidant in the above raw materials is shown in Table 2 below:

[0078] Table 2...

Embodiment 3

[0086] This embodiment relates to a flame-retardant high-viscosity environment-friendly sealant and a preparation method thereof. The sealant is composed of the following raw materials in parts by weight:

[0087] 49 parts of vinyl chloride-acrylate copolymers;

[0088] 35 parts of tert-butylphenol-formaldehyde tackifying resins;

[0089] 11 parts of illite powder with a particle size of 25 μm;

[0090] 4 parts of methylisothiazolinone;

[0091] 9 parts of fluff powder with a particle size of 20 μm;

[0092] 7 parts of triphenylmethane triisocyanate;

[0093] 4 parts flaxseed gum;

[0094] 5 parts of tris (butoxyethyl) phosphate;

[0095] Dispersant FT-781 parts;

[0096] 4 parts of crosslinking agent;

[0097] Accelerator 1.3 parts;

[0098] Antioxidant 2 parts;

[0099] 0.5 parts of coupling agent.

[0100] The selection of crosslinking agent, coupling agent, accelerator and antioxidant in the above raw materials is shown in Table 3 below:

[0101] table 3

[010...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant, high-viscosity and environmental-protection sealant, and relates to the technical field of building sealant, wherein the sealant includes the following raw materials: a vinyl chloride-acrylate copolymer, tert-butyl phenolic tackifying resin, illite powder with a particle size of 20-30 [mu]m, methyl isothiazolinone, flocking powder with a particle size of15-30 [mu]m, triphenylmethane triisocyanate, flaxseed gum, tris(butoxyethyl)phosphate, a dispersant FT-78, a crosslinking agent, an accelerator, an antioxidant, and a coupling agent. The sealant has the advantages of simple and convenient preparation, fast surface drying speed, compact and stable cross-linking structure of an adhesive layer, good tensile bonding performance, flame retardancy, highand low temperature resistance, water prevention and weather resistance, heat preservation, sound insulation, insect expelling and mildew resistance, green energy saving and environmental protection,wide application occasion fields and long service life.

Description

technical field [0001] The invention relates to the technical field of building sealants, in particular to a flame-retardant high-viscosity environment-friendly sealant. Background technique [0002] At present, most of the building sealants commonly used at home and abroad are polyurethane sealants and silicone rubber sealants. The production process of polyurethane sealant is complicated, the equipment requirements are high, and the investment is large. Moreover, due to the use of moisture curing principle, the storage stability of polyurethane sealant is poor. If the airtightness is not strict or the temperature is slightly high, it is easy to cure and fail. Polyurethane sealants have weak adhesion to vinyl materials such as PVC, EVA, PE and other common building materials, and the bonding strength often fails to meet the requirements. In addition, because the residual isocyanate of polyurethane sealant is harmful to human body, it is not environmentally friendly and has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J127/06C09J161/08C09J11/04C09J11/06C09J11/08
CPCC08L2201/02C08L2201/04C08L2205/03C08L2312/00C09J11/04C09J11/06C09J11/08C09J127/06C08L61/06C08L71/02C08K13/02C08K3/346C08K5/47C08K5/521
Inventor 沈涛
Owner HEFEI LONGYANG AGRI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com