Solder additive for brazing of high nitrogen steel

An additive and high-nitrogen steel technology, applied in the direction of welding/cutting medium/material, welding medium, welding equipment, etc., to achieve the effect of good forming, excellent performance, and optimized structure and performance

Active Publication Date: 2018-12-18
NORTH CHINA UNIV OF WATER RESOURCES & ELECTRIC POWER
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the difficulties in selecting the ratio of weld depth and width and the high In order to solve the serious problem of nitrogen element loss in nitrogen steel, the invention provides a brazing additive for high nitrogen steel brazing, by adding the reinforcing agent of the present invention into the brazing filler metal and then brazing the high ni

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A brazing filler metal additive for high nitrogen steel brazing, said brazing filler metal additive is mixed with a mass ratio of 1:7:3 by reinforcing agent, water-based adhesive and BJQ mixture, and said reinforcing agent is nickel-plated graphite ene or vanadium-coated graphene or a mixture of both in any mass ratio, and the BJQ mixture is formed by mixing barium glass powder, fumed silica and tartaric acid in a mass ratio of 1:3.5:1.

[0053] In the present embodiment, described water-based adhesive can select conventional adhesive for use, but preferably select the water-based adhesive of following composition: according to weight ratio, this water-based adhesive consists of 24 parts of zinc phosphate, 45 parts of ammonium chloride, 15 parts of polyethylene glycol and 14 parts of butyl cyanoacrylate are mixed.

[0054] The high-nitrogen steel described in this embodiment is preferably a high-nitrogen steel with the following components. According to the weight ratio...

Embodiment 2

[0068] A brazing filler metal additive for high nitrogen steel brazing, said brazing filler metal additive is mixed with a mass ratio of 1:8:5 by reinforcing agent, water-based adhesive and BJQ mixture, and said reinforcing agent is nickel-plated graphite ene or vanadium-coated graphene or a mixture of both in any mass ratio, and the BJQ mixture is formed by mixing barium glass powder, fumed silica and tartaric acid in a mass ratio of 1:3.5:1.

[0069] In the present embodiment, the water-based adhesive can be selected from conventional adhesives, but the water-based adhesive of the following components is preferred: according to the weight ratio, the water-based adhesive consists of 36 parts of zinc phosphate, 61 parts of ammonium chloride, 23 parts of polyethylene glycol and 22 parts of butyl cyanoacrylate are mixed.

[0070] The high-nitrogen steel described in this embodiment is preferably a high-nitrogen steel with the following components. According to the weight ratio, ...

Embodiment 3

[0084] A brazing filler metal additive for high nitrogen steel brazing, said brazing filler metal additive is mixed with a mass ratio of 1:7.5:4 by reinforcing agent, water-based adhesive and BJQ mixture, and said reinforcing agent is nickel-plated graphite ene or vanadium-coated graphene or a mixture of both in any mass ratio, and the BJQ mixture is formed by mixing barium glass powder, fumed silica and tartaric acid in a mass ratio of 1:3.5:1.

[0085] In the present embodiment, the water-based adhesive can be selected from conventional adhesives, but the water-based adhesive of the following components is preferred: according to the weight ratio, the water-based adhesive consists of 30 parts of zinc phosphate, 53 parts of ammonium chloride, 19 parts of polyethylene glycol and 18 parts of butyl cyanoacrylate are mixed.

[0086] The high-nitrogen steel described in this embodiment is preferably a high-nitrogen steel with the following components. According to the weight ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a solder additive for brazing of high nitrogen steel. The solder additive is composed of a reinforcing agent, a water-based adhesive and a BJQ mixture in a mass ratio of 1:7 to 8:3 to 5,the reinforcing agent being nickel-plated graphene or vanadium-plated graphene or a mixture of the nickel-plated graphene and the vanadium-plated graphene in any mass ratio, the BJQ mixture being a mixture of barium glass powder, fumed silica and tartaric acid in a mass ratio of 1:3.5:1. When the additive of the present invention is added to the solder for brazing, the high nitrogen steel base material hardly melts, so that the nitrogen element is not lost, overcoming the pore defects of the conventional welding method, so that the nitrogen element has almost no loss; and because the high nitrogen steel base material hardly melts, that is, no deformation is caused, and the connection strength and mechanical properties of the joint are improved to a certain extent, and the welded joint is formed very well.

Description

technical field [0001] The invention relates to a brazing filler metal in the field of metal welding, in particular to a brazing filler metal additive for high-nitrogen steel brazing. Background technique [0002] High-nitrogen steel has properties such as corrosion resistance, oxidation resistance, wear resistance and excellent mechanical properties. These excellent properties make it one of the important materials in the manufacture of aviation, ship and weapon equipment, and welding technology determines its application scope. important process link. Due to the high nitrogen content of high-nitrogen steel itself, the welding porosity problem is often caused by the precipitation of base metal nitrogen during the welding process. The precipitation of nitrides in the heat-affected zone is a major loss of solid-solution nitrogen, and induces the appearance of other hard and brittle phases, thereby weakening the weld. Material properties, reducing the overall performance of w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/363B23K35/40
CPCB23K35/362B23K35/40
Inventor 王星星李帅韦乐余何鹏王博马佳
Owner NORTH CHINA UNIV OF WATER RESOURCES & ELECTRIC POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka