Copper alloy strip with high intensity, high conductivity and high bending performance and preparation method thereof

A copper alloy strip, high-strength technology, applied in the direction of metal rolling, can solve the problems of poor strength of electronic copper strip, low softening temperature, coarse grain structure, etc., to achieve refined structure of finished products, shorten production process, crystal The effect of particle size reduction

Inactive Publication Date: 2018-12-14
FUJIAN ZIJIN COPPER
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] One of the technical problems to be solved by the present invention is to provide a copper alloy strip with high strength, high conductivity, and high bending performance, which can solve the problems of poor strength, general conductivity, and coarse grain structure in existing electronic copper strips. Bending cracking, low softening temperature and other problems caused by

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copper alloy strip with high intensity, high conductivity and high bending performance and preparation method thereof
  • Copper alloy strip with high intensity, high conductivity and high bending performance and preparation method thereof
  • Copper alloy strip with high intensity, high conductivity and high bending performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0074] The thickness of the finished product is 0.08mm, requiring tensile strength ≥ 900MPa, electrical conductivity ≥ 40%, elongation ≥ 1%, grain size ≤ 0.005mm, high-strength, non-brittle when bent at 90 degrees when R / T = 1, Production process of copper alloy strip with high conductivity and high bending performance:

[0075] In step a, during semi-continuous casting, the alloy composition is strictly controlled at Ni: 1.5%, Si: 0.5%, Sn: 0.4%, Zn: 0.6%, Fe≤0.02%, Mg≤0.01%, and the balance is Cu and unavoidable impurities, the casting temperature is 1250°C, and the pull-stop-reverse process is adopted, and the size of the slab obtained by casting is 200mm in thickness and 650mm in width;

[0076] In step b, the billet is annealed at high temperature, the annealing temperature is 900°C, and the holding time is 5h;

[0077] Step c, after the billet is annealed, hot rolling is carried out, and the billet is rolled from a thickness of 200mm to 16mm;

[0078] Step d, the bille...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
crystal sizeaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a copper alloy strip with high intensity, high conductivity and high bending performance and a preparation method thereof. The copper alloy strip is prepared from the followingraw material components in percentage by weight: 1.5 to 2 percent of Ni, 0.4 to 0.6 percent of Si, 0.3 to 0.6 percent of Sn, 0.4 to 0.7 percent of Zn, less than or equal to 0.02 percent of Fe, less than or equal to 0.01 percent of Mg and the balance of Cu and unavoidable impurities. The preparation method comprises the following steps: adding the raw materials during semi-continuous casting for casting to form a cast blank, performing high-temperature annealing, hot-rolling cogging, all-side milling, rough rolling, intermediate rolling, softening annealing in an elevator furnace, cleaning, secondary intermediate rolling, solution treatment in an air-cushion furnace, aging in the elevator furnace, rolling of a twenty-roller finished product, cleaning, low-temperature annealing in the elevator furnace, secondary cleaning, bending and straightening and shearing of the finished product, and packaging the product in a warehouse. The copper alloy strip can solve the problem that an existingelectronic copper strip cracks during bending and is low in anti-softening temperature due to low strength, poor conductivity and thick grain structures.

Description

【Technical field】 [0001] The invention relates to the field of metal materials, in particular to a copper alloy strip with high strength, high conductivity and high bending performance and a preparation method thereof. 【Background technique】 [0002] Compared with pure copper strips, electronic alloy copper strips have higher elasticity, corrosion resistance and fatigue resistance, and are widely used in connectors in mobile phones, computers, TVs, and automobiles, such as USB interfaces, memory card slots, RF Connectors, battery sockets, etc., but with the rapid development of the electronic information industry, the requirements for connectors continue to develop in the direction of miniaturization, complexity, and high current, requiring electronic copper strips to have extremely thin thickness and high tensile strength , High electrical conductivity, high anti-softening temperature, excellent bending performance and anti-fatigue performance. [0003] At present, the com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/06C22F1/08B21B1/26B21B3/00
CPCC22C9/06B21B1/26B21B3/00B21B2003/005C22F1/08
Inventor 刘羽飞王矿金陈春刚李健邱建根王腾云巫金芳王月明周建辉邱丽梅
Owner FUJIAN ZIJIN COPPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com