Fire-resistant heat-preservation coating material for pipelines

A coating material, refractory insulation technology, applied in the field of insulation materials, refractory insulation coating materials for pipelines, can solve the problems that the packaging material is difficult to cover, affect the usability of the coating material, etc., to achieve sufficient fire resistance, suitable refractory components, Ease of use

Inactive Publication Date: 2018-12-14
无锡市明江保温材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the general foam layer structure is relatively thick. In order to obtain sufficient fire resistance and fire resistance, the usability of the coating material will be affected, making it difficult for the coating material to be coated on pipes or machinery and equipment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: A refractory and heat-insulating coating material for pipelines is prepared by the following steps:

[0018] 100 parts by weight of polyurethane resin made of polyisocyanate and polyols, 0.1 parts by weight of potassium acetate, 0.1 parts by weight of blowing agent propane, 0.1 parts by weight of silicone foam stabilizer, 5 parts by weight of flame retardant additives, flame retardant additives adopt Ammonium dihydrogen phosphate, hexabromobenzene, zinc borate, antimony trioxide, aluminum hydroxide, wollastonite in a weight ratio of 1:1:1:1:1:1;

[0019] Said polyisocyanate adopts toluene diisocyanate; said polyol can adopt polycaprolactone diol as hardening agent.

[0020] After mixing the above components, directly spray, coat, and print on the surface of the pipe, or dip the pipe into the mixed covering material, so as to obtain a flame-retardant foaming layer on the surface of the pipe that matches the shape of the pipe; The thickness of the flame-ret...

Embodiment 2

[0022] Embodiment 2: A kind of refractory and thermal insulation coating material for pipelines is prepared by the following steps:

[0023] 100 parts by weight of polyurethane resin made of polyisocyanate and polyol, 10 parts by weight of potassium acetate, 10 parts by weight of blowing agent butane, 10 parts by weight of silicone foam stabilizer, 50 parts by weight of flame retardant additive, flame retardant additive Ammonium dihydrogen phosphate, hexabromobenzene, zinc borate, antimony trioxide, aluminum hydroxide, wollastonite with a weight ratio of 1:2:2:1:1:2 are used;

[0024] The polyisocyanate adopts diphenylmethane diisocyanate; the polyhydric alcohol can adopt ethylene glycol as a hardening agent.

[0025] After mixing the above components, directly spray, coat, and print on the surface of the pipe, or dip the pipe into the mixed covering material, so as to obtain a flame-retardant foaming layer on the surface of the pipe that matches the shape of the pipe; The th...

Embodiment 3

[0027] Embodiment 3: A kind of refractory insulation coating material for pipelines, which is prepared by the following steps:

[0028] 100 parts by weight of polyurethane resin made of polyisocyanate and polyol, 1 part by weight of potassium acetate, 1 part by weight of blowing agent hexane, 1 part by weight of silicone foam stabilizer, 10 parts by weight of flame retardant additive, flame retardant additive Ammonium dihydrogen phosphate, hexabromobenzene, zinc borate, antimony trioxide, aluminum hydroxide, wollastonite with a weight ratio of 1:1.5:1.5:1:1:1.5 are used;

[0029] The polyisocyanate adopts triphenylmethane triisocyanate; the polyalcohol as hardening agent can adopt butanediol.

[0030] After mixing the above components, directly spray, coat, and print on the surface of the pipe, or dip the pipe into the mixed covering material, so as to obtain a flame-retardant foaming layer on the surface of the pipe that matches the shape of the pipe; The thickness of the fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fire-resistant heat-preservation coating material for pipelines. The material is characterized by comprising the following components in parts by weight: 100 parts of polyurethane resin prepared from polyisocyanate and polyalcohol, 0.1-10 parts of potassium acetate, 0.1-10 parts of a foaming agent, 0.1-10 parts of an organic silicon foam stabilizer and 5-50 parts of a flame-retardant additive, wherein the flame-retardant additive is prepared from ammonium dihydrogen phosphate, hexabromobenzene, zinc borate, antimony trioxide, aluminum hydroxide and wollastonite according to a weight ratio of 1:(1-2):(1-2):1:1:(1-2). The fire-resistant heat-preservation coating material has fire resistance and heat preservation performance, has good usability, and is suitable forcoating the peripheries of pipelines or equipment.

Description

technical field [0001] The invention relates to a thermal insulation material, in particular to a refractory thermal insulation coating material for pipelines, which belongs to the technical field of thermal insulation. Background technique [0002] At present, people's awareness of energy saving in various production and life is constantly improving, and thermal insulation coating materials are widely used in various industrial pipelines, kilns, buildings, etc. Existing commonly used insulation materials such as asbestos, glass fiber felt or glass fiber cloth, etc., in order to improve the insulation effect, the method of increasing the thickness of the material is mostly used. However, due to the increase in the thickness of the material itself, when the insulation material needs to be coated on the pipe When it is applied, it will affect the coating effect and the number of layers of coating. [0003] In the prior art, aluminum foil has a certain application in thermal i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D175/04C09D5/18C09D7/63C08G18/42C08G18/76C08G18/32C08J9/14
CPCC08G18/3206C08G18/4277C08G18/7614C08G18/7664C08G18/7671C08J9/0019C08J9/0061C08J9/141C08J2203/14C08J2375/06C08K2003/2227C08K2003/321C08K2003/387C09D5/18C09D7/63C09D175/04C09D175/06C08K13/02C08K5/03C08K3/38C08K3/34C08K3/32C08K3/2279
Inventor 周致中
Owner 无锡市明江保温材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com