Application of novel epoxy modified heat-resisting liquid silicon rubber

A technology of liquid silicone rubber and application, which is applied in the direction of epoxy resin glue, epoxy resin coating, adhesive, etc., to achieve the effects of short time, increased bonding strength and broad market application prospects

Pending Publication Date: 2018-12-11
SICHUAN UNIV
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Modification of silicone rubber with other polymers can improve the above shortcomings. At present, there is no report on the use of bisphenol A epoxy resin for modifying liquid silicone rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of novel epoxy modified heat-resisting liquid silicon rubber
  • Application of novel epoxy modified heat-resisting liquid silicon rubber
  • Application of novel epoxy modified heat-resisting liquid silicon rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1, the preparation of adhesive of the present invention

[0024] One, the preparation method of the liquid silicone rubber of epoxy resin modification of the present invention

[0025] 1 Experimental raw materials

[0026]

[0027] 2 Preparation of bisphenol A type epoxy resin-silane coupling agent prepolymer

[0028]

[0029] To a three-necked flask equipped with a thermometer, a mechanical stirrer and a reflux condenser device, an epoxy resin (E44, 50 g) and a silane coupling agent (SCA-L, 13.04 g) were sequentially added in a molar ratio of 1:1 to feed an inert Exhaust the air in the device, raise the temperature to 100°C and keep it constant, start stirring to make the mixture evenly mixed. By changing the time of the prepolymerization reaction and the amount of catalyst (tetraisopropyl titanate) (see Table 1), 9 groups of different primary products were prepared respectively, and the primary products were taken out, and the unreacted silane disul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides application of novel epoxy modified heat-resisting liquid silicon rubber. Specifically, the invention provides application of heat-resisting type liquid silicon rubber with improved strength and interface bonding performance to a preparation of a coating, a binding agent and a composite material. The epoxy modified heat-resisting liquid silicon rubber is prepared from the following raw materials in parts by weight: 100 parts of liquid silicon rubber, 10 parts of a bisphenol A type epoxy resin-silane coupling agent pre-polymer, 3 parts of a curing agent and 0.2 part of acatalyst A. To sum up, the strength and elongation at break of modified liquid silicon rubber are greatly improved (the tensile strength is improved to reach 0.83MPa and is improved by 162 percent when being compared with that of a pure sample, the bonding performance is 0.81MPa and is improved by 160 percent when being compared with that of the pure sample, and the elongation at break reaches 268percent and is improved by about 2 times when being compared with that of the pure sample); the rigidity and toughness of a material matrix are improved at the same time, and the interface bonding strength with filler and the matrix is remarkably increased when the liquid silicon rubber is used for a coating, a bonding agent and a composite material; the application field of the liquid silicon rubber is expanded and the service life of the liquid silicon rubber is prolonged. Meanwhile, the heat resisting performance still can keep a relatively high level, and the heat residual weight at 800 DEG C reaches 53.53 percent; a synthesis process has the advantages of simplicity, easiness for processing, short time and few steps and has a wide market application prospect.

Description

technical field [0001] The invention relates to the use of a novel epoxy-modified heat-resistant liquid silicone rubber, in particular to a heat-resistant liquid silicone rubber with improved molecular cohesion strength and interface bonding performance in the preparation of coatings, adhesives and composite materials use in . Background technique [0002] Silicone rubber is a linear type in which the main chain is composed of silicon-oxygen bonds (Si-O) alternately, and organic groups (such as methyl, ethyl, vinyl, phenyl, trifluoropropyl, etc.) form its side groups. polyorganosiloxane. Due to the particularity of structure and composition, silicone rubber materials combine the characteristics and functions of inorganic and organic substances, and have excellent properties that many other materials cannot have at the same time, such as excellent high and low temperature resistance, excellent oil resistance, solvent resistance, UV resistance, radiation resistance, good agi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/07C09D163/00C09D7/65C09J183/07C09J163/00C09J11/08C08L83/07C08L63/00C08L83/05
CPCC08L83/04C08L2201/08C08L2205/025C08L2205/03C09D183/04C09J11/08C09J183/04C09D7/65C08L63/00
Inventor 邹华维张斌陈洋梁梅
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com