A kind of preparation method of water treatment activated alumina ball

A technology of activated alumina and water treatment, applied in water/sewage treatment, chemical instruments and methods, special compound water treatment, etc., can solve the problems of unfavorable continuous treatment of pollutants, etc. Good results

Active Publication Date: 2021-04-06
山西炬华新材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The adsorption-regeneration process causes the interruption of the adsorption treatment process, which is not conducive to the continuous treatment of pollutants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method for water treatment activated alumina balls, comprising the following process steps:

[0024] Step 1, prepare the aluminum-zinc mixture:

[0025] (1) Add 255mL of ethanol, 8g of zinc acetate, and 11g of aluminum isopropoxide in a 500mL round-bottomed flask, and install a spherical condenser at the mouth of the flask. With tap water as the cooling medium, the solution is heated to 68°C. Heat preservation and reflux for 50min;

[0026] (2) Add 9 mL of 15% tetrabutylammonium hydroxide ethanol solution, 3 g of sodium acetate, and 3.5 mL of tributyl phosphate into the round bottom flask, and continue to insulate and reflux at 68° C. for 70 min;

[0027] (3) Install the flask on a rotary evaporator, control the temperature of the water bath to 70°C, and rotate the flask at a speed of 100rpm, and evaporate to the remaining 2 / 3 of the solution volume to obtain the aluminum-zinc mixed solution;

[0028] Step 2, Al-Zn-O surface bonding:

[0029] (1) 20g ac...

Embodiment 2

[0036] A preparation method for water treatment activated alumina balls, comprising the following process steps:

[0037] Step 1, prepare the aluminum-zinc mixture:

[0038] (1) Add 280mL of ethanol, 12g of zinc acetate, and 15g of aluminum isopropoxide into a 500mL round-bottom flask in sequence, install a spherical condenser, use tap water as the cooling medium, heat the solution to 68°C, and keep at this temperature for 50min under reflux;

[0039] (2) Add 11 mL of 15% tetrabutylammonium hydroxide ethanol solution, 5 g of sodium acetate, and 4.5 mL of tributyl phosphate into the round-bottomed flask, and continue to insulate and reflux at 68° C. for 70 min;

[0040] (3) Install the flask on a rotary evaporator, control the temperature of the water bath to 70°C, and rotate the flask at a speed of 100rpm, and evaporate to the remaining 2 / 3 of the solution volume to obtain the aluminum-zinc mixed solution;

[0041] Step 2, Al-Zn-O surface bonding:

[0042] (1) 20g activated ...

Embodiment 3

[0049] A preparation method for water treatment activated alumina balls, comprising the following process steps:

[0050] Step 1, prepare the aluminum-zinc mixture:

[0051] (1) Add 310mL of ethanol, 15g of zinc acetate, and 18g of aluminum isopropoxide into a 500mL round-bottomed flask in sequence, install a spherical condenser, use tap water as the cooling medium, heat the solution to 68°C, and keep at this temperature for 50min under reflux;

[0052] (2) Add 13 mL of 15% tetrabutylammonium hydroxide ethanol solution, 7 g of sodium acetate, and 5.5 mL of tributyl phosphate into the round-bottomed flask, and continue to insulate and reflux at 68° C. for 70 min;

[0053] (3) Install the flask on a rotary evaporator, control the temperature of the water bath to 70°C, and rotate the flask at a speed of 100rpm, and evaporate to the remaining 2 / 3 of the solution volume to obtain the aluminum-zinc mixed solution;

[0054] Step 2, Al-Zn-O surface bonding:

[0055] (1) 20g activate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A method for preparing water-treatment activated alumina balls, which belongs to the field of environmental purification functional materials; the preparation method: 1) mixing ethanol, zinc acetate and aluminum isopropoxide in a flask, heating and keeping it warm, and then adding 15% four Butyl ammonium hydroxide ethanol solution, sodium acetate, tributyl phosphate, continue to heat and keep warm, evaporate the solution in the flask to the remaining 2 / 3 of the volume, and then prepare the aluminum-zinc mixed solution; 2) add activated alumina balls treated with phosphoric acid into the aluminum-zinc mixed solution, carry out hydrothermal reaction, filter the solid-liquid mixture after the reaction, and clean the solid matter; 3) dry the solid matter after cleaning, then calcinate at high temperature, and obtain water-treated activated alumina balls after cooling; The invention prepares an Al-Zn-O surface bonding coating on the surface of an activated alumina sphere, which can not only remove pollutants in water through adsorption, but also degrade the adsorbed organic pollutants through a photocatalytic reaction so as to have continuous adsorption capacity.

Description

technical field [0001] The invention belongs to the field of environmental purification functional materials, and in particular relates to a preparation method of water treatment activated alumina balls. Background technique [0002] Activated alumina balls are also known as water-purifying activated alumina, and the alumina used in catalysts is usually called activated alumina. It is a porous, highly dispersed solid material with a large surface area, and its microporous surface has the characteristics required for catalysis, such as adsorption performance, fluorine removal performance, drying performance, surface activity, and excellent thermal stability. properties, etc., so it is widely used as a household desiccant and a catalyst and catalyst carrier for chemical reactions. Modern water-purifying activated alumina is white spherical porous particles with uniform particle size, smooth surface, high mechanical strength and strong hygroscopicity. In addition to being use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/06B01J35/08B01J35/10C02F1/30C02F1/28C02F101/30
CPCB01J23/002B01J23/06B01J35/004B01J35/08B01J35/10C02F1/281C02F1/30C02F2101/30C02F2305/10
Inventor 张文杰韩铭张悦董英昊李昊伦
Owner 山西炬华新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com