Tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and preparation method and application thereof

A nitrogen-doped carbon and catalyst technology, applied in electrical components, battery electrodes, circuits, etc., can solve problems such as low specific surface area and low ORR catalytic activity

Inactive Publication Date: 2018-11-06
XIANGTAN UNIV
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the catalyst prepared by this method has low ORR catalytic activity due to the low specific surface area, and the use of porous organic polymer (POP) as a single precursor to prepare N / C catalysts came into being.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and preparation method and application thereof
  • Tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and preparation method and application thereof
  • Tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] A nitrogen-doped carbon-oxygen reduction catalyst based on tetrazine ring polycarbazole, which is prepared by the following preparation method: first, 3,6-bis(3,5-dimethylpyrazole)-1,2 , 4,5-tetrazine prepared 3,6-bis(carbazolyl)-1,2,4,5-tetrazine (TCy) monomer by substitution reaction, and then 3,6-bis(carbazolyl) -1,2,4,5-Tetrazine (TCy) is obtained by Friedel-Crafts alkylation reaction to obtain tetrazine ring polycarbazole; then tetrazine ring polycarbazole is pyrolyzed to obtain tetrazine ring polycarbazole Nitrogen-doped carbon-oxygen reduction catalysts.

Embodiment 2

[0068]A nitrogen-doped carbon-oxygen reduction catalyst based on tetrazine ring polycarbazole, which is prepared by the following preparation method: first, 3,6-bis(3,5-dimethylpyrazole)-1,2 , 4,5-tetrazine prepared 3,6-bis(carbazolyl)-1,2,4,5-tetrazine (TCy) monomer by substitution reaction, and then 3,6-bis(carbazolyl) -1,2,4,5-tetrazine (TCy) can be obtained tetrazine ring polycarbazole through oxidative coupling reaction; then tetrazine ring polycarbazole is pyrolyzed to obtain tetrazine ring polycarbazole-based nitrogen-doped Heterocarbon oxygen reduction catalyst.

Embodiment 3

[0070] A method for preparing a nitrogen-doped carbon-oxygen reduction catalyst based on tetrazine ring polycarbazole, comprising the following steps:

[0071] (1) Preparation of 3,6-bis(carbazolyl)-1,2,4,5-tetrazine (TCy): add 10mmol 3,6-bis(3,5-dimethylpyrazole) -1,2,4,5-tetrazine suspension in acetonitrile was added to the flask with 22mmol carbazole salt (preparation method: carbazole was added KOH at 0°C, stirred for 5h), stirred at room temperature for one hour, refluxed for 8h; cooled to At room temperature, filter, wash with acetonitrile and dry, and finally pass through the column with petroleum ether / chloroform; figure 2 is the composite map of TCy, image 3 is the NMR map of TCy;

[0072] (2) Synthesis based on 1,2,4,5-tetrazine ring polycarbazole hypercrosslinked polymer network (PTCy-1): add 40mmol dimethoxymethane to the nitrobenzene solution system of 10mmolTCy, stir 30min, then 40mmol FeCl 3 Added to the reaction system, and reacted at 45°C for 5h, and rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and a preparation method thereof. The method comprises the steps of firstly synthesizing 3,6-bis(carbazolyl)-1,2,4,5-tetrazine (TCy) through a simple method; synthesizing a novel super-crosslinked polymer tetrazine ring polycarbazole (PTCy-1 or PTCy-2) by taking TCy as a monomer through Friedel-Crafts alkylation reaction or oxidative coupling reaction; and obtaining the tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst (N / C) from the tetrazine ring polycarbazole through a direct pyrolysis method. The synthesized catalyst has excellent oxygen reduction (ORR) catalytic activity and electrochemical stability.

Description

technical field [0001] The invention relates to an oxygen reduction catalyst and a preparation method thereof, in particular to a tetrazine ring polycarbazole-based nitrogen-doped carbon-oxygen reduction catalyst and a preparation method thereof, belonging to the field of fuel cell science and technology. Background technique [0002] Environmental pollution and energy shortages brought about by the development of industrialization have prompted people to urgently look for new energy devices. Fuel cells are a kind of green energy that can directly convert chemical energy into electrical energy, and its process is not limited by the Caljo cycle. New energy devices have set off a research boom in recent years. However, Pt and Pt-based catalysts that catalyze the oxygen reduction reaction (ORR) at the cathode of fuel cells have seriously hindered the large-scale commercial production of fuel cells due to their high price, poor stability, and poor resistance to methanol. Theref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/90
CPCH01M4/9091Y02E60/50
Inventor 陈红飙孙滔阳梅刘益江黎华明
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap