Preparation method of graphite oxide capable of being washed directly

A technology of water washing and graphite, which is applied in chemical instruments and methods, graphite, inorganic chemistry, etc., can solve the problems that neutral graphite oxide cannot be obtained by direct washing, it is difficult to industrial scale, and the development of graphite oxide is limited. Optimize, reduce the range of motion, and avoid damage

Active Publication Date: 2018-10-12
SHANGHAI LEVSON ENTERPRISE GRP
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In summary, none of the existing graphite oxide preparation methods can obtain neutral graphite oxide through direct washing, which consumes a lot of manpower and material resources in actual operation, and is difficult to industrial scale, which severely limits the development of graphite oxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphite oxide capable of being washed directly
  • Preparation method of graphite oxide capable of being washed directly
  • Preparation method of graphite oxide capable of being washed directly

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0058] The present invention will be further described below in conjunction with the accompanying drawings.

[0059] see figure 1, figure 2 , a method for preparing graphite oxide that can be directly washed with water, comprising the following steps, step 1, using flake graphite as a raw material, adding a main intercalation agent and an auxiliary intercalation agent for intercalation treatment, and intercalating at 0-45°C React for 0.1-20h to obtain graphite intercalation compound; the main intercalation agent is at least one of formic acid, acetic acid, phosphoric acid, concentrated nitric acid, and concentrated sulfuric acid; the auxiliary intercalation agent is a 30% aqueous hydrogen peroxide solution with a concentration of 90% performic acid, the concentration is at least one of 50% peracetic acid; step 2, after the graphite intercalation compound is filtered to remove excess main intercalation agent and auxiliary intercalation agent, put it into ice water, filter and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of graphite oxide capable of being washed directly. The preparation method comprises the following steps that step one, crystalline flake graphite is takenas a raw material, a main intercalator and an auxiliary intercalator are added for intercalation treatment to obtain a graphite intercalation compound; the main intercalator is at least one of formicacid, acetic acid, phosphoric acid, concentrated nitric acid and concentrated sulfuric acid; the auxiliary intercalator is at least one of an aqueous hydrogen peroxide solution, performic acid and peracetic acid; step two, after redundant main intercalator and auxiliary intercalator of the graphite intercalation compound are filtered out, the filtered graphite intercalation compound is put into ice water, tiny impurity particles and water are filtered and washed off with a sieve, and the graphite intercalation compound with less impurities is obtained; step three, an oxidizing agent is added in the filtered graphite intercalation compound, oxidation is carried out for 0.5-50 hours under the condition of 0-45 DEG C, and the graphite oxide of which a PH value is 0-1 and capable of being washed directly by the water is obtained. By the method, the volume of the raw material is swelled to 300 times to 500 times or above.

Description

technical field [0001] The invention relates to the technical field of graphite manufacture, in particular to a preparation method of graphite oxide. Background technique [0002] The current methods for preparing graphite oxide include Brodie, Staudernmaie, and Hummers methods. The oxidation degree of graphite oxide obtained by Brodie method and Standenmaier method is low, and the oxidation degree of graphite oxide prepared by Hummers method is high. Graphite oxide or graphene oxide prepared by these methods is subjected to suction filtration, centrifugation, or dialysis and water washing to obtain a graphene oxide aqueous phase dispersion with a pH between 4 and 7. [0003] In summary, none of the existing graphite oxide preparation methods can obtain neutral graphite oxide through direct washing, which consumes a lot of manpower and material resources in actual operation, and is difficult to industrial scale, which severely limits the development of graphite oxide. Con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/23C01B32/198
CPCC01B32/198C01B32/23
Inventor 武桐段亚强张燕萍赵志国
Owner SHANGHAI LEVSON ENTERPRISE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com