Temperature-resistant and corrosion-resistant building glass ceramic

A glass-ceramic and corrosion-resistant technology, applied in the field of temperature-resistant and corrosion-resistant architectural glass-ceramics, can solve the problems of poor fire resistance and limited applicability, and achieve the effects of long service life, wide range and excellent temperature resistance.

Inactive Publication Date: 2018-09-28
HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of glass-ceramics has good mechanical strength and acid and alkali corrosion resistance, but its fire resistance is poor, and its application is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperature-resistant and corrosion-resistant building glass ceramic
  • Temperature-resistant and corrosion-resistant building glass ceramic
  • Temperature-resistant and corrosion-resistant building glass ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] This embodiment relates to a heat-resistant and corrosion-resistant architectural glass-ceramic and its preparation process. The glass-ceramic is composed of the following raw materials in parts by weight:

[0068] 68 parts of siliceous shale;

[0069] 37 pieces of Yuliang stone;

[0070] 24 parts of vanadium-lead flotation tailings;

[0071] 27 parts limestone;

[0072] 18 parts of witherite;

[0073] 15 parts broken glass;

[0074] Na 2 CO 3 10 parts of powder;

[0075] Yb 2 o 3 6 parts of powder;

[0076] 3 parts of compound clarifying agent;

[0077] The above-mentioned composite clarifying agent is obtained by combining sodium nitrate, calcium sulfate, strontium chloride, and antimony-doped tin dioxide according to the mass ratio of 3:4:1:2.

[0078] The preparation process of this kind of glass-ceramic is generally carried out according to the following steps:

[0079] (1) Prepare raw materials: obtain raw materials according to the proportioning by we...

Embodiment 2

[0087] This embodiment relates to a heat-resistant and corrosion-resistant architectural glass-ceramic and its preparation process. The glass-ceramic is composed of the following raw materials in parts by weight:

[0088] 72 parts of siliceous shale;

[0089] 40 parts of Yuliang stone;

[0090] 28 parts of vanadium-lead flotation tailings;

[0091] 29 parts limestone;

[0092] 20 parts of witherite;

[0093] 18 parts broken glass;

[0094] Na 2 CO 3 12 parts of powder;

[0095] Yb 2 o 3 7 parts of powder;

[0096] 4 parts of compound clarifying agent;

[0097] The above composite clarifier is obtained by combining sodium nitrate, calcium sulfate, strontium chloride and antimony-doped tin dioxide according to the mass ratio of 3.5:4.5:1.5:2.5.

[0098] The preparation process of this kind of glass-ceramic is generally carried out according to the following steps:

[0099] (1) Prepare raw materials: obtain raw materials according to the proportioning by weight, and p...

Embodiment 3

[0107] This embodiment relates to a heat-resistant and corrosion-resistant architectural glass-ceramic and its preparation process. The glass-ceramic is composed of the following raw materials in parts by weight:

[0108] 75 parts of siliceous shale;

[0109] 43 pieces of Yuliang stone;

[0110] 30 parts of vanadium-lead flotation tailings;

[0111] 31 parts of limestone;

[0112] 22 parts of witherite;

[0113] 20 parts broken glass;

[0114] Na 2 CO 3 13 parts of powder;

[0115] Yb 2 o 3 8 parts of powder;

[0116] 5 parts of compound clarifying agent;

[0117] The above-mentioned composite clarifying agent is obtained by combining sodium nitrate, calcium sulfate, strontium chloride, and antimony-doped tin dioxide according to the mass ratio of 4:5:2:3.

[0118] The preparation process of this kind of glass-ceramic is generally carried out according to the following steps:

[0119] (1) Prepare raw materials: obtain raw materials according to the proportioning by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses temperature-resistant and corrosion-resistant building glass ceramic, and relates to the technical field of glass ceramic. The temperature-resistant and corrosion-resistant building glass ceramic comprises siliceous shale, limonite, vanadinite flotation tailing, limestone, witherite, broken glass, Na2CO3 powder, Yb2O3 powder and compound clarifying agents. The temperature-resistant and corrosion-resistant building glass ceramic has the advantages of simplicity and convenience in preparation, excellent temperature resistance, high mechanical strength, good chemical stability, long service life and wide application places and fields.

Description

technical field [0001] The invention relates to the technical field of glass-ceramics, in particular to a glass-ceramic for heat-resistant and corrosion-resistant buildings. Background technique [0002] Glass-ceramics, also known as ceramic glass, has dual characteristics of glass and ceramics; glass-ceramics is composed of crystals, and its atomic arrangement is regular. Therefore, glass-ceramics has higher brightness than ceramics and stronger toughness than glass. Glass-ceramics combines the triple advantages of glass, ceramics and natural stone, and is superior to natural stone and ceramics. It can be used in building curtain walls and indoor high-end decoration, becoming an ideal substitute for high-grade stone. At present, the waste rate of existing glass-ceramic products is high, especially in the finished glass-ceramic plates, unclosed pores and shrinkage cavities are prone to occur, resulting in a decrease in the mechanical properties of the product, which in turn ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/00C03C6/10C03C6/02C03C1/00C03B32/02C03B25/00
CPCC03B25/00C03B32/02C03C1/004C03C10/0063
Inventor 徐仙峰
Owner HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com