High-carbon steel surface corrosion resistant non-spangle type hot dipping Y containing zinc alloy

A hot-dip galvanizing and corrosion-resistant technology, which is applied in the field of alloys, can solve the problems of no efficient and simple production methods and processing techniques, and achieve excellent volatility and oxidation resistance, low annual cost of funds, and good corrosion resistance. Effect

Inactive Publication Date: 2018-08-17
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the higher requirements of the automobile and other industries, people have long proposed the idea of ​​eliminating high-carbon steel spangles and making spangles thinner, but so far there is no efficient and simple production method or processing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A corrosion-resistant zinc-free pattern hot-dip zinc alloy containing Y is used on the surface of high-carbon steel at 360-450 degrees. In terms of weight percentage, the chemical composition of the alloy is: Li: 0.8wt.%, Y: 0.2wt.%, Si: 1.2wt.%, In: 1.4wt.%, Sc: 0.2wt.%, Er: 0.1wt.% .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating to 500-600 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy The liquid is kept at 500-600 degrees for 10 minutes and then cast into the equipment at the same level as the hot top for semi-continuous casting into the required round ingot. The ingot moves down at a speed of 5-10m / min. The ingot can be used as raw material for hot-dip galvanizing for subsequent hot-dip galvanizing treatment to protect steel wires. ...

Embodiment 2

[0020] A corrosion-resistant zinc-free pattern hot-dip zinc alloy containing Y is used on the surface of high-carbon steel at 360-450 degrees. In terms of weight percentage, the chemical composition of the alloy is: Li: 0.8wt.%, Y: 0.4wt.%, Si: 1.6wt.%, In: 1.2wt.%, Sc: 0.3wt.%, Er: 0.2wt .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating to 500-600 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy The liquid is kept at 500-600 degrees for 10 minutes and then cast into the equipment at the same level as the hot top for semi-continuous casting into the required round ingot. The ingot moves down at a speed of 5-10m / min. The ingot can be used as raw material for hot-dip galvanizing for subsequent hot-dip galvanizing treatment to protect steel wires. Th...

Embodiment 3

[0023] A corrosion-resistant zinc-free pattern hot-dip zinc alloy containing Y is used on the surface of high-carbon steel at 360-450 degrees. In terms of weight percentage, the chemical composition of the alloy is: Li: 0.9wt.%, Y: 0.4wt.%, Si: 1.5wt.%, In: 1.2wt.%, Sc: 0.2wt.%, Er: 0.1wt.% .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating to 500-600 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy The liquid is kept at 500-600 degrees for 10 minutes and then cast into the equipment at the same level as the hot top for semi-continuous casting into the required round ingot. The ingot moves down at a speed of 5-10m / min. The ingot can be used as raw material for hot-dip galvanizing for subsequent hot-dip galvanizing treatment to protect steel wires. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-carbon steel surface corrosion resistant non-spangle type hot dipping Y containing zinc alloy and a machining technology thereof. The alloy is prepared from the ingredients, in percentage by weight: 0.8-1.0% of Li, 0.2-0.5% of Y, 1.0-2.0% of Si, 1.0-1.5% of In, 0.2-0.3% of Sc, 0.1-0.2% of Er and the balance of zinc. The development of the alloy can solve the phenomenon that spangles occur on the surface of a plating piece in the industrial hot dipping galvanizing process. The alloy has the characteristics of being low in production cost and convenient for scale production.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a zinc alloy. Background technique [0002] The most widely used steel material in the industry will be corroded to varying degrees when used in environments such as the atmosphere, sea water, soil, and building materials. According to statistics, the annual loss of steel materials due to corrosion in the world can account for about 1 / 3 of its total output. In order to ensure the normal use of steel products and prolong their service life, the anti-corrosion protection technology of steel has been widely valued by people. [0003] The melting point of zinc is very low, only 419.7°C, and it can be dipped in the temperature range of 450-480°C. The generally obtained gray coating consists of two layers: the outer layer is a zinc layer, and the inner layer is an iron-zinc intermetallic compound layer. The formation of intermetallic compounds can make the metallurgical bond between ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/06C22C18/00C22C1/02
CPCC23C2/06C22C1/02C22C18/00
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com