A technology of rubber composition and rubber matrix, which is applied in the field of rubber, and can solve the problems of difficult crosslinking, large steric hindrance, affecting processing efficiency and product performance, etc.

Active Publication Date: 2018-07-24
HANGZHOU XINGLU TECH CO LTD +1
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Rubber generally needs to be cross-linked before use. Among the commonly used cross-linking methods for ethylene-propylene rubber, peroxide cross-linking or radiation cross-linking are suitable for ethylene-α-olefin copolymers. Both are mainly through the capture of tertiary carbons. Hydrogen atoms form tertiary carbon radicals, and then form carbon-carbon crosslinks through free radicals, but the copolymer of ethylene and 1-octene (hereinafter referred to as POE) has fewer tertiary carbon atoms, and the branch connected to the tertiary carbon atoms Chain length, large steric hindrance, difficult free radical reaction, resulting in difficulty in crosslinking, affecting processing efficiency and product performance, such as unsatisfactory compression set resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition, processing method, application and production of application
  • Rubber composition, processing method, application and production of application
  • Rubber composition, processing method, application and production of application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0118] The branched polyethylene number used is PER-4.

[0119] The processing steps are as follows:

[0120] (1) Rubber mixing: set the temperature of the internal mixer to 90°C, and the rotor speed to 50 rpm, add 70 parts of EPDM rubber and 30 parts of branched polyethylene for pre-compression mixing for 90 seconds; add 40 parts of white Carbon black, knead for 3 minutes; then add 2 parts of cross-linking agent dicumyl peroxide (DCP), knead for 2 minutes and degum. Thinly pass the mixed rubber on the open mill, increase the roller distance to obtain a thin sheet with a thickness of about 2.5mm, and park it for 20 hours. Re-smelting, make triangular bags 3 times on the open mill, adjust the roller distance to 2.5mm, and unload.

[0121] (2) Perform various tests after parking for 16 hours after vulcanization.

Embodiment 2

[0123] The branched polyethylene number used is PER-4.

[0124] The processing steps are as follows:

[0125] (1) Rubber mixing: set the temperature of the internal mixer to 90°C, and the rotor speed to 50 rpm, add 50 parts of EPDM rubber and 50 parts of branched polyethylene for pre-compression mixing for 90 seconds; add 40 parts of white Carbon black, knead for 3 minutes; then add 2 parts of cross-linking agent dicumyl peroxide (DCP), knead for 2 minutes and degum. Thinly pass the mixed rubber on the open mill, increase the roller distance to obtain a thin sheet with a thickness of about 2.5mm, and park it for 20 hours. Re-smelting, make triangular bags 3 times on the open mill, adjust the roller distance to 2.5mm, and unload.

[0126] (2) Perform various tests after parking for 16 hours after vulcanization.

Embodiment 3

[0128] The branched polyethylene number used is PER-4.

[0129] The processing steps are as follows:

[0130] (1) Rubber mixing: set the temperature of the internal mixer to 90°C, the rotor speed to 50 rpm, add 100 parts of branched polyethylene for pre-compression mixing for 90 seconds; add 40 parts of white carbon black, and mix for 3 minutes; Then add 2 parts of cross-linking agent dicumyl peroxide (DCP), mix for 2 minutes, and remove the glue. Thinly pass the mixed rubber on the open mill, increase the roller distance to obtain a thin sheet with a thickness of about 2.5mm, and park it for 20 hours. Re-smelting, make triangular bags 3 times on the open mill, adjust the roller distance to 2.5mm, and unload.

[0131] (2) Perform various tests after parking for 16 hours after vulcanization.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Branching factoraaaaaaaaaa
Login to View More

Abstract

The invention discloses a rubber composition and a processing method thereof, and application of the rubber composition to the processing of a white carbon black reinforced rubber product. The rubbercomposition comprises a rubber matrix and necessary components, wherein the rubber matrix comprises the following components: branched polyethylene with the content a being greater than 0 and smallerthan or equal to 100 parts; ethyene-propylene rubber and ethylene propylene terpolymer with the content b being greater than or equal to 0 and smaller than 100 parts; the necessary components comprisethe following components: 1 to 10 parts of a cross-linking agent, and 15 to 80 parts of white carbon black. The rubber composition has the benefits that the rubber composition has high mechanical strength, and can be used for producing high-voltage insulation sleeve size, high temperature-resistance conveying belts, waterproof roll, color rubber particles for surface layers of plastic runways, rubber plugs, rubber rolls, inner tubes, tire treads, side walls of tires, and inner rubber layers of air conditioner rubber tubes.

Description

technical field [0001] The invention belongs to the technical field of rubber, and in particular relates to a rubber composition reinforced by white carbon black and a processing method thereof, as well as a rubber product using the rubber composition and a production method. Background technique [0002] Silica is currently the most commonly used light-colored filler with good reinforcement. Ethylene-propylene rubber reinforced with silica often has good tear resistance, high adhesion strength, wet-slip resistance, wear resistance and biochemical properties. The heat is small, and can be used to produce various rubber products such as waterproof membranes, conveyor belts, plastic runways, washing machine door seals, rubber rollers, rubber plugs, rubber plugs, inner tubes, tire treads, tire sidewalls, air-conditioning hoses, etc. However, it is weaker than ethylene-propylene rubber products reinforced by carbon black in terms of resilience and compression set resistance. Su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/06C08L71/02C08K13/02C08K3/36C08K5/14C08K3/06C08K3/22C08K5/09H01B3/28H01B3/44B65G15/34B60C1/00B29B9/06B29C35/02B29C43/24
CPCH01B3/28H01B3/441B65G15/34C08K3/06C08K3/36C08K5/14C08L23/06C08L23/16B29B9/06B29C35/02B29C43/24B60C1/0016B60C1/0025C08K2003/2296C08L2205/035C08L2205/03C08L2205/025C08L2203/18C08L2207/07C08L71/02C08K13/02C08K3/22C08K5/09B29B7/183B29B7/005B29B7/103B29B7/286B29B7/7495B29K2995/0088B29K2105/0094B29K2023/16B29K2019/00B29L2031/7092B29L2023/005B29L2023/007B29L2023/006C08L91/00C08K3/346C08F110/02C08F4/7006C08F2500/09C08F2500/04C08F2500/17B29K2509/08C08F10/02C08F2810/20C08L2203/202C08L2312/00
Inventor 不公告发明人
Owner HANGZHOU XINGLU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com