Three-layer co-extrusion high heat preservation light conversion po film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A three-layer co-extrusion, shed film technology, applied in the field of agricultural shed film, can solve problems such as single function, achieve the effects of good optical performance, improved flexibility, and high heat sealing strength
Active Publication Date: 2020-01-14
HENAN YINFENG PLASTIC
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But at present PO agricultural shed film generally has a single function deficiency. The applicant has improved the PO agricultural shed film in the invention patent "three-layer co-extrusion EVA long-life anti-fog and environmental protection multifunctional greenhouse film 201310219304.2" applied in the previous period. Mix the formulations of the outer layer, middle layer and inner layer evenly, and use a twin-head threaded screw twin-screw extruder to make a masterbatch, which is extruded through a co-extrusion die to form a three-layer film, which has excellent anti-aging performance and no mist. Functional agricultural greenhouse film
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0044] The raw material formula of the present invention is as follows: each component is calculated by weight percentage,
[0045] Inner layer: linear low density polyethylene (LLDPE) 0209AA: 10%, metallocene linear low density polyethylene mLLDPE1018HA: 55%, low density polyethylene LDPE2420D: 15%, long-life masterbatch 15%, rheological agent 5%.
[0047] Outer layer: linear low density polyethylene (LLDPE) 0209AA: 10%, metallocene linear low density polyethylene mLLDPE1018HA: 60%, low density polyethylene LDPE2420D: 10%, long-life masterbatch 16%, rheological agent 4%.
[0048] The longevity masterbatch is composed of the following components, each component in weight percentage: dripping agent...
Embodiment 2
[0052] The raw material formula of the present invention is as follows: each component is calculated by weight percentage, inner layer: linear low density polyethylene (LLDPE) 0209AA: 10%, metallocene linear low density polyethylene mLLDPE1018HA: 60%, low density polyethylene LDPE2420D: 15 %, longevity masterbatch 10%, rheological agent 5%.
[0054] Outer layer: linear low density polyethylene (LLDPE) 0209AA: 20%, metallocene linear low density polyethylene mLLDPE1018HA: 50%, low density polyethylene LDPE2420D: 10%, longevity masterbatch 16%, rheological agent 4%.
[0055] The longevity masterbatch is composed of the following components, each component in weight percentage: dripping agent 20%; ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
elongation at break
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a three-layer co-extruded high-heat-preservation light-conversion PO film, and belongs to the field of agricultural greenhouse films. According to the invention, on the basis of a previous product, ethylene-vinyl acetate copolymer (EVA) is added into metallocene polyethylene (mPE), a light-conversion master batch is added into a middle layer, the formulas of an outer layer,the middle layer and an inner layer are different, the formulas of the outer layer, the middle layer and the inner layer are mixed uniformly respectively, master batches are prepared by using a two-thread worm double-screw extruder, a three-layer film extrusion is formed through a co-extrusion die head to prepare a PO agricultural greenhouse film, and water-based dripping fog-eliminating coatingliquid is coated outside the PO film. The film is anti-aging and free of fog drops, and excellent in puncture resistance and has a service life of 3 years or more. After inspection and testing by an authoritative department, all quality and technical indexes reach or exceed a national standard, some of which are more than twice as good as the national standard. The PO film is good in light-conversion effect, has a light conversion rate reaching 13% or more, is very beneficial to the growth of crops and shortens the growth period of the crops at the same time.
Description
Technical field [0001] The invention relates to a PO film and a preparation process thereof, in particular to the preparation of a PO film using high-grade olefin raw materials and other auxiliary agents as raw materials, and belongs to the field of agricultural greenhouse films. Background technique [0002] PO film (agricultural greenhouse film) is an agricultural composite layer greenhouse film. The first is a new type of multi-layer high-grade functional polyolefin agricultural greenhouse produced by using high-grade olefin raw materials and other additives in Japan and drying after spraying. membrane. [0003] PO film is a new generation of agricultural greenhouse film. Since its introduction, PO film has been favored by the majority of growers with its excellent anti-fogging and dripping properties, high light transmittance, and high thermal insulation. The life of the greenhouse film is synchronized. In recent years, my country's agricultural film industry manufacturers ha...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more