Preparation method of nano-ntc thermosensitive material

A heat-sensitive material and nanotechnology, applied in the field of preparation of nano-NTC heat-sensitive materials, can solve the problems of inability to obtain dense nano-NTC heat-sensitive materials, complicated preparation methods, expensive equipment, etc. Effect of particle growth, high material constant

Active Publication Date: 2020-05-19
NINGXIA UNIVERSITY
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, nanonized NTC thermosensitive materials mostly appear in thin film materials, and thin film preparation methods such as evaporation method, magnetron sputtering method, pulse laser method and organic pyrolysis method, etc., these methods will inevitably bring in vacancies or interstitial atoms, As a result, there is no significant difference between the resistivity and material constants and the corresponding bulk materials, and its preparation method is complicated and the equipment is expensive
However, the traditional solid-state sintering method cannot obtain dense nano-NTC thermosensitive materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nano-ntc thermosensitive material
  • Preparation method of nano-ntc thermosensitive material
  • Preparation method of nano-ntc thermosensitive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] S1 nano powder preparation: 46.48ml concentration is 50% Mn (NO 3 ) 2 solution and 20.36g of Ni(NO 3 ) 2 ·6H 2 After O mixing, add deionized water until completely dissolved, then add 67.50g of citric acid, stir until completely dissolved, then add 18.59ml of ethylene glycol, mix well to obtain a transparent solution; then adjust the pH value of the transparent solution to 3 with ammonia water, Then put the transparent solution in a 70°C water bath to stir and evaporate the solvent to obtain a wet gel, then transfer the wet gel to an oven at 120°C until it is completely dried to obtain a dry gel, then place the dry gel on In the muffle furnace, the temperature was raised to 500°C at a rate of 2°C / min and kept for 1 hour to obtain a calcined powder. Add 95% ethanol to the calcined powder and put it in a ball mill for 1 hour, then put it in an oven at 100°C until completely drying to obtain nickel-manganese spinel powder.

[0025] S2 Tabletting: The obtained nickel-m...

Embodiment 2

[0029] S1 nano powder preparation: 46.48ml concentration is 50% Mn (NO 3 ) 2 solution and 20.36g of Ni(NO 3 ) 2 ·6H 2 After O mixing, add deionized water until completely dissolved, then add 67.50g of citric acid, stir until completely dissolved, then add 18.59ml of ethylene glycol, mix well to obtain a transparent solution; then adjust the pH value of the transparent solution to 3 with ammonia water, Then put the transparent solution in a 70°C water bath to stir and evaporate the solvent to obtain a wet gel, then transfer the wet gel to an oven at 120°C until it is completely dried to obtain a dry gel, then place the dry gel on In the muffle furnace, the temperature was raised to 500°C at a rate of 2°C / min and kept for 1 hour to obtain a calcined powder. Add 95% ethanol to the calcined powder and put it in a ball mill for 1 hour, then put it in an oven at 100°C until completely drying to obtain nickel-manganese spinel powder.

[0030] S2 Tabletting: The obtained nickel-m...

Embodiment 3

[0033] S1 nano powder preparation: 46.48ml concentration is 50% Mn (NO 3 ) 2 solution and 20.36g of Ni(NO 3 ) 2 ·6H 2 After O mixing, add deionized water until completely dissolved, then add 67.50g of citric acid, stir until completely dissolved, then add 18.59ml of ethylene glycol, mix well to obtain a transparent solution; then adjust the pH value of the transparent solution to 3 with ammonia water, Then put the transparent solution in a 70°C water bath to stir and evaporate the solvent to obtain a wet gel, then transfer the wet gel to an oven at 120°C until it is completely dried to obtain a dry gel, then place the dry gel on In the muffle furnace, the temperature was raised to 500°C at a rate of 2°C / min and kept for 1 hour to obtain a calcined powder. Add 95% ethanol to the calcined powder and put it in a ball mill for 1 hour, then put it in an oven at 100°C until completely drying to obtain nickel-manganese spinel powder.

[0034]S2 Tabletting: The obtained nickel-ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel method for preparing a nano NTC (Negative Temperature Coefficient) thermal-sensitive material. The novel method comprises the following steps: firstly, preparing nickel-manganese spinel powder of which the particle size is 50nm by using a sol-gel method; treating nano powder by using modes of tabletting and isostatic pressing so as to obtain a raw blank; sintering the raw blank for 0-60 seconds in a super-fast sintering furnace at 1000-1040 DEG C; further sintering for 5-20 hours in an air furnace at 850-950 DEG C, thereby finally obtaining the thermal-sensitiveNTC material of which the particle size is smaller than 500nm. The thermal-sensitive material has relatively high resistance and material constants.

Description

technical field [0001] The invention relates to the technical field of preparation of negative temperature coefficient (NTC) thermosensitive materials, in particular to a preparation method of nanometer NTC thermosensitive materials. Background technique [0002] NTC thermal temperature sensor is widely used in temperature measurement, temperature alarm, temperature compensation, suppression of surge current and other fields. It is currently a temperature sensor with a wide range of applications, the highest sensitivity and low cost. Appropriate room temperature resistivity and high material constant are important development directions of NTC thermosensitive materials, and nanometerization is an effective method to improve material constant. [0003] At present, nanonized NTC thermosensitive materials mostly appear in thin film materials, and thin film preparation methods such as evaporation method, magnetron sputtering method, pulse laser method and organic pyrolysis metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/01C04B35/624
CPCC04B35/01C04B35/624C04B2235/602C04B2235/6562C04B2235/6567C04B2235/661
Inventor 梁森崔苗苗张笑袁羽李海波高忙忙
Owner NINGXIA UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com