Manufacturing process for carbon fiber composite forming membrane disk

A composite material and manufacturing process technology, which is applied in the field of carbon fiber composite material forming membrane disc manufacturing process, can solve the problems of strong wear resistance, high strength, and inability to produce quality, and achieve good corrosion resistance, fatigue resistance, and The effect of small thermal expansion coefficient

Inactive Publication Date: 2018-05-11
刘长喜
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to clarify a carbon fiber composite material forming membrane disk manufacturing process, in order to solve the problem in the prior art that carbon fiber composite materials cannot be used to manufacture light weight, high strength, and strong wear-resistant membrane disks, and then provide a Manufacture process of carbon fiber composite molded membrane disc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process for carbon fiber composite forming membrane disk
  • Manufacturing process for carbon fiber composite forming membrane disk
  • Manufacturing process for carbon fiber composite forming membrane disk

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0023] The manufacturing process of the carbon fiber composite material forming membrane disc of the present embodiment, this kind of carbon fiber composite material forming membrane disc manufacturing process, it relates to the cutting method of the resin-based carbon fiber prepreg cloth, that is, firstly, the rolled prepreg cloth is assembled on the material rack First, limit and fix the edge of the prepreg and the position calibration mechanical structure, use a vibrating cutter to cut the prepreg into multiple prepregs of specified size, collect the cut prepregs, and repeat the above steps Until all the prepregs are cut.

[0024] The prepreg prepared by the cutting method of the resin-based carbon fiber prepreg has uniform thickness and precise size, which significantly improves the compactness, uniformity and dimensional accuracy of the product.

[0025] The manufacturing process of the carbon fiber composite molded film disk involves a preheating processing method, that ...

specific Embodiment approach 2

[0038] The difference from Embodiment 1 is that in the manufacturing process of the carbon fiber composite material forming membrane disc in this embodiment, the cutting is carried out according to the graphics drawn by the cutting machine as described in step 1, and the above steps are repeated until all the prepregs are cut. In the process, the prepreg is cut by the cutting method of the vibrating cutting knife of the coordinate cutting machine.

specific Embodiment approach 3

[0039] The difference from Embodiment 1 or Embodiment 2 is that, in the manufacturing process of the carbon fiber composite material molding disc of this embodiment, when using the heating device in step 2 to preheat and heat the prepreg obtained by cutting the prepreg in step 1, the The heating device is a digital heating platform device.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Longitudinal tensile strengthaaaaaaaaaa
Transverse tensile strengthaaaaaaaaaa
Shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process for a carbon fiber composite forming membrane disk. The manufacturing process comprises the steps that a prepreg is slit into a prepreg body in a certain shape and angle; a mold is cleaned and coated with a mold releasing agent; a heating platform is used for carrying out preheating treatment on the cut prepreg body; the prepreg body is laid to forma carbon fiber composite layer in a regular shape; a vacuum membrane bag is used for carrying out sealing treatment, and vacuumizing is carried out to form negative pressure; an oven is used for heating and solidifying the carbon fiber composite layer; the cooled carbon fiber composite layer is separated from the mold; the carbon fiber composite layer is cut and polished, and a finished product ofthe carbon fiber composite forming membrane disk is obtained. The membrane disk manufactured through the method has high-content fiber, the surface is bright without bubbles, the interlayer bonding intensity achieves an effect of a compression molding process, and the requirement for carbon fiber composite product production in the fields of aerospace and navigation.

Description

Technical field: [0001] The invention relates to a manufacturing process of a carbon fiber composite material forming membrane disc, in particular to a closed mold internal pressure forming process of a prepreg carbon fiber composite material. Background technique: [0002] Resin-based carbon fiber reinforced phase composite material is lighter than metal aluminum, but its strength is higher than steel, and it has the characteristics of corrosion resistance and high modulus. With many excellent properties, carbon fiber has high axial strength and modulus, low density, high specific performance, no creep, ultra-high temperature resistance in non-oxidizing environment, good fatigue resistance, specific heat and electrical conductivity between non-metal and metal Among them, the coefficient of thermal expansion is small and anisotropic, with good corrosion resistance and good ray transparency. Good electrical and thermal conductivity, good electromagnetic shielding, etc. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C70/34B29C70/54
CPCB29C70/345B29C70/545
Inventor 刘长喜
Owner 刘长喜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products