Preparation method of sulfydryl carbon nano-tube micro-sphere conductive adhesives for liquid-crystal display circuits

A carbon nanotube microsphere and liquid crystal display technology, applied in the field of conductive adhesive, can solve the problems of complex preparation process, high environmental pollution, and high content of conductive fillers, avoiding excessively high content, excellent conductive performance, and simple and easy-to-control process. Effect

Inactive Publication Date: 2018-04-27
CHENDU NEW KELI CHEM SCI CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Aiming at the defect that the bonding force between the carbon material and the metal interface is insufficient, pores and bubbles are easily generated, and bonding failure is easily caused when the composite structure is loaded, the present invention grafts mercapto groups on carbon nanotubes, and utilizes mercapto groups to form stronger bonds with the metal surface. Therefore, the adhesiveness of the prepared conductive adhesive has been greatly improved, and at the same time, it overcomes the shortcomings of the traditional conductive adhesive, such as excessively high content of conductive filler, high price, complicated preparation process, and high environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of sulfydryl carbon nano-tube micro-sphere conductive adhesives for liquid-crystal display circuits
  • Preparation method of sulfydryl carbon nano-tube micro-sphere conductive adhesives for liquid-crystal display circuits

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) The ratio of parts by mass is 5 : 0.01: 0.05 : 100, taking styrene monomer, azobisisobutyronitrile initiator, chloroform and solvent ethanol, and reacting at 90°C for 5 hours to prepare a polymer micro Balls, the particle size of the polymer microspheres is 6 μm;

[0035] (2) Using single-walled carbon nanotubes with a diameter of 40 nm and a purity greater than 97% as raw materials, the original carbon nanotubes were added to H 2 SO 4 :HNO 3 =3:1 in the mixed acid, the mass ratio of the carbon nanotubes to the mixed acid was 1:180, ultrasonically dispersed for 30 min, placed on a constant temperature magnetic stirrer and stirred at 80 °C for 30 min; then the treated carbon The nanotubes are added to a large amount of deionized water to cool, centrifuged, and repeatedly sucked to neutrality, and vacuum dried to obtain carbon dioxide nanotubes. Weigh the raw materials according to the mass ratio of oxidized carbon nanotubes, 3-mercaptopropyltrimethoxysilane and di...

Embodiment 2

[0040] (1) The ratio of parts by mass is 30 : 0.2 : 0.15 : 100, taking styrene monomer, azobisisobutyronitrile initiator, mercaptoethanol and solvent ethanol, and reacting at 65°C for 18 hours to prepare a polymer Microspheres, the polymer microspheres have a particle size of 4 μm;

[0041] (2) Using multi-walled carbon nanotubes with a diameter of 10 nm and a purity greater than 97% as raw materials, the original carbon nanotubes are added to the mixed acid of H2SO4:HNO3=3:1, and the mass ratio of the carbon nanotubes to the mixed acid is It was 1:190, ultrasonically dispersed for 30 min, placed on a constant temperature magnetic stirrer, and stirred at 80 °C for 30 min; then the treated carbon nanotubes were added to a large amount of deionized water to cool, centrifuged, and repeatedly sucked to medium properties, vacuum drying, prepared carbon dioxide nanotubes. Weigh the raw materials according to the mass ratio of oxidized multi-walled carbon nanotubes, 3-mercaptopropyl...

Embodiment 3

[0046] (1) The ratio of parts by mass is 15 : 0.5 : 3 : 100, taking styrene monomer, azobisisobutyronitrile initiator, mercaptoacetic acid and solvent ethanol, and reacting at 70°C for 12 hours to prepare a polymer Microspheres, the polymer microspheres have a particle size of 5 μm;

[0047] (2) Using single-wall carbon nanotubes and multi-wall carbon nanotubes with a diameter of 30 nm and a purity greater than 97% as raw materials, the original carbon nanotubes are added to the mixed acid of H2SO4:HNO3=3:1, and the carbon nanotubes The mass ratio of the tube to the mixed acid was 1:190, ultrasonically dispersed for 30 min, and placed on a constant temperature magnetic stirrer at 80 °C for 30 min under reflux; then the treated carbon nanotubes were added to a large amount of deionized water to cool, centrifuged, And repeated suction filtration to neutrality, and vacuum drying to obtain oxidized carbon nanotubes. Weigh the raw materials according to the mass ratio of oxidized ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of sulfydryl carbon nano-tube micro-sphere conductive adhesives for liquid-crystal display circuits. The method includes the steps: preparing monomers, initiating agents, dispersing agents and solvents into macro-molecular micro-spheres; preparing sulfydryl modified carbon nano-tubes; wrapping and growing the sulfydryl modified carbon nano-tubes on thesurfaces of the treated macro-molecular micro-spheres by a low-temperature plasma enhanced chemical vapor deposition method to prepare sulfydryl modified carbon nano-tube micro-spheres; dispersing thesulfydryl modified carbon nano-tube micro-spheres into acrylic resin adhesives comprising acrylic resin, curing agents, surface active agents and coupling agents; performing defoaming treatment to obtain the sulfydryl modified carbon nano-tube micro-sphere conductive adhesives. According to the method, sulfydryl is grafted on the carbon nano-tubes, the sulfydryl and a lot of metal generate strongresultant force, so that the cohesiveness of prepared conductive adhesives is greatly improved, and the method overcomes the shortcomings that conductive fillers in tradition conductive adhesives arehigh in content, high in prices, complicated in preparation process, high in environmental pollution and the like.

Description

technical field [0001] The invention relates to the field of conductive adhesives, in particular to a method for preparing a mercapto carbon nanotube microsphere conductive adhesive for liquid crystal display circuits. Background technique [0002] With the rapid development of the world's information and communication industries, display devices are becoming more and more important as the key components of human-machine dialogue. Thin film transistor-liquid crystal displays (TFT-LCDs) make The technology of fine processing of microelectronics is transplanted to the processing of thin film transistor (TFT) array on large area glass, and then the array substrate and another substrate with color filter film are used with the mature liquid crystal display (LCD) Technology to form a liquid crystal cell, and then go through post-processing such as polarizer coating and other processes, and finally form a liquid crystal display device. The FPD (flat panel display) industry with T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/04C09J9/02C08F112/08
CPCC08F112/08C08K2201/011C08L2203/20C08L2205/18C09J9/02C09J133/04C08L25/06C08K9/06C08K9/02C08K7/24
Inventor 陈庆司文彬
Owner CHENDU NEW KELI CHEM SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com