A treatment process and thermal spraying technology, applied in the direction of metal material coating process, coating, anti-corrosion coating, etc., can solve the problems of unreasonable combination of process steps, affecting the effect of spraying treatment, low bonding strength, etc., to achieve enhanced protection effect, Improved effect and good mechanical quality

Inactive Publication Date: 2018-04-13
马鞍山市宝奕金属制品工贸有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing thermal spraying treatment process is relatively rough, and the combination of process steps is unreasonable, resulting in low bonding strength between the thermal spraying coating and the metal substrate, and long-term use will cause problems such as interface cracking or even falling off, which in turn affects The effect of spraying treatment, this problem needs to be solved and improved by those skilled in the art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A thermal spraying treatment process, comprising the steps of:

[0026] (1) Metal surface pretreatment:

[0027] Put the metal into the chemical degreasing solution and soak for 10 minutes, take it out, put it into the nitric acid solution for 3 minutes, and finally take it out and rinse it with deionized water for later use;

[0028] (2) Coating treatment:

[0029] When the metal surface treated in step (1) is completely dry, use the pre-prepared sealing treatment agent to coat the metal surface, put it into the drying box for drying treatment after completion, and finally take it out for use; The sealing treatment agent is composed of the following parts by weight: 45 parts of silicone resin, 7 parts of titanium carbide, 4 parts of polyvinyl alcohol, 1 part of nonylphenol polyoxyethylene ether, 0.1 part of magnesium sulfate, 0.1 part of zinc chloride, 2 parts Methylcellulose, 0.2 parts of disodium edetate;

[0030] (3) Thermal spraying treatment:

[0031] Perform ...

Embodiment 2

[0040] A thermal spraying treatment process, comprising the steps of:

[0041] (1) Metal surface pretreatment:

[0042] First put the metal into the chemical degreasing solution for 13 minutes, then take it out and then put it into the nitric acid solution for 4 minutes, and finally take it out and rinse it with deionized water for later use;

[0043] (2) Coating treatment:

[0044] When the metal surface treated in step (1) is completely dry, use the pre-prepared sealing treatment agent to coat the metal surface, put it into the drying box for drying treatment after completion, and finally take it out for use; The sealing treatment agent is composed of the following parts by weight: 48 parts of silicone resin, 9 parts of titanium carbide, 6 parts of polyvinyl alcohol, 1.5 parts of nonylphenol polyoxyethylene ether, 0.3 parts of magnesium sulfate, 0.15 parts of zinc chloride, 3 parts Methylcellulose, 0.4 parts of disodium edetate;

[0045] (3) Thermal spraying treatment:

...

Embodiment 3

[0055] A thermal spraying treatment process, comprising the steps of:

[0056] (1) Metal surface pretreatment:

[0057] First put the metal into the chemical degreasing solution for 15 minutes, then take it out and put it into the nitric acid solution for 5 minutes, and finally take it out and rinse it with deionized water for later use;

[0058] (2) Coating treatment:

[0059] When the metal surface treated in step (1) is completely dry, use the pre-prepared sealing treatment agent to coat the metal surface, put it into the drying box for drying treatment after completion, and finally take it out for use; The sealing treatment agent is composed of the following parts by weight: 50 parts of silicone resin, 10 parts of titanium carbide, 7 parts of polyvinyl alcohol, 2.5 parts of nonylphenol polyoxyethylene ether, 0.4 parts of magnesium sulfate, 0.2 parts of zinc chloride, 4 parts Methylcellulose, 0.5 parts of disodium edetate;

[0060] (3) Thermal spraying treatment:

[0061]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a thermal spraying treatment process. The thermal spraying treatment process comprises the following steps of (1) metal surface pretreatment, (2) coating treatment, (3) thermalspraying treatment and (4) cooling treatment. According to the thermal spraying treatment process, thermal spraying treatment processes are reasonably improved and adjusted, the thermal spraying treatment effect is improved, a thermal spraying coating which is compact in structure, good in mechanical quality and high in abrasion resistance and corrosion resistance is formed on the surface of a metal matrix, the protection effect on metal is improved, the service life of metal is prolonged, and the thermal spraying treatment process has application and popularizing value.

Description

technical field [0001] The invention belongs to the technical field of metal processing, and in particular relates to a thermal spraying process. Background technique [0002] Metal materials are common and essential materials in people's lives, including iron, steel, aluminum and their alloys. Usually, the surface properties of metal materials are relatively active, and corrosion and other adverse phenomena are prone to occur under natural conditions, which in turn affects their quality and life. Therefore, it is necessary to modify the surface. The thermal spraying treatment method is a common metal surface treatment process, which can form a thermal spray coating on the metal surface to enhance the protection of the metal material, thereby improving its service quality and life. However, the existing thermal spraying treatment process is relatively rough, and the combination of process steps is unreasonable, resulting in low bonding strength between the thermal spraying ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C4/10C23C4/02C09D183/04C09D7/61C09D7/63C09D7/65C09D1/00C09D5/08
CPCC08K2003/168C08K2003/3063C08L2205/035C09D1/00C09D5/08C09D183/04C23C4/02C23C4/10C08L29/04C08L71/02C08L1/28C08K13/02C08K3/14C08K3/30C08K3/16C08K5/175
Inventor 孙军海
Owner 马鞍山市宝奕金属制品工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap