A method of manufacturing a high wear-resistant slurry nozzle

A manufacturing method and high wear-resistant technology, which are applied in the manufacturing field of high wear-resistant slurry nozzles, can solve the problems of the deterioration of the working condition of the combustion furnace of the base material, the poor mechanical processing technology, and the unsatisfactory service life, and achieve the mechanical processing technology. Good, long service life, high economic and social benefits

Active Publication Date: 2019-04-16
ZHEJIANG JINJU CHEM
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. It is made of high-performance integral materials, which has poor machining process, difficult welding, high cost and unsatisfactory service life;
[0004] 2. Due to the limitation of the thickness of the coating layer of the nozzle using the surface coating technology, once the coating layer is worn out, the rapid wear of the base material will quickly deteriorate the working conditions of the combustion furnace (the nozzles of some domestic enterprises using this technology have been exposed the seriousness of the problem);
[0005] 3. The nozzle made by the cemented carbide ring inserting method has serious problems of cracking or partial cracking of the cemented carbide ring during use.
[0006] To sum up the current situation, it can be seen that the existing manufacturing methods have obvious problems in terms of economy, safety of use and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] A method for manufacturing a high wear-resistant slurry nozzle of the present invention comprises the following steps:

[0037] (1) Blanking processing:

[0038] According to the design size, the raw material is cut into nozzle embryos, and then the shape of the nozzle embryo is processed by a lathe until the shape of the nozzle embryo reaches the design size, and then the nozzle embryo is drilled according to the design drawing to ensure that the inner hole diameter of the nozzle is larger than the design size 2mm , reserve a size of 2mm, which is convenient for actual processing, and prevents the subsequent manufacturing process of the nozzle from being deformed to form "under-embryo", resulting in material scrapping, and in processing, ensure that the chamfer at the bottom of the nozzle is greater than R3, and the groove of the nozzle The angle is greater than 135°, which facilitates the subsequent cladding treatment, prevents problems such as cracks due to incomplet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a high abrasion-resistant slurry nozzle. The manufacturing method comprises the following steps of (1) blanking processing, (2) laser cladding, specifically, laser cladding comprises (1) nozzle external surface treatment and (2) nozzle internal hole treatment, (3) nozzle finishing, specifically, nozzle finishing comprises (1) nozzle external surface treatment and (2) nozzle internal hole treatment, (4) nozzle checking, and (5) nozzle assembly assembling. According to the technical scheme of the manufacturing method of the high abrasion-resistant slurry nozzle, the unique manufacturing method is adopted, through a laser cladding technology and based on the advantage that combination of abrasion-resistant materials formulas is convenient, thefact that an easy-to-process high temperature-resistant material matrix is clad with a cladding layer with good high temperature resistance and excellent abrasion resistance in the process of nozzlemanufacturing is achieved, so that the abrasion resistance of a nozzle internal hole is better, the service life of the nozzle is prolonged, the foundation is laid for safety, economy and long periodstability of a device, and the economic benefit is improved.

Description

technical field [0001] The invention relates to a manufacturing method of a high wear-resistant slurry nozzle. Background technique [0002] The coal-water slurry nozzle (burner) is the key equipment of the coal-water slurry gasification device, and the slurry nozzle is the core component of the equipment. Its service life determines the safe, stable and long-term operation of the entire device, and determines the Therefore, improving the wear resistance of the slurry nozzle is a long-term research topic of research institutes and nozzle manufacturers at home and abroad. The methods currently used generally include: improving the high-temperature wear resistance of the material of the nozzle part; using surface wear-resistant coating technology for the working part of the nozzle; using cemented carbide inserts and other methods to prolong the service life. At present, the problems existing in the manufacturing methods of various injection combustion nozzles are as follows: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/16
CPCB23P15/16
Inventor 叶延寿赖颖峰邹芹芹翁子清金胜荣
Owner ZHEJIANG JINJU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products