Production process of high-strength plastic decorative plate

A high-strength plastic and production process technology, applied in the field of plastic processing, can solve problems such as cold material spots, silver streaks, air marks, unstable injection molding process, and unstable product quality, so as to reduce the defective rate and mix raw materials evenly Thorough, long-lasting effect

Inactive Publication Date: 2018-04-03
SUZHOU NIUDONG PRECISION MFG TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the plastic decorative board is the most widely used. When the usual plastic decorative board is processed, some are formed by extrusion, and some are formed by injection molding. Usually, it is easy to appear at the nozzle (glue point) during injection molding. Cold material Spots, silver streaks, air marks, and other appearance defects. The injection molding process cannot be stabilized, the product quality is unstable and the production efficiency is low, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The production process of the high-strength plastic decorative panel of the present embodiment comprises the following steps:

[0024] (1) Ingredients: The mass percentage of each component in the plastic of the plastic decorative board is: 3.14% epoxy resin, 2.55% polyvinyl chloride resin, 1.45% plasticizer, 1.17% anti-ultraviolet agent, 1.51% bone char, and the balance is phenolic resin . ;

[0025] (2) After mixing the raw materials according to the mass percentage, cleaning and crushing are carried out;

[0026] (3) Drying the raw materials, the drying temperature is 80-100°C, and the drying time is 4-6 hours;

[0027] (iv) Add the dried raw materials into the injection molding machine to complete the injection molding of the product;

[0028] (5) Cooling: Use cooling water to cool the mold, the temperature of the cooling water is 5-6°C, the flow rate is 0.4-0.5m / s, and the mold is cooled to room temperature;

[0029] (vi) Demolding: After cooling the mold, the ...

Embodiment 2

[0035] The production process of the high-strength plastic decorative panel of the present embodiment comprises the following steps:

[0036] (1) Ingredients: 3.68% epoxy resin, 2.62% polyvinyl chloride resin, 1.66% plasticizer, 1.38% anti-ultraviolet agent, 2.65% bone charcoal, and the balance is phenolic resin;

[0037] (2) After mixing the raw materials according to the mass percentage, cleaning and crushing are carried out;

[0038] (3) Drying the raw materials, the drying temperature is 80-100°C, and the drying time is 4-6 hours;

[0039] (iv) Add the dried raw materials into the injection molding machine to complete the injection molding of the product;

[0040] (5) Cooling: Use cooling water to cool the mold, the temperature of the cooling water is 5-6°C, the flow rate is 0.4-0.5m / s, and the mold is cooled to room temperature;

[0041] (vi) Demolding: After cooling the mold, the injection-molded plastic plate is separated from the mold;

[0042] (vii) Place a layer o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of a high-strength plastic decorative plate, and belongs to the technical field of plastic processing. The production process of the high-strength plasticdecorative plate comprises the following steps: (1) preparing raw materials; (2) mixing the raw materials according to mass percentage, cleaning and pulverizing; (3) performing drying treatment on the raw materials; (4) adding the dried raw materials into an injection molding machine to complete injection molding of a product; (5) cooling; (6) demoulding; (7) putting one layer of steel wire net in the middle of two layers of plastic plates and performing adhesion through adhesive; (8) cutting the plastic plate after adhesion, and mounting an aluminum alloy frame at the periphery of the cut plastic plate; (9) electroplating a pure aluminum plating layer; and (10) guaranteeing the high-strength plastic decorative plate to enter a storage. The high-strength plastic decorative plate has excellent high-pressure resistance due to scientific component proportion, has excellent corrosion resistance and heat resistance, and has long service life. One layer of steel wire net is placed in the middle of the two layers of plastic plates to perform adhesion, so the mechanical strength of the high-strength plastic decorative plate is greatly enhanced.

Description

technical field [0001] The invention relates to a production process of a high-strength plastic decorative board, belonging to the technical field of plastic processing. Background technique [0002] There are many kinds of decorative materials, including stainless steel decorative materials, plastic decorative materials, and composite board decorative panels, each of which has its own characteristics. Among them, the plastic decorative board is the most widely used. When the usual plastic decorative board is processed, some are formed by extrusion, and some are formed by injection molding. Usually, it is easy to appear at the nozzle (glue point) during injection molding. Cold material Spots, silver streaks, air marks, and other appearance defects. The injection molding process cannot be stabilized, the product quality is unstable, the production efficiency is low, and the cost is high. Contents of the invention [0003] The technical problem to be solved by the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/06C08L63/00C08L27/06C08K3/32
CPCC08L61/06C08L2205/03C08L63/00C08L27/06C08K3/32
Inventor 冉宏敏
Owner SUZHOU NIUDONG PRECISION MFG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com