Method for producing desulfurization and denitrification hollow activated carbon

A production method, desulfurization and denitrification technology, applied in separation methods, chemical instruments and methods, inorganic chemistry, etc., can solve problems such as uneven activation inside and outside, high cost of use, unstable indicators, etc., and achieve good market application value and save energy. The effect of resource and adsorption index stabilization

Active Publication Date: 2018-03-27
SHANXI XINHUA CHEM
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a new production method of desulfurization and denitrification activated carbon, which solves the problems of uneven activation inside and outside of the traditional desulfurization and denitrification activated carbon, high stacking weight, unstable index and high cost of use, and is used for dry desulfurization. Denitrification and impregnation field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing desulfurization and denitrification hollow activated carbon
  • Method for producing desulfurization and denitrification hollow activated carbon
  • Method for producing desulfurization and denitrification hollow activated carbon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A method for producing hollow activated carbon for desulfurization and denitrification, comprising the steps of:

[0034] (1) Grinding: put bituminous coal, coking coal, coke powder, and asphalt into the pulverizer in a weight ratio of 30:30:25:10 for grinding, and the particle size requires 325 mesh and 70% pass;

[0035] (2) Mixing: Mix the ground carbon powder, coal tar, and water in a weight ratio of 80:10:15, and the mixing temperature is 35°C to 40°C;

[0036] (3) Granulation: add the mixture into the mold to make hollow activated carbon raw material, the outer diameter of the hollow activated carbon raw material is 9.0-10.0mm, and the inner diameter is 2-3mm; then the hollow activated carbon raw material is cut into the required length by a cutter as pellets;

[0037] (4) Drying: The granulated material is dried in a dryer at a drying temperature of 90°C~95°C;

[0038] (5) Carbonization: Put the dry material into the converter for carbonization, the temperature...

Embodiment 2

[0043] A method for producing hollow activated carbon for desulfurization and denitrification, comprising the steps of:

[0044] (1) Grinding: put bituminous coal, coking coal, coke powder, and asphalt into the pulverizer at a weight ratio of 35:20:20:15, and the particle size is required to be 325 mesh and 70% pass;

[0045] (2) Mixing: Mix the ground carbon powder, coal tar, and water in a weight ratio of 80:12:10, and the mixing temperature is 45°C to 50°C;

[0046] (3) Granulation: add the mixture into the mold to make hollow activated carbon raw material, the outer diameter of the hollow activated carbon raw material is 9.0-10.0mm, and the inner diameter is 2-3mm; then the hollow activated carbon raw material is cut into the required length by a cutter as pellets;

[0047] (4) Drying: The granulated material is dried in a dryer at a drying temperature of 95°C~100°C;

[0048] (5) Carbonization: Put the dry material into the converter for carbonization, the temperature is...

Embodiment 3

[0053] A method for producing hollow activated carbon for desulfurization and denitrification, comprising the steps of:

[0054] (1) Grinding: put bituminous coal, coking coal, coke powder, and asphalt into the pulverizer in a weight ratio of 40:25:15:12 for grinding, and the particle size requires 325 mesh and 70% pass;

[0055] (2) Mixing: Mix the ground carbon powder, coal tar, and water in a weight ratio of 80:15:12, and the mixing temperature is 40°C to 45°C;

[0056] (3) Granulation: Add the mixture into the mold to make hollow activated carbon raw materials. The outer diameter of the hollow activated carbon raw material is 9.0-10.0mm, and the inner diameter is 2-3mm; then the hollow activated carbon raw material is cut into the required length by a cutter as pellets;

[0057] (4) Drying: The granulated material is dried in a dryer at a drying temperature of 100°C~110°C;

[0058] (5) Carbonization: Put the dry material into the converter for carbonization, the temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Outer diameteraaaaaaaaaa
The inside diameter ofaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing desulfurization and denitrification hollow activated carbon. The method comprises the following steps: (1) grinding, namely grinding soft coal, coking coal, coke powder and asphalt in a weight ratio of (30-40):(20-30):(15-25):(10-15) in a grinding machine till 70% of the raw materials with granularity of 325 meshes can pass; (2) mixing, namely mixingthe grinded carbon powder, coal tar and water in a weight ratio of 80:(10-15):(10-15) at 35-50 DEG C; and (3) pelletizing, namely pelletizing the mixed material in a pelletizing machine, wherein the diameter of the pelletized material is 9.0-10.0mm, and the inner diameter of the pelletized material is 2-3mm. The method disclosed by the invention is reasonable in design, and compared with conventional desulfurization and denitrification activated carbon, the desulfurization and denitrification hollow activated carbon produced by using the method has the advantages of being activated both insideand outside, light in piling weight, large in adsorption contact area, and the like, and has very good market application values.

Description

technical field [0001] The invention belongs to the field of activated carbon preparation, in particular to a production method of desulfurization and denitrification hollow activated carbon. Background technique [0002] Desulfurization and denitrification activated carbon is mainly used in the treatment of sintering flue gas in steel mills, power plants, cement plants, etc. It is mainly used to remove sulfur dioxide, nitrogen oxides, mercury, dioxins and dust in flue gas. The use of desulfurization and denitrification activated carbon is increasing year by year. In 2016, its use in the country has reached 100,000 tons. It is estimated that the market demand in 2017 will be around 120,000 tons. As the dry desulfurization and denitrification technology gradually matures, the application is more and more extensive, but there are certain problems. Because the desulfurization and denitrification activated carbon is a cylindrical solid carbon, the required carbonization temperat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B32/33B01D53/02
CPCB01D53/02B01D2253/102B01D2258/0283
Inventor 雷彭陈琪张会涛黄济民李怀珠张志军佟德刚李若梅
Owner SHANXI XINHUA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com