Environment-friendly and flame-retarding polydicyclopentadiene material and preparation method thereof

A polydicyclopentadiene, environmentally friendly technology, applied in the field of environmentally friendly flame-retardant polydicyclopentadiene materials and their preparation, can solve the problems affecting the mechanical and physical and chemical properties of polydicyclopentadiene, mechanical performance damage, safety hazards, etc. , to achieve the effects of close relationship, enhanced interface performance, and accelerated preparation speed

Inactive Publication Date: 2018-03-23
克琴新材料科技(上海)有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polydicyclopentadiene is composed of hydrocarbons containing unsaturated double bonds, which is very flammable, which limits its application in many fields such as electronic appliances and decorative materials.
[0003] In the existing technology, the flame retardant performance of polydicyclopentadiene is often achieved by adding a high proportion of flame retardants. However, it has been found that the addition of a high proportion of flame retardants will affect the mechanical and physical properties of polydicyclopentadiene. performance, when it is used in the automotive field or the aerospace industry, it will cause safety hazards due to the loss of its mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly and flame-retarding polydicyclopentadiene material and preparation method thereof
  • Environment-friendly and flame-retarding polydicyclopentadiene material and preparation method thereof
  • Environment-friendly and flame-retarding polydicyclopentadiene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The polydicyclopentadiene material 1# of the present embodiment is made of the following components by weight percentage:

[0050]

[0051] Prepare environment-friendly flame-retardant polydicyclopentadiene material 1# according to the following steps:

[0052] 1) Weigh 50% wt of dicyclopentadiene, aluminum hydroxide modified by a titanate coupling agent, Clariant’s Exolit series phosphate flame retardant, and kh550, and fully mix it as a dosage A;

[0053] 2) The remaining dicyclopentadiene, catalyst, 2,6-di-tert-butyl-4-methylphenol, tris(2,4-di-tert-butylphenyl) phosphite, UV-327, UV- 1157 is fully mixed to make dosage B;

[0054] 3) Add the mixed ingredients A and B to the two silos of the injection molding machine respectively, and adjust the rate ratio of suction to 4.3:1;

[0055] 4) After starting the injection molding machine, suck the two kinds of materials A and B into the injection gun head at the same time and mix them;

[0056] 5) Inject the mixed ma...

Embodiment 2

[0059] The polydicyclopentadiene material 2# of the present embodiment is made of the following components by weight percentage:

[0060]

[0061] Prepare environment-friendly flame-retardant polydicyclopentadiene material 2# according to the following steps:

[0062] 1) Weigh 50%wt of dicyclopentadiene, aluminum hydroxide modified by silane coupling agent, Clariant's Exolit series phosphate flame retardant, TMC-201 and fully mix it as material A;

[0063] 2) Fully mix the remaining dicyclopentadiene, catalyst, bis(3,5-di-tert-butyl-4-hydroxyphenyl) sulfide, UV-1164, UV-1157 to prepare material B;

[0064] 3) Add the mixed ingredients A and B to the two silos of the injection molding machine respectively, and adjust the rate ratio of suction to 4.3:1;

[0065] 4) After starting the injection molding machine, suck the two kinds of materials A and B into the injection gun head at the same time and mix them;

[0066] 5) Inject the mixed material into the mold (mold temperatu...

Embodiment 3

[0069] The polydicyclopentadiene material 3# of the present embodiment is made of the following components by weight percentage:

[0070]

[0071] Prepare environment-friendly flame-retardant polydicyclopentadiene material 3# according to the following steps:

[0072] 1) Weigh 40%wt of dicyclopentadiene, aluminum hydroxide modified by silane coupling agent, TMC-201, heat to 45°C and fully mix as dosage A;

[0073] 2) Weigh 40% wt of dicyclopentadiene, Clariant's Exolit series of phosphate flame retardants, and kh550 and mix them fully to prepare material B;

[0074] 3) Fully mix the remaining dicyclopentadiene, catalyst and other remaining components to make dosage C;

[0075] 4) After mixing material A and material B while they are hot, add material C and mix evenly and inject it into the mold;

[0076] 5) When the mold temperature is 50-80°C, hold the pressure for 1-2 minutes;

[0077] 6) Open the mold and remove the mold to obtain an environmentally friendly flame-ret...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an environment-friendly and flame-retarding polydicyclopentadiene material. The environment-friendly and flame-retarding polydicyclopentadiene material is characterized by beingprepared from the following components in percentage by weight: 75 percent to 85 percent of dicyclopentadiene, 0.01 percent to 1 percent of a catalyst, 10 percent to 22 percent of a flame retardant,0.2 percent to 5 percent of a coupling agent, 0.1 percent to 3 percent of an anti-ageing auxiliary agent and 0.1 percent to 3 percent of an ultraviolet absorbent, wherein the catalyst is selected fromone or more of ruthenium alkyidene carbine catalysts; the flame retardant is a compound mixture of modified aluminum hydroxide and / or modified magnesium hydroxide and one or more of flame retardantsincluding an organic silicon type flame retardant, a melamine phosphate, a phosphate type flame retardant and pentaerythritol. The environment-friendly polydicyclopentadiene material provided by the invention has good performance and has a good flame-retarding function.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an environment-friendly flame-retardant polydicyclopentadiene material and a preparation method thereof. Background technique [0002] Polydicyclopentadiene material has excellent physical and mechanical properties and good chemical properties, and its raw material dicyclopentadiene has a low viscosity (about 0.3Pa s), and can be quickly ring-opened and polymerized under the introduction of a little heat and a catalyst , the reaction rate is very fast, so dicyclopentadiene is particularly suitable for reaction injection molding (RIM), especially for the production of large structural parts. However, polydicyclopentadiene is composed of hydrocarbons containing unsaturated double bonds and is very flammable, which limits its application in many fields such as electronic appliances and decorative materials. [0003] In the existing technology, the flame retard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F132/08C08F4/70C08F2/44C08K9/06C08K9/04C08K3/22C08K5/521C08K5/053
Inventor 吴江张伟张冬杰叶书建
Owner 克琴新材料科技(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com