Halogen-free flame-retardant fiberglass-reinforced PA (Polyamide)/ASA (Acrylonitrile Styrene Acrylate Copolymer) composite material and preparation method thereof

A composite material and glass fiber technology, applied in the field of polymer materials, can solve the problems of insufficient low temperature and dry toughness, poor dimensional stability, poor weather resistance, etc., to reduce material shrinkage performance, good mechanical properties, improve compatibility effect

Inactive Publication Date: 2018-03-20
GUANGDONG JUHANG INST FOR ADVANCED MATERIALS CO LTD +2
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it has defects such as high water absorption, poor dimensional stability, insufficient toughness at low temperature and dry state, insufficient temperature resistance, and flammability in case of fire, which greatly limits its application in certain fields.
In recent years, ABS and PA blended alloys have attracted market attention. The addition of ABS can effectively improve the water absorption performance and notch toughness of PA. However, due to the existence of unsaturated double bonds in the molecular structure of ABS, the weather resistance of ABS / PA alloy materials Deterioration, prone to aging outdoors or under sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant fiberglass-reinforced PA (Polyamide)/ASA (Acrylonitrile Styrene Acrylate Copolymer) composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material is provided, the components and parts by mass of the halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material are as follows: polyamide: 30 wt. Parts; Graft copolymer of acrylate rubber body and acrylonitrile, styrene: 18 parts by weight; Flame retardant: 25 parts by weight; Compatibilizer: 4 parts by weight; Glass fiber: 18 parts by weight; Toughener: 5 parts by weight; nucleating agent: 0.1 parts by weight; lubricant: 0.1 parts by weight; antioxidant: 0.1 parts by weight.

[0029] The polyamide is PA6, and the relative ratio of the polyamide is 2.45.

[0030] The melt index of said ASA is 15g / 10min.

[0031] The flame retardant is compounded by organic hypophosphite, aluminum hypophosphite and ammonium polyphosphate APP.

[0032] The compatibilizer is a mixture of polystyrene-acrylonitrile-GMA copolymer SAG and ABS grafted maleic anhydride ABS-g-MAH.

[0033] The ...

Embodiment 2

[0044] A halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material is provided, the components and parts by weight of the halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material are as follows: polyamide: 45 wt. Graft copolymer of acrylate rubber body and acrylonitrile, styrene: 20 parts by weight; Flame retardant: 18 parts by weight; Compatibilizer: 3.5 parts by weight; Glass fiber: 20 parts by weight; Toughener: 5 parts by weight; nucleating agent: 0.1 parts by weight; lubricant: 0.1 parts by weight; antioxidant: 0.1 parts by weight.

[0045] The polyamide is PA66, and the relative viscosity of the polyamide is 2.8P·S.

[0046] The melt index of the graft copolymer of the acrylic rubber body, acrylonitrile and styrene is 20g / 10min.

[0047] The flame retardant is melamine cyanurate MCA.

[0048] The compatibilizer is a mixture of polystyrene-maleic anhydride copolymer SMA and polyethylene-methyl acrylate copolymer EMA.

[0049] ...

Embodiment 3

[0060] A halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material is provided, the components and parts by mass of the halogen-free flame-retardant, glass fiber-reinforced PA / ASA composite material are as follows: polyamide: 20 wt. Parts; Graft copolymer of acrylate rubber body and acrylonitrile, styrene: 30 parts by weight; Flame retardant: 15 parts by weight; Compatibilizer: 2 parts by weight; Glass fiber: 30 parts by weight; Toughener: 3 parts by weight; nucleating agent: 0.5 parts by weight; lubricant: 0.5 parts by weight; antioxidant: 0.5 parts by weight.

[0061] The polyamide is PA66, and the relative viscosity range of the polyamide is 2.6 P·S.

[0062] The melt index of the graft copolymer of the acrylic rubber, acrylonitrile and styrene is 18g / 10min.

[0063] The flame retardant is compounded by aluminum hypophosphite, ammonium polyphosphate APP and melamine cyanurate MCA.

[0064] The compatibilizer is a mixture of ABS grafted maleic anhydrid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a halogen-free flame-retardant fiberglass-reinforced PA (Polyamide) / ASA (Acrylonitrile Styrene Acrylate Copolymer) composite material. The halogen-free flame-retardant fiberglass-reinforced PA / ASA composite material is prepared from the following components in parts by weight: 20 to 65 parts of PA, 10 to 30 parts of an acrylonitile-styrene grafted acrylate rubber copolymer,10 to 25 parts of a flame retardant, 2 to 5 parts of a compatilizer, 10 to 30 parts of fiberglass, 3 to 8 parts of a toughening agent, 0.1 to 1 part of a nucleating agent, 0.1 to 1 part of a lubricating agent and 0.1 to 1 part of an antioxidant. According to the halogen-free flame-retardant fiberglass-reinforced PA / ASA composite material provided by the invention, compounding of the ASA and the PAis adopted, so that the water absorption performance of the PA is effectively improved, the material shrinkage performance is reduced, the size stability is remarkably improved, and meanwhile, good weather resistance and good aging resistance are given to the halogen-free flame-retardant fiberglass-reinforced PA / ASA composite material.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a halogen-free flame-retardant, glass fiber reinforced PA / ASA composite material and a preparation method thereof. Background technique [0002] Polyamide has become one of the top five engineering plastics due to its excellent mechanical strength, corrosion resistance, wear resistance and self-lubricating properties. Especially the glass fiber-reinforced and modified products are widely used in electric tools, automobile industry, machinery industry, sports equipment, office equipment and other fields. However, it has defects such as high water absorption, poor dimensional stability, insufficient toughness at low temperature and dry state, insufficient temperature resistance, and flammability in case of fire, which greatly limits its application in certain fields. In recent years, ABS and PA blended alloys have attracted market attention. The addition of ABS can effectively imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L51/04C08L55/02C08L51/06C08K13/06C08K9/06C08K7/14C08K3/34C08K5/134C08K5/526
CPCC08L51/04C08L77/00C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L2205/08C08L2205/24C08L55/02C08L51/06C08K13/06C08K9/06C08K7/14C08K3/34C08K5/1345C08K5/526
Inventor 杨金波陈旭东杨军明姚跃许宏武邓佳琪其他发明人请求不公开姓名
Owner GUANGDONG JUHANG INST FOR ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com