Low temperature resistant and high strength nylon and preparation method thereof

A high-strength, low-temperature-resistant technology, applied in the field of low-temperature-resistant high-strength nylon and its preparation, can solve the problems of poor toughness, brittleness, and reduced impact performance of nylon materials, so as to improve low-temperature strength, solve low-temperature brittleness, improve Effect of room temperature impact strength

Inactive Publication Date: 2018-03-06
昆山飞奔塑胶模具有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, nylon material has poor toughness, especially when used at low temperature, it is easy to become brittle. For materials with long-term use conditions below zero degrees Celsius, the low-temperature strength must be high. Specially modified nylon can be used at -30°C. Long-term use, and its impact performance is only slightly reduced, which can meet the long-term use requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature resistant and high strength nylon and preparation method thereof
  • Low temperature resistant and high strength nylon and preparation method thereof
  • Low temperature resistant and high strength nylon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A low-temperature-resistant high-strength nylon, comprising the following components in parts by weight:

[0027]

[0028]

[0029] Among them, the toughening agent is ordinary EPDM and grafted EPDM; the auxiliary agent includes a mixture of heat stabilizer CIPNOX 1098, color stabilizer IRGAFOX 168, silicone lubricant GM-100A and dispersant EBS.

Embodiment 2

[0031] A low-temperature-resistant high-strength nylon, comprising the following components in parts by weight:

[0032]

[0033] Among them, the toughening agent is ordinary EPDM and grafted EPDM; the auxiliary agent includes a mixture of heat stabilizer CIPNOX 1098, color stabilizer IRGAFOX 168, silicone lubricant GM-100A and dispersant EBS.

[0034] The product material performance table of table 1 comparative example and embodiment 1 and embodiment 2

[0035] Performance

[0036] Wherein, comparative example is the PA66 / PA6 of common EPDM toughening, and embodiment 1 and embodiment 2 are the PA66 / PA6 of grafting EPDM toughening.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low temperature resistant and high strength nylon, which comprises the following components by weight: 40-60 parts of PA6; 10-20 parts of PA66; and 10-30 parts of a toughening agent. Specifically, when the total mass of PA6, PA66 and the toughening agent is 100 mass parts, 0.1-0.8 part of an assistant and 0-2 parts of toner are additionally added, PBT, glass fiber, inorganic filler, a flame retardant and a synergistic flame retardant are 100 mass parts totally, and the assistant and toner are added in an additional way. The low temperature resistant toughening agent adopted by the invention is grafted EPDM, and the impact strength retention rate is 85% or above under a condition of minus 30DEG C.

Description

technical field [0001] The invention relates to a low-temperature-resistant high-strength nylon and a preparation method thereof. Background technique [0002] Nylon is one of the earliest developed engineering plastics. It has the advantages of high mechanical strength, good toughness, fatigue resistance, self-lubrication, small friction coefficient, wear resistance, heat resistance (long-term use within 100°C), easy modification and molding, etc. , has good comprehensive performance and wide application. However, nylon material has poor toughness, especially when used at low temperature, it is easy to become brittle. For materials with long-term use conditions below zero degrees Celsius, the low-temperature strength must be high. Specially modified nylon can be used at -30°C. Long-term use, and its impact performance is only slightly reduced, which can meet the long-term use requirements. Contents of the invention [0003] The technical problem to be solved by the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08L23/16C08L51/04C08L83/04C08K5/526C08K5/20
CPCC08L77/02C08K2201/014C08L2205/02C08L2205/035C08L2205/06C08L77/06C08L23/16C08L51/04C08L83/04C08K5/526C08K5/20
Inventor 邓德权甘明亮
Owner 昆山飞奔塑胶模具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com