Modification agent and modification treatment method for special cast aluminum alloy for IC equipment
A technology for casting aluminum alloy and modification treatment, which is applied in the field of modification agent, which can solve the problems of inconvenient multiple modification treatment, long residence time of molten aluminum, deterioration and recession of castings, etc., to achieve long duration of modification, reduce the number of repeated modification treatments, delay The effect of metamorphic decay
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] Example 1: Preparation of modifier
Embodiment 1-1
[0041] Preparation of modifier A: The raw materials used are based on weight percentages, including 63.6% aluminum-cerium alloy powder (with Ce content of 55% and the balance being Al), 12% aluminum-strontium alloy powder (with Sr content being 25% and the balance Is Al), 4.5% electrolytic manganese powder (purity of 99.9%), 10% metal Bi powder (purity of 99.9%) and 9.9% metal Al powder (A00) are mixed uniformly, and pressed into a cylinder of Φ10×10mm on the briquetting machine Shaped particles to obtain modifier A;
[0042] Preparation of modifier B: The raw materials used are based on weight percentages of 22% NaCl, 22% KCl, 45% NaF, 6% SrCO 3 , 3%K 2 TiF 6 And 2% BaCl 2 The mixture is uniformly mixed and compressed on a briquetting machine to form cylindrical particles with a diameter of 10×10 mm to obtain the modifier B.
Embodiment 1-2
[0044] Preparation of modifier A: The raw materials used are based on weight percentages, including 72.7% aluminum-cerium alloy powder (including 55% Ce content and Al), 10% aluminum-strontium alloy powder (including 25% Sr and the balance It is Al), 5% electrolytic manganese powder (purity of 99.9%), 8% metal Bi powder and 4.3% metal Al powder (A00) (purity 99.9%) mixed uniformly, and pressed into a cylinder of Φ10×10mm on the briquetting machine Shaped particles to obtain modifier A;
[0045] Preparation of modifier B: The raw materials used are calculated by weight percentages, 20% NaCl, 23% KCl, 46.5% NaF, 5% SrCO 3 , 4%K 2 TiF 6 And 1.5% BaCl 2 The mixture is uniformly mixed and compressed on a briquetting machine to form cylindrical particles with a diameter of 10×10 mm to obtain the modifier B.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com