High-weatherability BOPP release film and preparation method thereof

A technology of high weather resistance and release film, which is applied in the field of film manufacturing, can solve the problems of poor weather resistance of BOPP release film, and achieve the effects of reasonable and clear production process, balanced film materials, good weather resistance and mechanical properties

Inactive Publication Date: 2018-02-23
YANGZHOU ALVIN FILM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at the shortcomings of the existing BOPP release film such as poor weather resistance, and provides a high weather resistance BOPP release film and a preparation method thereof, which can obtain higher weather resistance without adding additional processing steps and processing costs. performance, can meet the use of high-demand occasions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below:

[0021] A BOPP release film with high weather resistance, which consists of the following components in parts by weight: 95 parts of BOPP, 5-8 parts of BOPP weather-resistant masterbatch, 2-6 parts of nano-silica, aminopropyltriethoxysilane 6-8 parts, 3-8 parts of butyl acrylate, 5-45 parts of methyl methacrylate, 1-2 parts of stearyl methacrylate, 10-20 parts of polyethylene glycol, 10-20 parts of ethanol, 20-30 parts of deionized water, 5-10 parts of natural latex, 0.3-0.5 parts of defoamer, and 0.3-0.5 parts of thickener.

[0022] A high weather resistance BOPP release film and a preparation method thereof, comprising the steps of:

[0023] (1) Preparation of BOPP weather-resistant masterbatch: Weigh the required raw materials according to the weight ratio;

[0024] (2) Put BOPP, weathering additives, antioxidants and auxiliary antioxidants into a high-speed mixer and stir for 10 minutes;

[0025] (3) Extrudi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A BOPP release film with high weather resistance and its preparation method belong to the field of film manufacturing technology. The production process of the present invention is reasonable and clear. The present invention adopts BOPP as the main component of the composite film, and adds BOPP weather-resistant masterbatch at the same time, so that the prepared The weather resistance of the release film is greatly enhanced, and nano-silica is added at the same time, which can improve the mechanical properties of the product and increase its tensile strength by about 150%. In this way, the prepared product is a kind of product with good weather resistance The release film with excellent performance and mechanical properties further expands the application range; it is also convenient for the next step to disperse the matrix and inorganic fillers evenly, and the components are mixed evenly, and the prepared film material is balanced, and natural latex is also added to enhance the viscosity and Flexibility, and finally add some auxiliary additives such as defoamers and thickeners, so that the prepared Harima material has more balanced and superior performance.

Description

technical field [0001] The invention belongs to the technical field of film manufacture, and relates to a method for preparing a release film, in particular to a high weather resistance BOPP release film and a preparation method thereof. Background technique [0002] Release film, also known as peeling film, isolation film, separation film, barrier film, release film, film, plastic film, hole masking film, silicone oil film, silicone oil paper, anti-adhesive film, slip film, Tianna paper, release film Paper, silliconfilm, releasefilm, release. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with silicon (silicone) release agent on the surface of the film material, such as PET, PE, OPP, BOPP, etc.; it can show extremely light and stable release force for various organic pressure-sensitive adhesives (such as hot-melt adhesives, acrylic adhesives and rubber-based pressure-sens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L71/02C08L7/02C08K13/02C08K3/36C08K5/544C08J3/22
CPCC08L23/12C08J3/226C08J2323/12C08K2201/011C08L2203/16C08L2205/025C08L2205/035C08L71/02C08L7/02C08K13/02C08K3/36C08K5/544
Inventor 李刚
Owner YANGZHOU ALVIN FILM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products