Preparation method for waterproof coiled polyvinyl chloride material

A polyvinyl chloride and waterproof membrane technology, applied in the field of waterproof membranes, can solve the problems of cancer induction, DOP toxicity, human poisoning, etc., and achieve the effects of improving environmental protection performance, simple preparation method, and reducing dosage

Inactive Publication Date: 2018-02-09
成都圻坊生物科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most of the existing PVC waterproof membranes contain DOP plasticizers. Studies have shown that DOP is toxic and prone to volatilization and migration. DOP can cause human poisoning and even cancer; EU countries have strongly restricted the application of DOP

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An environment-friendly polyvinyl chloride waterproof membrane, which mainly includes the following components in terms of parts by mass: PVC resin powder SG-3: 100 parts; CM: 10 parts; powdered nitrile rubber: 15 parts; silane coupling agent KH550: 1 parts; new plant-based environmentally friendly plasticizer ID37: 48 parts; calcium-zinc composite heat stabilizer: 7 parts; calcium carbonate: 30 parts; the powdered nitrile rubber contains 30 wt% of acrylonitrile.

[0033] Stir and blend PVC resin powder with functional small materials, fillers, and calcium-zinc composite heat stabilizer in a high-speed mixer. The temperature of the blend is lower than 85°C, and the stirring speed is 150 rpm; then stir at a low speed for 45 rpm / min, at 40°C, add an environmentally friendly plasticizer at 50 rpm and stir evenly; finally mix the elastic material CM and powder NBR at 55 rpm and add a coupling agent, stir and mix evenly to obtain the base material; through a twin-screw extru...

Embodiment 2

[0038]An environment-friendly polyvinyl chloride waterproof membrane, which mainly includes the following components in terms of parts by mass: PVC resin powder SG-5: 100 parts; CM: 10 parts; powdered nitrile rubber: 10 parts; silane coupling agent KH550: 1 parts; new plant-based environmentally friendly plasticizer ID37: 55 parts; calcium-zinc composite heat stabilizer: 7 parts; calcium carbonate: 30 parts; the powdered nitrile rubber contains 30 wt% of acrylonitrile.

[0039] Stir and blend PVC resin powder with functional small materials, fillers, and calcium-zinc composite heat stabilizer in a high-speed mixer. The temperature of the blend is lower than 85°C, and the stirring speed is 150 rpm; then stir at a low speed for 50 rpm / min, at 40°C, add an environmentally friendly plasticizer at 50 rpm and stir evenly; finally mix the elastic material CM and powder NBR at 60 rpm and add a coupling agent, stir and mix evenly to obtain the base material; through a twin-screw extrud...

Embodiment 3

[0044] An environment-friendly polyvinyl chloride waterproof membrane, which mainly includes the following components in terms of parts by mass: PVC resin powder SG-3: 100 parts; CM: 10 parts; superfine vulcanized powdered nitrile rubber: 20 parts; silane coupling agent KH550: 1 part; new plant-based environmental protection plasticizer ID37 and acetyl tri-n-butyl citrate according to the mass ratio of 1:2.5: 50 parts; calcium zinc composite heat stabilizer: 7 parts; calcium carbonate: 30 parts; The powdered nitrile rubber contains 26wt% acrylonitrile.

[0045] Stir and blend PVC resin powder with functional small materials, fillers, and calcium-zinc composite heat stabilizer in a high-speed mixer. The temperature of the blend is lower than 85°C, and the stirring speed is 150 rpm; then stir at a low speed for 50 rpm / min, at 40°C, add new plant-based environmentally friendly plasticizer ID37 and acetyl tri-n-butyl citrate and stir evenly at 60 rpm; finally mix elastic material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a waterproof coiled polyvinyl chloride material. The waterproof coiled polyvinyl chloride material is prepared through blending, granulation, cooling and shaping, and reeling successively. An environment-friendly plasticizer enhances the toughness of the coiled polyvinyl chloride material and allows the environment-friendly non-toxic coiled polyvinyl chloride material to be obtained; and the environment-friendly plasticizer used in a step A is one or more selected from a group consisting of tributyl citrate, dioctyl terephthalate, trioctyl trimellitate, the novel plant-based environment-friendly plasticizer ID37 and tri-n-butyl acetylacetate. According to the invention, through addition of an elastic material, the low temperature resistanceand the toughness of polyvinyl chloride are improved, the usage of the environment-friendly plasticizer is reduced, and the performance of the coiled polyvinyl chloride material is enhanced; a stirring speed is changed for different mixed materials to effectively keep the performance of the material, realize uniform mixing, control mixing temperature and reduce the performance loss of added materials.

Description

technical field [0001] The invention belongs to the technical field of waterproof coiled material, and in particular relates to a preparation method of polyvinyl chloride waterproof coiled material. Background technique [0002] With the development of the domestic economy and the rapid development of the construction industry, building waterproofing occupies a very important position in architectural design. Waterproofing engineering is an important subdivision of buildings. Layer waterproofing technology is to ensure that the building structure is free from water erosion, and the internal space A science and technology that is not damaged by water. The key to layer waterproofing lies in the quality of waterproof materials. At present, people's emphasis on the quality of building waterproof materials has changed from emphasizing economical cost to emphasizing environmental protection. [0003] The main types of new building waterproof membranes in my country are: asphalt m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L9/02C08K13/02C08K5/09C08K5/00C08K3/26C08K5/11C08K5/544
CPCC08L27/06C08K2003/265C08L2203/18C08L2205/035C08L23/286C08L9/02C08K13/02C08K5/09C08K5/0016C08K3/26C08K5/11C08K5/544
Inventor 张欢
Owner 成都圻坊生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap