Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High-strength plastic flooring and manufacture method thereof

A plastic floor, high-strength technology, used in the field of zinc oleate 2-3, plastic floor and its preparation, polyarylether ether nitrile 17-29, magnesium oleate, can solve the problem of low mechanical strength and cannot meet the market Demand and other issues, to achieve the effect of improving mechanical strength, high mechanical strength, and good wear resistance

Inactive Publication Date: 2018-01-23
JIANGYIN ZHIYUAN AUTOMOBILE DECORATION PARTS CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional plastic floor still has the disadvantage of low mechanical strength, which cannot meet the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength plastic flooring and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high-strength plastic floor made of the following raw materials by weight (kg): PVC resin 50, polyether thermoplastic polyurethane elastomer 24, dioctyl isophthalate 15, ultrafine alumina 10, graphene air condensation Glue 5, polyarylether ether nitrile 17, zinc oleate 2, magnesium oleate 1, palm wax 5, quartz powder 18, chloromethoxy fatty acid methyl ester 10, polyacrylonitrile-based carbon fiber 10.

[0015] A preparation method for a high-strength plastic floor, comprising the following steps:

[0016] (1) Add PVC resin, polyether-type thermoplastic polyurethane elastomer, polyarylether ether nitrile, polyacrylonitrile-based carbon fiber, dioctyl isophthalate, and dibasic lead phosphite into the high-speed mixer. Mix at -80°C for 10-12 minutes at high speed, then add zinc oleate, magnesium oleate, graphene airgel, ultrafine alumina, quartz powder, chloromethoxy fatty acid methyl ester and other raw materials in sequence, at 100-110 Stir at high speed for 4-75min ...

Embodiment 2

[0021] A high-strength plastic floor made of the following raw materials by weight (kg): PVC resin 60, polyether thermoplastic polyurethane elastomer 32, dioctyl isophthalate 17, ultra-fine alumina 12, graphene air condensation Glue 8, polyarylether ether nitrile 23, zinc oleate 2.5, magnesium oleate 1.5, palm wax 6, quartz powder 22, chloromethoxy fatty acid methyl ester 13, polyacrylonitrile-based carbon fiber 12.

[0022] The preparation method is the same as in Example 1.

Embodiment 3

[0024] A high-strength plastic floor made of the following raw materials by weight (kg): PVC resin 70, polyether thermoplastic polyurethane elastomer 38, dioctyl isophthalate 20, ultra-fine alumina 15, graphene air condensation Glue 10, polyarylether ether nitrile 29, zinc oleate 3, magnesium oleate 2, palm wax 7, quartz powder 26, chloromethoxy fatty acid methyl ester 15, polyacrylonitrile-based carbon fiber 15.

[0025] The preparation method is the same as in Example 1.

[0026] The performance test results of the plastic floor made in the above-mentioned Examples 1-3 are shown in the table below.

[0027]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-strength plastic flooring and a manufacture method thereof. The high-strength plastic flooring is made from, by weight part, 50-70 of PVC resin, 24-38 of polyether-type thermoplastic polyurethane elastomer, 15-20 of dioctyl isophthalate, 10-15 of ultrafine alumina, 5-10 of graphene aerogel, 17-29 of poly(arylene ether ether nitrile), 2-3 of zinc oleate, 1-2 of magnesium oleate, 5-7 of palm wax, 18-26 of quartz powder, 10-15 of chloro-methoxy fatty acid methyl ester, and 10-15 of polyacrylonitrile-based carbon fibers. The polyacrylonitrile-based carbon fibers and graphene aerogel which are light in weight and high in strength are used to improve the mechanical strength of plastic flooring. The manufactured plastic flooring is relatively high in mechanical strength, particularly in tensile strength and bending strength, is excellent in wear resistance, heat resistance and corrosion resistance, and adapts to the situation that requires high strength.

Description

Background technique [0001] The invention relates to a plastic floor and a preparation method thereof, in particular to a high-strength plastic floor and a preparation method thereof. Background technique [0002] In modern society, there are more and more varieties of floor decoration materials, from the traditional cement mortar floor to the generally bare terrazzo floor, to floor tiles, granite, and wooden floors, and new materials emerge in endlessly. Among them, the plastic floor is widely used in kindergartens, hotels, hospitals, office buildings, residences, airports, gymnasiums, railway stations and many other fields due to its advantages of small weight, fast construction speed, good appearance quality, various colors, comfortable walking, and anti-skid. . In recent years, with the rapid development of industrial technology and the continuous improvement of people's living standards, the performance requirements of plastic flooring are getting higher and higher. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L75/08C08L91/06C08L71/10C08K13/04C08K7/06C08K5/12C08K3/22C08K3/04
Inventor 刘跃清
Owner JIANGYIN ZHIYUAN AUTOMOBILE DECORATION PARTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com