Gas shielded solid welding wire used for steel with yield strength being 460 MPa and manufacturing method

A yield strength, solid wire technology, used in welding media, manufacturing tools, welding equipment, etc., to achieve the effect of improving low temperature toughness, excellent operating performance, and good weld formation

Inactive Publication Date: 2018-01-19
LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem that there is currently no high-toughness gas-shielded solid welding wire that can be used for welding high-strength steel with a yield strength of 460MPa in the above-mentioned prior art, the present invention provides a gas-shielded solid welding wire for steel with a yield strength of 460MPa and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gas shielded solid welding wire used for steel with yield strength being 460 MPa and manufacturing method
  • Gas shielded solid welding wire used for steel with yield strength being 460 MPa and manufacturing method
  • Gas shielded solid welding wire used for steel with yield strength being 460 MPa and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The present invention will be further elaborated below in combination with specific embodiments.

[0025] A gas-shielded solid welding wire for steel with a yield strength of 460MPa, comprising the following components: by mass percentage, C: 0.04%-0.12%, Mn: 0.9%-1.4%, Si: 0.4%-0.8%, Ni: 0.8%-1.1%, Mo: 0.08%-0.2%, Ti: 0.02%-0.05%, B: 0.0015%-0.0030%, Cu: 0.20%-0.25%, Al≤0.01%, S≤0.010%, P≤ 0.020%, O≤0.005%, N≤0.005%, Ce: 0.0050%-0.010%, the balance is iron powder and unavoidable impurities.

[0026] A method for preparing a gas-shielded solid welding wire for steel with a yield strength of 460MPa as described above: take each component according to the mass percentage, smelt the steel ingot, roll the wire rod, anneal the wire rod, draw and reduce the diameter, finish drawing and The copper plating process finally obtains ΦY1.2mm finished welding wire.

[0027] Examples 1-5 are all high-toughness gas-shielded solid welding wires suitable for 460MPa steel. The composi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a gas shielded solid welding wire used for steel with the yield strength being 460 MPa and a manufacturing method. The gas shielded solid welding wire comprises, by mass, 0.04%-0.12% of C, 0.9%-1.4% of Mn, 0.4%-0.8% of Si, 0.8%-1.1% of Ni, 0.08%-0.2% of Mo, 0.02%-0.05% of Ti, 0.0015%-0.0030% of B, 0.20%-0.25% of Cu, less than or equal to 0.01% of Al, less than or equal to0.010% of S, less than or equal to 0.020% of P, less than or equal to 0.005% of O, less than or equal to 0.005% of N, 0.0050%-0.010% of Ce, and the balance iron powder and unavoidable impurities. Whengas shielded welding with 80% of Ar and 20% of CO2 is conducted, the mechanical properties of deposited metal reach welding requirements of steel with the yield strength being 460 MPa and used for marine engineering, impact energy at -40 DEG C is over 120 J, and NDT is below -60 DEG C.

Description

technical field [0001] The invention relates to the field of welding materials, in particular to a gas-shielded solid welding wire for steel with a yield strength of 460MPa and a manufacturing method thereof. Background technique [0002] Steel plates with a yield strength of 460MPa are widely used in high-end technical fields such as marine engineering, construction machinery, and bridge construction. Structural steel plates in these fields are generally thicker, and the service conditions are relatively harsh, so higher requirements are put forward for the corresponding welding materials: (1) Good welding processability, which can meet the welding needs of different positions, and can adapt to many (2) It has excellent low temperature toughness and good impact value at -40°C. In addition, due to the harsh service environment of marine engineering, the drop weight test can be used to measure the zero plastic transition temperature (NDT) of steel, which can characterize the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/30B23K35/40
Inventor 孔红雨朱官朋冯兆龙王志银
Owner LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com