Tile adhesive and preparation method thereof

A ceramic tile adhesive, cellulose ether technology, applied in the direction of adhesives, adhesive types, cellulose adhesives, etc., can solve the problems of construction quality impact, poor water resistance, easy corrosion, etc., achieve low porosity, improve Mechanical properties, the effect of dense internal structure

Inactive Publication Date: 2017-12-22
东莞市西牛建材科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the natural vegetable gum is modified by cationic etherification or non-ionic hydroxypropylation, its cohesiveness and water solubility are greatly improved, but its water resistance is poor.
This defect makes it easy to be affected by moisture, easy to corrode, easy to fall off and easy to crack when exposed to the air during application, which will have a certain impact on the quality of the building
Chinese patent CN 02115787 .1 publicly reported a polymer water-soluble rubber powder adhesive, which is mainly composed of guar gum, hydroxypropyl squash gum powder, etc. Because the agent is modified by hydroxypropylation, its water solubility, adhesiveness and environmental protection have been greatly improved, but a multifunctional wall scraping putty powder has been reported, which is mainly composed of guar gum , plant dragon rubber powder, etc., although its environmental protection and comprehensive performance have been improved, but its poor water resistance still exists
Although the above-mentioned invention patent uses natural vegetable glue with better water solubility, which greatly improves its comprehensive performance such as environmental protection, its water resistance is poor, making it easy to fall off, easy to corrode, and easy to turtle in application. Defects such as cracks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The preparation method of ceramic tile adhesive comprises the steps:

[0018] Step a, weighing 60 g of raw materials methyl ethyl cellulose ether, 60 g of methyl hydroxypropyl cellulose ether, 160 g of starch ether and 50 g of triterpene saponin, and mixing them uniformly to obtain mixture A;

[0019] Step b, weighing 280g of raw material heavy metal sludge and 480g of acrylic pressure-sensitive adhesive aqueous solution according to the proportion and stirring them evenly in a mixer for 1-15 minutes to obtain a stirred mixture B;

[0020] In step c, mix the mixture A and mixture B stirred in steps a and b, and then stir for 8-15 minutes to obtain the tile adhesive of Example 1.

Embodiment 2

[0022] The preparation method of ceramic tile adhesive comprises the steps:

[0023] Step a, weighing 70 g of methyl ethyl cellulose ether, 50 g of methyl hydroxypropyl cellulose ether, 180 g of starch ether and 50 g of triterpene saponin, and mixing them uniformly to obtain mixture A;

[0024] Step b, weighing 300 g of raw material heavy metal sludge and 450 g of acrylic pressure-sensitive adhesive aqueous solution according to the proportion and stirring them evenly in a mixer for 1-15 minutes to obtain a stirred mixture B;

[0025] In step c, mix the mixture A and mixture B stirred in steps a and b, and then stir for 8-15 minutes to obtain the tile adhesive of Example 2.

Embodiment 3

[0027] The preparation method of ceramic tile adhesive comprises the steps:

[0028] Step a, weighing 80g of methyl ethyl cellulose ether, 60g of methyl hydroxypropyl cellulose ether, 260g of starch ether and 80g of triterpene saponin as raw materials, and mixing them uniformly to obtain mixture A;

[0029] Step b, weighing 380 g of raw material heavy metal sludge and 380 g of acrylic pressure-sensitive adhesive aqueous solution according to the proportion and stirring them evenly in a mixer for 1-15 minutes to obtain a stirred mixture B;

[0030] In step c, mix the mixture A and mixture B stirred in steps a and b, and then stir for 8-15 minutes to obtain the tile adhesive of Example 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a tile adhesive. The tile adhesive is prepared from components of raw materials in parts by weight as follows: 20-40 parts of heavy metal sludge, 5-10 parts of methylethylcellulose ether, 5-10 parts of methyl hydroxypropyl cellulose ether, 8-28 parts of starch ether, 30-50 parts of an acrylic pressure-sensitive adhesive solution and 3-10 parts of triterpenoid saponins. The tile adhesive has the advantages of rapid hardness, early strength, high strength and small shrinkage deformation; by means of the adhesive, the mechanical performance and the durability of a slurry-aggregate interface can be improved.

Description

technical field [0001] The technical field of building materials of the present invention particularly relates to a ceramic tile adhesive and a preparation method thereof. Background technique [0002] Environmental protection has become an inevitable trend in the development of building materials, and construction adhesives, which are widely used in the construction industry, are bound to face higher environmental protection requirements. Tile adhesive is one of the commonly used construction adhesives. It is generally made of cement, quartz sand, polymer cement and various additives through mechanical mixing. Tile adhesive is mainly used to bond tiles and tiles, also known as polymer tile bonding mortar. The tile adhesive reduces the dependence of the traditional construction process on the process of watering the base and soaking the bricks, and better avoids insufficient watering due to soaking the bricks. Mix a pack of materials according to the specified water ratio,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/00C09J101/28C09J11/04C09J11/08
CPCC08L2205/02C08L2205/035C09J11/04C09J11/08C09J133/00C09J2301/302C08L1/28C08L1/284C08L3/08C08K11/005C08K3/08
Inventor 夏先正
Owner 东莞市西牛建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com