Transparent crystal negative ion foaming wall paper, used paste material and preparation method of paste material

A negative ion, crystal technology, applied in textiles and papermaking, coatings, building components, etc., can solve problems such as strong plastic texture, and achieve the effect of improving quality and enriching varieties

Inactive Publication Date: 2017-12-22
ZHEJIANG ANYSA DECORATION MATERIAL CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional PVC wallpaper, after foaming and softening, is generally pressed and cooled by embossing rollers. The products produced are hard and have a strong plastic texture, which cannot meet the needs of people at all levels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Preparation of Paste

[0025] Put 30 parts of glyceryl citrate (15 parts of monoester, 15 parts of diester), 15 parts of epoxidized soybean oil into the reactor, stir properly at a low speed, then add 3 parts of calcium carbonate and magnesium carbonate in turn, 100 parts of PVC resin, 3 parts of crystal pearlescent pigment, 10 parts of strange ice stone, 6 parts of potassium zinc stabilizer and stir well.

[0026] Preparation of transparent crystal negative ion foam wallpaper

[0027] Take the non-woven fabric as the base paper, paint the base color on the non-woven fabric in turn, apply the aforementioned paste by rotary screen printing, then put it in an oven to foam and emboss to obtain the transparent crystal anion foamed wallpaper.

Embodiment 2

[0029] Preparation of paste Put 50 parts of glycerin citrate (25 parts of monoester, 25 parts of diester), 10 parts of epoxidized soybean oil into the reactor, stir at low speed, then add 3 parts of magnesium carbonate, 120 parts of PVC resin, crystal 5 parts of pearlescent pigment, 10 parts of tourmaline, 3 parts of potassium zinc stabilizer and stir well.

[0030] The preparation process of the transparent crystal anion foamed wallpaper is the same as in Example 1, and will not be repeated.

Embodiment 3

[0032] Preparation of Paste

[0033] Put 40 parts of glycerin citrate (16 parts of monoester, 24 parts of diester), 13 parts of epoxidized soybean oil into the reactor, stir at low speed, then add 2 parts of magnesium carbonate and calcium bicarbonate, 110 parts of PVC resin, 4 parts of crystal pearlescent pigment, 5 parts of tourmaline, 10 parts of shell powder, 5 parts of potassium zinc stabilizer and stir well.

[0034] The preparation process of the transparent crystal anion foamed wallpaper is the same as in Example 1, and will not be repeated.

[0035] Epoxidized soybean oil of the present invention, PVC resin, crystal pearlescent pigment; Potassium zinc stabilizer is the commodity of market sale.

[0036] Epoxidized soybean oil used in the present invention, PVC resin, crystal pearlescent pigment; Potassium zinc stabilizer adopts the commodity sold in the market to get final product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides paste material used for transparent crystal negative ion foaming wall paper. The paste material is formed by mixing the following ingredients in parts by mass: 30 to 50 parts of glyceride citrate, 10 to 15 parts of epoxidized soybean oil, 3 to 6 parts of foaming agents, 100 to 120 parts of PVC resin, 3 to 5 parts of crystal pearlescent pigments, 3 to 6 parts of potassium zinc stabilizers and 10 to 15 parts of anion superfine powder body materials. The invention also discloses a preparation method of the paste material, and the wall paper using the paste material. The crystal pearlescent pigments, the foaming agents and the PVC resin are used as connecting materials to be prepared into the paste material; the paste material is printed onto the non-woven fabric through a round screen; then, through operation according to design requirements or conventional printing, the flickering and transparent effects are achieved after the high-temperature baking, so that the produced product has the three-dimensional effects and the pearl effects; the requirement of rich layers of the wall paper is better met; the quality of the wall paper is improved; the types of the wall paper is enriched; the requirements of the customers are better met.

Description

technical field [0001] The invention relates to a foamed PVC wallpaper, a paste used for the wallpaper and a preparation method of the paste. Background technique [0002] Wallpaper is the most popular soft decoration in decoration now, because its simplicity and convenience bring a more comfortable and natural living atmosphere to home life. There are many kinds of wallpapers, including wood fiber wallpapers, pure paper wallpapers, non-woven wallpapers, PVC wallpapers and so on. PVC wallpaper has good waterproof and moisture resistance, and is convenient for construction. After the surface is polluted, it can be wiped with a clean sponge or towel. It is durable and easy to maintain. This type of wallpaper is currently the most widely used wallpaper and is deeply loved by consumers. However, the traditional PVC wallpaper, after foaming and softening, is generally pressed and cooled by embossing rollers. The products produced are hard and have a strong plastic texture, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/06C09D191/00C09D5/00C09D7/12C08J9/08D06N3/00
CPCC09D127/06C08J9/08C08J2203/02C08J2327/06C08J2491/00C08K2003/265C08K2201/014C08L2201/10C08L2203/14C09D5/00D06N3/0043D06N7/0002D06N2211/063C08L91/00C08K13/02C08K5/11C08K3/38C08K3/26
Inventor 蒋明聪孟正兵
Owner ZHEJIANG ANYSA DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap