Water-permeable concrete having temperature-sensing color-changing function

A technology of permeable concrete and temperature-sensitive discoloration, applied in the field of permeable concrete, can solve the problems of lack of permeable concrete, and achieve the effects of easy promotion, strong economy, and increased cost

Active Publication Date: 2017-12-22
厦门美益绿建科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Unfortunately, the current pervious concrete does not have such a function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Preparation of a temperature-sensitive color-changing material: Weigh 19 parts of water-based resin, 8 parts of temperature-sensitive color-changing powder, nano-SiO 2 3 parts, 1 part of talcum powder, 1.5 parts of redispersible latex powder, 0.15 parts of water-repellent agent, mix well at room temperature, and obtain the thermochromic material;

[0032] The water-based resin is water-based polyurethane acrylate emulsion; the temperature-sensitive color-changing powder is a triarylmethane phthalide-type temperature-sensitive color-changing material, the chromogenic agent is crystal violet lactone, the chromogenic agent is bisphenol A, and the solvent is myristyl alcohol. The color change process of thermochromic powder occurs in the range of 33-38°C, when it is lower than this range, it is close to white, and when it is higher than this range, it is blue; nano-SiO 2 Hydrophilic gas-phase nano-SiO with an average particle size of no more than 50nm 2 ; The specificatio...

Embodiment 2

[0034] Preparation of a temperature-sensitive color-changing material: Weigh 17 parts of water-based resin, 6 parts of temperature-sensitive color-changing powder, nano-SiO 2 2 parts, 1 part of talcum powder, 0.8 part of redispersible latex powder, 0.10 part of water-repellent agent, mix well at room temperature, and obtain the temperature-sensitive color-changing material;

[0035] The water-based resin is a water-based epoxy acrylate emulsion; the thermochromic powder is a fluoran-type thermochromic material, and the chromogenic agent is 2-anilino-3-methyl-6-diethylaminofluorane (ODB-1) , the color developer is bisphenol A, and the solvent is benzophenone. The color change process of this thermochromic powder occurs in the range of 36-43°C. When it is lower than this range, it is close to white, and when it is higher than this range, it is black; nano-SiO 2 Hydrophilic gas-phase nano-SiO with an average particle size of no more than 50nm 2; The specification of talcum pow...

Embodiment 3

[0037] A kind of permeable concrete with thermochromic function, made by the following method:

[0038] (1) Preparation of thermochromic material: preparation method and raw materials are the same as in Example 1;

[0039] (2) Preparation of permeable concrete: Weigh 260 parts of white Portland cement, 20 parts of reinforcing components, 1680 parts of stones, 106 parts of water, 5 parts of water-reducing agent, and the temperature-sensitive concrete prepared in step (1) by weight. 17 parts of color-changing materials are mixed uniformly at room temperature to obtain permeable concrete with temperature-sensitive color-changing function.

[0040] Wherein, Portland cement is white Portland cement with P.W 42.5 label. The reinforcing component is nano-calcium carbonate with an average particle size not higher than 60 μm. The stones are rationally graded white stones with a particle size of 6-10 mm and mainly single-graded. The water is the water meeting the requirements of "Con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to water-permeable concrete having a temperature-sensing color-changing function. The water-permeable concrete comprises, by mass, 250-300 parts of silicate cement, 20-30 parts of enhancing component, 1500-1700 parts of pebble, 105-115 parts of water, 4-7 parts of water reducer and 15-25 parts of temperature-sensing color-changing material. Compared with the prior art, the water-permeable concrete has the advantages that when outside temperature changes, color changes along with changing of temperature within a certain interval, so that good decorating effect is realized. Needed raw materials are simple and easy to obtain, and the water-permeable concrete does not need special preparation process and is high in economic efficiency and convenient for popularization.

Description

technical field [0001] The invention relates to permeable concrete, in particular to a permeable concrete with temperature-sensitive color changing function. Background technique [0002] Thermochromic materials, also known as reversible thermochromic materials, refer to special functional materials whose color changes reversibly with temperature within a certain temperature range. Judging from the composition and properties of the existing thermochromic materials, they can be divided into three categories: inorganic, liquid crystal and organic. Compared with inorganic and liquid crystal materials, organic thermochromic materials have the following advantages: a wide range of temperature changes, and the color change range can be between -200 and 200 °C; there is a large choice, and the color can be freely selected; the color change temperature is generally low , long life and high sensitivity, good stability, high resolution of discoloration, relatively cheap and so on. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/28C04B28/04C04B111/82
CPCC04B28/04C04B40/0039C04B2111/00284C04B2111/82C04B14/02C04B2103/302C04B14/28C04B18/146C04B24/28C04B2103/54C04B24/026C04B14/062C04B14/042C04B24/26C04B24/08C04B24/281C04B24/008
Inventor 王浩任赵明伍根伙邹冬森刘文龙谢芳
Owner 厦门美益绿建科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com