A kind of acrylic acid epoxy core-shell emulsion and preparation method thereof

A technology of acrylic and epoxy core, applied in the field of acrylic epoxy core-shell emulsion and its preparation, to achieve the effects of improving compactness, improving film forming compactness, and perfecting the raw material system

Active Publication Date: 2019-08-06
佛山市顺德区巴德富实业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are currently no products with such functions on the market. Therefore, how to develop an acrylic epoxy core-shell emulsion with both excellent properties is a technical problem in the emulsion industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acrylic acid epoxy core-shell emulsion and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] In addition, the present invention also provides a method for preparing the acrylic epoxy core-shell emulsion described in any one of the above, which specifically includes the following steps in terms of parts by mass,

[0037] 1) Pre-emulsification: Under normal temperature and pressure, mix 2-10 parts of anionic emulsifier, 20-30 parts of water, 5-10 parts of epoxy resin and 10-40 parts of butyl acrylate in a pre-emulsification tank, fully stir and dissolve , and sequentially add 20-40 parts of styrene, 5-20 parts of butyl acrylate, and 0.5-3 parts of acrylic acid;

[0038]2) Polymerization: add 90-210 parts of water and 1-2 parts of anionic emulsifier to the bottom of the reaction kettle, raise the temperature to 80-90°C, stir for 20-40 minutes, add dropwise the pre-emulsion obtained in step 1) and 0.1-0.5 part of initiator is used for chemical reaction, the dropping time is 150-300 minutes, the reaction temperature is 80-90°C, and the reaction time is 170-340 minut...

Embodiment 1

[0046] A preparation method of an acrylic epoxy core-shell emulsion, calculated in parts by mass, including 150 parts of water, 30 parts of styrene, 30 parts of methyl methacrylate, 20 parts of isooctyl acrylate, 20 parts of butyl acrylate, acrylic acid 0.5 parts, 0.5 parts of methacrylic acid, 5 parts of epoxy resin, 5 parts of anionic emulsifier, 1 part of crosslinking monomer, 5 parts of water-based epoxy curing agent, 0.5 parts of initiator, 0.1 part of oxidizing agent, and 0.1 part of reducing agent;

[0047] Wherein, the epoxy resin is E44;

[0048] Described anionic emulsifier is sodium lauryl sulfate;

[0049] The crosslinking monomer is trimethylolpropane trimethacrylate;

[0050] The water-based epoxy curing agent is an amine curing agent;

[0051] Described initiator is sodium persulfate;

[0052] The oxidant is an organic peroxide;

[0053] Described reducing agent is sodium binitrite;

[0054] The preparation method of this emulsion specifically comprises the...

Embodiment 2

[0064] A preparation method of an acrylic epoxy core-shell emulsion, calculated in parts by mass, including 200 parts of water, 45 parts of styrene, 45 parts of methyl methacrylate, 50 parts of isooctyl acrylate, 50 parts of butyl acrylate, acrylic acid 3 parts, 3 parts of methacrylic acid, 7 parts of epoxy resin, 10 parts of anionic emulsifier, 3 parts of crosslinking monomer, 10 parts of water-based epoxy curing agent, 1 part of initiator, 0.3 part of oxidizing agent, and 0.3 part of reducing agent;

[0065] Wherein, described epoxy resin is that E44, E35 are mixed according to 1:1;

[0066] Described anionic emulsifier is sodium dodecylbenzenesulfonate;

[0067] The cross-linking monomer is trimethylolpropane acrylate, tripropylene glycol diacrylate mixed according to 1:1;

[0068] The water-based epoxy curing agent is an alcohol curing agent;

[0069] Described initiator is ammonium persulfate;

[0070] The oxidant is an organic peroxide;

[0071] The reducing agent is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an acrylic epoxy core-shell emulsion and a preparation method thereof, which specifically include the following components in parts by mass: 150-300 parts of water, 30-60 parts of styrene, and 30-60 parts of methyl methacrylate , 20-75 parts of isooctyl acrylate, 20-75 parts of butyl acrylate, 0.5-5 parts of acrylic acid, 0.5-5 parts of methacrylic acid, 5-10 parts of epoxy resin, 5-20 parts of anionic emulsifier, crosslinking 1-5 parts of monomer, 5-15 parts of water-based epoxy curing agent, 0.5-2 parts of initiator, 0.1-0.5 parts of oxidizing agent, and 0.1-0.5 parts of reducing agent. The acrylic epoxy core-shell emulsion combines acrylic emulsion and epoxy resin, which makes up for the shortcomings of epoxy resin such as easy yellowing, poor heat and humidity resistance, and poor toughness, and improves the hardness and wear resistance of the acrylic emulsion.

Description

technical field [0001] The invention relates to a core-shell emulsion and a preparation method thereof, in particular to an acrylic epoxy core-shell emulsion and a preparation method thereof. Background technique [0002] Epoxy resin has the characteristics of low shrinkage, excellent mechanical properties, excellent electrical properties, and stable chemical properties, but epoxy resin has poor impact resistance, poor toughness, brittleness, non-yellowing resistance, and poor weather resistance. During the construction process, most of the properties of the epoxy resin also need to play a role through the selection of the curing agent. Traditional acrylic emulsion has excellent elasticity, certain flexibility, excellent weather resistance, fast drying speed, etc., but it also has disadvantages such as poor fullness and easy to be affected by the external environment. Therefore, if the two can be combined and complement each other, so that the shortcomings of the two can co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/10C08F212/08C08F220/14C08F220/18C08F220/06C08F2/26C08F4/40
CPCC08F2/26C08F4/40C08F283/10C08F220/1808C08F220/1804
Inventor 成煬霈黄祥斌罗云
Owner 佛山市顺德区巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap