High-performance water-based lubricating oil for copper-zinc alloy cold stamping
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cold stamping, high-performance technology, applied in the field of stamping lubricants, can solve the problems of metal flow discontinuity, burning (smoke, plate fracture, etc.), and achieve the effect of keeping the surface smooth, reducing defects, and reducing thermal friction
Active Publication Date: 2017-11-24
广州杜朗介质科技有限公司
View PDF4 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Cold stamping is a pressure processing method that uses a stamping die to apply pressure to a sheet or hot material on a press at room temperature to cause plastic deformation or separation to obtain parts of the desired shape and size. The process is simple, but cold During the stamping process, the friction force is large, and the metal flow is intermittent, which may easily cause the plate to break and wrinkle. As the deformation temperature of the metal in the stamping die will continue to rise, the oil-based lubricating oil will become thinner, and in some cases it will Reach the flash point or burn (smoke), lubrication failure, so high-performance water-based lubricating oil is required
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] A high-performance water-based lubricating oil for copper-zinc alloy cold stamping, made of the following raw materials in parts by weight: tungsten disulfide 5, fluorinated graphite 3, fullerene 0.6, nickel sulfide 0.05, polyether modified silicon 0.02, Water 600.
[0018] The tungsten disulfide is nanometer tungsten disulfide.
[0019] A preparation method of high-performance water-based lubricating oil for copper-zinc alloy cold stamping, comprising the following steps:
[0020] (1) Heat tungsten disulfide to 220°C, add nickel sulfide, keep warm for 3 hours, cool down at a rate of 4°C / min, cool down to 140°C, and keep warm for 50 minutes to increase the oxidation resistance of tungsten disulfide and nickel sulfide. Wear resistance, can maintain the golden color of copper-zinc alloy stamping parts, prolong service life, high temperature during cold stamping, reduce the volume of nickel sulfide, reduce the gap between copper-zinc alloy and mold, make cold stamping mor...
Embodiment 2
[0025] A high-performance water-based lubricating oil for copper-zinc alloy cold stamping, made of the following raw materials in parts by weight: tungsten disulfide 6, fluorinated graphite 4, fullerene 0.7, nickel sulfide 0.06, polyether modified silicon 0.03, Water 650.
[0026] The tungsten disulfide is nanometer tungsten disulfide.
[0027] The preparation method is the same as in Example 1.
Embodiment 3
[0029] A high-performance water-based lubricating oil for copper-zinc alloy cold stamping, made of the following raw materials in parts by weight: tungsten disulfide 7, fluorinated graphite 5, fullerene 0.8, nickel sulfide 0.07, polyether modified silicon 0.04, Water 700.
[0030] The tungsten disulfide is nanometer tungsten disulfide.
[0031] The preparation method is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention mainly relates to the technical field of stamping lubricants and discloses a high-performance water-based lubricating oil for copper-zinc alloy cold stamping. The high-performance water-based lubricating oil for copper-zinc alloy cold stamping is prepared from the following raw materials: tungsten disulfide, carbon monofluoride, fullerene, nickel sulfide, polyether modified silicon and water. Water is volatilized during cold stamping, so that the cold stamping temperature is reduced by 40-50 DEG C; the heat frictional force generated by copper-zinc alloy cold stamping is obviously reduced, and the copper-zinc alloy continuously flows during cold stamping, so that the breakage rate is reduced by 17.3%, and the wrinkling rate is reduced by 12.6%; tungsten disulfide and nickel sulfate are mixed at a high temperature, so that the resistance to oxidation of tungsten disulfide and the wear resistance of the nickel sulfate are increased; a golden yellow color and luster of a copper-zinc alloy cold stamping part can be maintained, the service life is prolonged, and the cold stamping temperature is relatively high, so that the size of nickel sulfate is reduced, the gaps between the copper-zinc alloy and a mold are reduced, and therefore, cold stamping is more accurate; the size of the nickel sulfate is gradually increased after temperature reduction, the gaps are increased, and demolding is facilitated, so that the surface of the copper-zinc alloy cold stamping part is smooth and the defective rate is reduced.
Description
technical field [0001] The invention mainly relates to the technical field of stamping lubricants, in particular to a high-performance water-based lubricating oil for copper-zinc alloy cold stamping. Background technique [0002] Copper-zinc alloy is a kind of memory alloy, golden yellow, like the color of gold, commonly known as brass, and has a wide range of uses. Small fractures and flaws produced in the cold stamping process will affect the use value of copper-zinc alloy. [0003] Cold stamping is a pressure processing method that uses a stamping die to apply pressure to a sheet or hot material on a press at room temperature to cause plastic deformation or separation to obtain parts of the desired shape and size. The process is simple, but cold During the stamping process, the friction force is large, and the metal flow is intermittent, which may easily cause the plate to break and wrinkle. As the deformation temperature of the metal in the stamping die will continue to ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.