Crystal lamp glass production technology

A production process, crystal lamp technology, applied in metal material coating process, ion implantation plating, coating and other directions, can solve the problems of crystal lamp glass no longer crystal clear, affecting the use effect, easy to wear or corrode, etc. Good light transmittance and absorption, good use effect, energy saving effect

Inactive Publication Date: 2017-11-21
HEFEI LIYUTAI GLASS PROD CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing method for making crystal lamp glass is complicated, and the produced crystal lamp glass products are easy to wear or corrode during use. After a period of use, dirt such as dust will accumulate on the surface, making the crystal lamp glass no longer crystal clear Thorough, affecting the effect of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A production process of crystal lamp glass, comprising the following steps:

[0024] (1) Clean and dry the formed crystal lamp ornaments, put them into the magnetron sputtering tray, and then send them to the vacuum coating machine for coating; the specific process of cleaning is: put the formed crystal lamp ornaments in acetone and ultrasonically After cleaning for 12 minutes, ultrasonically clean with ethanol for 15 minutes, and finally ultrasonically clean for 13 minutes in deionized water. Among them, the crystal lamp ornaments are crystal lamp pendants, crystal lamp loose beads or crystal lamp decoration balls.

[0025] (2) Use oxygen as the reactive gas, argon as the protective gas, and DC power supply to sputter the stainless steel planar target, and magnetron sputter a TiOx layer on the crystal lamp jewelry; the volume ratio of argon to oxygen is 1:2.3, The sputtering power was 108 kW, and the thickness of the TiOx layer was 46 nm.

[0026] (3) Use a mixed gas...

Embodiment 2

[0030] A production process of crystal lamp glass, comprising the following steps:

[0031] (1) Clean and dry the formed crystal lamp ornaments, put them into the magnetron sputtering tray, and then send them to the vacuum coating machine for coating; the specific process of cleaning is: put the formed crystal lamp ornaments in acetone and ultrasonically After cleaning for 15 minutes, ultrasonically clean with ethanol for 16 minutes, and finally ultrasonically clean for 17 minutes in deionized water. Among them, the crystal lamp ornaments are crystal lamp pendants, crystal lamp loose beads or crystal lamp decoration balls.

[0032] (2) Use oxygen as the reactive gas, argon as the protective gas, sputter the stainless steel planar target with DC power supply, and magnetron sputter a TiOx layer on the crystal lamp jewelry; the volume ratio of argon to oxygen is 1:2.6, The sputtering power was 120 kW, and the thickness of the TiOx layer was 45 nm.

[0033] (3) Use a mixed gas o...

Embodiment 3

[0037] A production process of crystal lamp glass, comprising the following steps:

[0038] (1) Clean and dry the formed crystal lamp ornaments, put them into the magnetron sputtering tray, and then send them to the vacuum coating machine for coating; the specific process of cleaning is: put the formed crystal lamp ornaments in acetone and ultrasonically After cleaning for 12 minutes, ultrasonically clean with ethanol for 17 minutes, and finally ultrasonically clean for 15 minutes in deionized water. Among them, the crystal lamp ornaments are crystal lamp pendants, crystal lamp loose beads or crystal lamp decoration balls.

[0039] (2) Use oxygen as the reaction gas, argon as the protective gas, sputter the stainless steel plane target with DC power supply, and magnetron sputter a TiOx layer on the crystal lamp jewelry; the volume ratio of argon to oxygen is 1:2.5, The sputtering power was 110 kW, and the thickness of the TiOx layer was 47 nm.

[0040] (3) Use a mixed gas of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of crystal lamp glass. The production process includes the following steps: (1) cleaning and drying the formed crystal lamp ornaments, and sending them to a vacuum coating machine for coating; (2) coating the crystal lamp ornaments Magnetron sputtering a TiOx layer on top; (3) Magnetron sputtering a chromium nitride film layer on the TiOx layer; (4) Magnetron sputtering a zinc tin oxide layer on the chromium nitride film layer; (5) A titanium oxide layer is magnetron sputtered on the zinc tin oxide layer. The process of the invention is simple and controllable, saves energy consumption, and the produced crystal lamp glass is wear-resistant and corrosion-resistant. The multi-layer coating film can use the photocatalytic effect to achieve the effect of self-cleaning, has good light transmission, and has certain economic benefits.

Description

technical field [0001] The invention relates to the technical field of crystal glass processing, in particular to a production process of crystal lamp glass. Background technique [0002] Crystal lighting is generally made of K9 crystal processing. With the help of the crystal clear and pure color, it forms a bright and sparkling decorative effect. Originated from European court nobles, it has developed richly in China and has a variety of varieties. It is a necessary decorative item for home furnishing. The existing method for making crystal lamp glass is complicated, and the produced crystal lamp glass products are easy to wear or corrode during use. After a period of use, dirt such as dust will accumulate on the surface, making the crystal lamp glass no longer crystal clear Thorough, affecting the effect of use. Therefore, the manufacture method of existing crystal lamp pendant glass remains to be further perfected. Contents of the invention [0003] The object of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/35C23C14/08C03C17/34
CPCC23C14/352C03C17/3417C23C14/0036C23C14/083C23C14/086
Inventor 武娟
Owner HEFEI LIYUTAI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com