Transmission belt material and preparation method thereof

A technology of transmission belt and anti-aging agent, which is applied in the field of transmission belt materials and its preparation, can solve the problems of rubber materials such as insignificant high temperature and wear resistance, improve physical and mechanical properties and processing performance, broaden the market and application prospects, and enhance heat resistant effect

Inactive Publication Date: 2017-11-07
ANYANG INST OF TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of such an approach on the improvement of the high temperature and wear resistance of the rubber material is not significant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1 The formula of transmission belt material consists of: 10 parts of natural rubber, 25 parts of styrene-butadiene rubber, 60 parts of nitrile rubber, 1 part of sulfur, 5 parts of plasticizer, 2 parts of adhesive, 7 parts of zinc oxide, anti-aging agent 2 parts of RD, 1.5 parts of anti-aging agent NBC, 0.5 parts of anti-aging agent DNP, 15 parts of carbon black, 5 parts of white carbon black, 1 part of N-cyclohexyl-2-benzothiazole sulfenamide, 2, 2'- 1 part of dithiodibenzothiazole, 3 parts of stearic acid, 10 parts of coumarone resin, 3.5 parts of pine tar, the above are parts by mass.

[0019] The preparation method of embodiment 1 comprises the following steps

[0020] According to the formula, put natural rubber, styrene-butadiene rubber, and nitrile rubber into the internal mixer at room temperature, heat to 110°C, then add half of the carbon black and heat up to 145°C for 4 minutes of mixing, and then follow the order to Add zinc oxide, binder, white c...

Embodiment 2

[0029] The formula of embodiment 2 driving belt material consists of: 25 parts of natural rubber, 40 parts of styrene-butadiene rubber, 75 parts of nitrile rubber, 4 parts of sulfur, 8 parts of plasticizer, 5 parts of adhesive, 11 parts of zinc oxide, anti-aging agent 4 parts of RD, 3 parts of anti-aging agent NBC, 2 parts of anti-aging agent DNP, 18 parts of carbon black, 6 parts of white carbon black, 3 parts of N-cyclohexyl-2-benzothiazole sulfenamide, 2, 2'-di Thiodibenzothiazole 2 parts, stearic acid 5 parts, coumarone resin 11 parts, pine tar oil 5 parts. The above are parts by mass.

[0030] The preparation method of embodiment 2 comprises the following steps

[0031] According to the formula, put natural rubber, styrene-butadiene rubber, and nitrile rubber into the internal mixer at room temperature, heat to 120°C, then add half of the carbon black and heat up to 155°C for 6 minutes of mixing, and then follow the order to the compactor Add zinc oxide, binder, white c...

Embodiment 3

[0034] Embodiment 3 The formula of transmission belt material consists of: 20 parts of natural rubber, 35 parts of styrene-butadiene rubber, 70 parts of nitrile rubber, 3 parts of sulfur, 6 parts of plasticizer, 4 parts of adhesive, 9 parts of zinc oxide, anti-aging agent 3 parts of RD, 2.25 parts of anti-aging agent NBC, 1.5 parts of anti-aging agent DNP, 15 parts of carbon black, 5 parts of white carbon black, 2 parts of N-cyclohexyl-2-benzothiazole sulfenamide, 2, 2'- Dithiodibenzothiazole 1.5 parts, stearic acid 4 parts, coumarone resin 10.5 parts, pine tar oil 4 parts. The above are parts by mass.

[0035] The preparation method of embodiment 3 comprises the following steps

[0036] According to the formula, put natural rubber, styrene-butadiene rubber, and nitrile rubber into the internal mixer at room temperature, heat to 115°C, then add half of the carbon black and heat up to 150°C for 5 minutes of mixing, and then follow the order to the compactor Add zinc oxide, bi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a transmission belt material. A formula of the material comprises the following components in parts by mass: 10 to 25 parts of natural rubber, 25 to 40 parts of styrene butadiene rubber, 60 to 75 parts of nitrile rubber, 1 to 4 parts of sulfur, 5 to 8 parts of plasticizer, 2 to 5 parts of bonding agent, 7 to 11 parts of zinc oxide, 2 to 4 parts of anti-aging agent RD, 1.5 to 3 parts of anti-aging agent NBC, 0.5 to 2 parts of anti-aging agent DNP, 15 to 18 parts of carbon black, 5 to 6 parts of white carbon black, 1 to 3 parts of N-cyclohexyl-2-benzothiazolesulfenamide, 1 to 2 parts of 2,2'-dibenzothiazyl disulfide, 3 to 5 parts of stearic acid, 10 to 11 parts of coumatone resin, and 3.5 to 5 parts of pine tar. A preparation method comprises the following steps: (1), putting the natural rubber, the styrene butadiene rubber and the nitrile rubber into a banbury mixer, heating to the temperature of 110 to 120 DEG C; (2), adding half of the carbon black and rising the temperature to be 145 to 155 DEG C for milling for 4 to 6min, sequentially adding the zinc oxide, the white carbon black, the coumatone resin, an accelerator and the anti-aging agents for milling; (3), adding the rest carbon black, the plasticizer, the sulfur and the pine tar into a open mill for carrying out milling for 6 to 9min to obtain masterbatch; (4), putting the masterbatch into a vulcanizing mold for carrying out vulcanization treatment.

Description

technical field [0001] The invention belongs to the technical field of rubber materials, and in particular relates to a transmission belt material and a preparation method thereof. Background technique [0002] The essence of the transmission belt is a connection belt that transmits the power source to the equipment by means of the connection of the mechanical structure, so that the equipment can run. Because the transmission belt has the excellent performance of free variable speed, low price and convenient replacement, it plays an important role in today's mechanical transmission parts, so the quality of the transmission belt material will directly affect the operation of mechanical equipment and the quality of its production parts. With the rapid development of the contemporary machinery industry, especially some new agricultural machinery, automobile and other industries, the requirements for the performance of transmission belt materials are becoming more and more strin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L9/06C08L7/00C08L45/02C08K13/02C08K3/06C08K3/22C08K3/04C08K5/47C08K5/09
CPCC08K2003/2296C08K2201/014C08L9/02C08L2201/08C08L2205/035C08L9/06C08L7/00C08L45/02C08K13/02C08K3/06C08K3/22C08K3/04C08K5/47C08K5/09
Inventor 李安玲张阳明杨慷孔令豪王涛刘松锋郭娅晨周杨京
Owner ANYANG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com