Insulating arc suppression nanomaterial modified transformer oil and preparation method thereof

A technology of nano-materials and transformer oil, which is applied in the petroleum industry, lubricating compositions, etc., can solve the problems of carcinogenicity and toxicity, and achieve the effects of increasing the ignition point, improving flame retardancy, and good flame retardancy

Inactive Publication Date: 2017-11-03
合肥轻风飏电气科技有限责任公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polychlorinated biphenyls, which are not fuel oils, are carcinogenic and toxic, and have been banned. Fluorine oils are rarely used because of their high prices and limited availability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An insulating arc-extinguishing nanomaterial modified transformer oil of the present embodiment includes the following raw materials by weight:

[0036] 6 parts of nano-modified material, 1 part of metal passivator, 2 parts of benzyl alcohol, 1 part of magnesium stearate, 1 part of sodium tungstate, 700 parts of compound base oil, 7 parts of hydroquinone, nitrotriacetic acid 0.3 part of tetrasodium, 0.2 part of polymaleic anhydride, 0.8 part of compound antioxidant, 0.4 part of red phosphorus flame retardant, and 0.4 part of coupling agent.

[0037] The nano-modified material in this embodiment is a mixture of nano-zirconia, nano-titanium oxide, nano-zinc oxide, and nano-aluminum nitride in a weight ratio of 2:2:2:1.

[0038] The metal passivating agent in this embodiment is thiadiazole and its derivatives.

[0039] The compound base oil in this embodiment is a mixture of refined vegetable oil and naphthenic base oil in a weight ratio of 1:3.

[0040] The compound ant...

Embodiment 2

[0048] An insulating arc-extinguishing nanomaterial modified transformer oil of the present embodiment includes the following raw materials by weight:

[0049] 8 parts of nano-modified material, 2 parts of metal passivator, 4 parts of benzyl alcohol, 2 parts of magnesium stearate, 3 parts of sodium tungstate, 800 parts of compound base oil, 9 parts of hydroquinone, nitrotriacetic acid 0.5 part of tetrasodium, 0.5 part of polymaleic anhydride, 1.2 part of compound antioxidant, 0.6 part of red phosphorus flame retardant, and 0.8 part of coupling agent.

[0050] The nano-modified material in this embodiment is a mixture of nano-zirconia, nano-titanium oxide, nano-zinc oxide, and nano-aluminum nitride in a weight ratio of 2:2:2:1.

[0051] The metal deactivator in this embodiment is benzotriazole and its derivatives.

[0052] The compound base oil in this embodiment is a mixture of refined vegetable oil and naphthenic base oil in a weight ratio of 1:3.

[0053] The compound anti...

Embodiment 3

[0061] An insulating arc-extinguishing nanomaterial modified transformer oil of the present embodiment includes the following raw materials by weight:

[0062] 7 parts of nano-modified materials, 1.5 parts of metal passivator, 3 parts of benzyl alcohol, 1.5 parts of magnesium stearate, 2 parts of sodium tungstate, 750 parts of compound base oil, 8 parts of hydroquinone, nitrotriacetic acid 0.4 part of tetrasodium, 0.4 part of polymaleic anhydride, 1 part of compound antioxidant, 0.5 part of red phosphorus flame retardant, and 0.6 part of titanate coupling agent.

[0063] The nano-modified material in this embodiment is a mixture of nano-zirconia, nano-titanium oxide, nano-zinc oxide, and nano-aluminum nitride in a weight ratio of 2:2:2:1.

[0064] The metal passivating agent in this embodiment is thiadiazole and its derivatives.

[0065] The compound base oil in this embodiment is a mixture of refined vegetable oil and naphthenic base oil in a weight ratio of 1:3.

[0066] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
ignition pointaaaaaaaaaa
ignition pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses insulating arc suppression nanomaterial modified transformer oil which comprises the following raw materials in parts by weight: 6-8 parts of modified nanomaterial, 1-2 parts of metal deactivator, 2-4 parts of benzyl alcohol, 1-2 parts of magnesium stearate, 1-3 parts of sodium tungstate, 700-800 parts of compound base oil, 7-9 parts of hydroquinone, 0.3-0.5 parts of nitrilotriacetic acid tetrasodium salt, 0.2-0.5 parts of polymaleic anhydride, 0.8-1.2 parts of compound antioxidant, 0.4-0.6 parts of red phosphorus flame retardant and 0.4-0.8 parts of coupling agent. The transformer oil has better insulativity and arc suppression performance, and has better oxidation resistance under a high temperature condition; the nanomaterial is introduced, so that the possibility of oxidation, aging and corrosion of the transformer oil is low, and the stability is improved; and in addition, the transformer oil has good flame retardation, is safe and reliable in raw material component, lower in cost and concise in technology, and has a higher practical value and a good application prospect.

Description

technical field [0001] The invention relates to the technical field of power equipment materials, in particular to an insulating arc-extinguishing nanomaterial modified transformer oil and a preparation method thereof. Background technique [0002] Transformer oil is flammable oil, generally does not include synthetic oil, that is, does not include non-fuel oil and high flash point oil. Otherwise, the oil will accumulate [0003] There are two kinds of chlorinated biphenyl (PCB) and fluorine oil, and high flash point oil has silicone oil, alpha oil, beta oil, M oil, polyalphaene, dodecyl benzene, E oil, gamma oil. The ignition point of transformer oil is 165 ℃, while the ignition point of high ignition point oil is above 300 ℃, and no fuel oil will not catch fire. High ignition point oil, also known as flame retardant oil, is mainly used in high ignition point oil-immersed transformers, flame retardant oil on-load tap-changers, capacitors, cables and other occasions. Poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/10C10N30/12C10N40/14
CPCC10M169/048C10M2201/06C10M2201/062C10M2207/021C10M2207/022C10M2207/126C10M2209/086C10M2215/00C10M2215/223C10M2219/106C10N2010/02C10N2010/04C10N2030/10C10N2030/12C10N2040/14
Inventor 张玉成
Owner 合肥轻风飏电气科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com