Water-based environmental-friendly welded anti-flash liquid and preparation method thereof

An environmentally friendly, anti-splash technology, used in anti-corrosion coatings, fire-resistant coatings, anti-fouling/underwater coatings, etc. Bacterial ability, good water solubility

Inactive Publication Date: 2017-10-24
山东天力润滑油有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the above problems and overcome the deficiencies of the prior art, the present invention provides a water-based environment-friendly welding anti-splash liquid with good water solubility, excellent thermal stability and environmental friendliness, which can effectively solve the problem of welding anti-splash liquid stability Cracking and stripping due to insufficient water solubility, resulting in residual coating after washing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Hydroxypropyl methylcellulose: 3%, polyvinyl alcohol: 5%, polyethylene glycol: 2%, disodium hydrogen phosphate: 3%, sodium benzoate: 0.5%, sodium silicate: 0.4%, calcium sulfate: 0.1%, borax: 1.0%, ethanol: 10.0%, the rest is deionized water;

Embodiment 2

[0020] Hydroxypropyl methylcellulose: 9%, polyvinyl alcohol: 15%, polyethylene glycol: 6%, disodium hydrogen phosphate: 6.5%, sodium benzoate: 1.25%, sodium silicate: 1.0%, calcium sulfate: 0.25%, borax: 2.0%, ethanol: 20.0%, the rest is deionized water;

Embodiment 3

[0022] Hydroxypropyl methylcellulose: 6%, polyvinyl alcohol: 10%, polyethylene glycol: 4%, disodium hydrogen phosphate: 4.75%, sodium benzoate: 0.9%, sodium silicate: 0.7%, calcium sulfate: 0.2%, borax: 1.5%, ethanol: 15.0%, the rest is deionized water;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses water-based environmental-friendly welded anti-flash liquid and belongs to the technical field of metal welding. The water-based environmental-friendly welded anti-flash liquid is characterized by comprising the following components in percentage by weight: 10.0-30.0% of a high-polymer film-forming agent, 3.0-6.5% of a flame retardant, 1.0-2.5% of a sustained-release formulation, 1.0-2.0% of a pH buffer agent, 10.0-20.0% of ethanol and the balance of water, wherein the high-polymer film-forming agent comprises hydroxypropyl methyl cellulose, polyvinyl alcohol and polyethylene glycol according to a weight ratio of 3:5:2; the flame retardant is sodium hydrogen phosphate; the corrosion inhibitors refer to sodium benzoate, sodium silicate and calcium sulfate according to a weight ratio of 5:4:1; and the pH buffer agent is borax. The water-based environmental-friendly welded anti-flash liquid disclosed by the invention has the beneficial effects that the anti-flash liquid has excellent thermal stability, water solubility, corrosion inhibition property and simplicity in cleaning; and the formulas belong to bio-based green resources and have excellent environment friendliness.

Description

Technical field [0001] The invention belongs to the technical field of metal welding anti-splash additives, and more specifically relates to a water-based environment-friendly welding anti-splash liquid and a preparation method thereof. Background technique [0002] Welding process is an indispensable universal processing technology in all walks of life. As long as there is a need for metal connection, most of the welding process needs to be completed. Welding is to heat two base materials that need to be connected together through a welding rod and heat them locally at a high temperature, so that the two base materials are firmly connected by solder. It is a very common phenomenon that "welding" appears during high-temperature heating. The "welding" splashes around and falls on the base material. Because the temperature of the "welding" is extremely high, it will be The materials are firmly connected together, and after cooling, a solder ball is formed. There are sometimes man...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/04C09D101/28C09D171/02C09D5/08C09D5/14C09D5/18C09D7/12
CPCC09D129/04C08K2003/387C08L2201/02C08L2201/08C08L2205/03C09D5/08C09D5/14C09D5/18C08L1/284C08L71/02C08K13/02C08K5/098C08K3/34C08K3/38
Inventor 王瑞战
Owner 山东天力润滑油有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap