A kind of preparation method of transparent flexible supercapacitor

A super capacitor and transparent technology, applied in the manufacture of hybrid/electric double layer capacitors, etc., can solve the problems of high brittleness and low energy density of transparent substrate materials, and achieve high power output performance, good flexibility, and high dressing density. Effect

Active Publication Date: 2019-01-08
HEBEI UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of high brittleness and low energy density of the transparent base material used in the transparent flexible supercapacitor existing in the current technology, and proposes a metal nanomesh transparent electrode prepared by spin coating as a current collector, and through deposition Carbon-containing materials such as graphene can be deposited on the PET pole piece with controllable light transmittance and uniformity, and finally a transparent flexible electrode is prepared.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of transparent flexible supercapacitor
  • A kind of preparation method of transparent flexible supercapacitor
  • A kind of preparation method of transparent flexible supercapacitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Spin-coat 0.5mg / ml nano-silver wire solution (10ml) on the surface of a layer of 10cm x 10cm PET substrate with a homogenizer. Heating for 5 minutes under the same conditions, a transparent and flexible current collector whose surface is covered with a network of metal nanowires is prepared, and the thickness of the coating is 100 nm.

[0035] (2) in the graphene of getting 25mg and 40ml mixed solution, (the composition of mixed solution is the concentrated sulfuric acid and the concentrated nitric acid, and the volume ratio is the concentrated sulfuric acid: concentrated nitric acid 3:1; The concentration of the concentrated sulfuric acid is mass fraction 98%, concentrated nitric acid The concentration is 65% of the mass fraction) and mixed, stirred at 70°C for 4h, then the mixed solution was suction filtered, and the solution after suction filtration was subjected to dialysis (that is, the above mixed liquid was poured into a dialysis bag, and then the dialysis bag...

Embodiment 2

[0041] (1) Spin-coat 0.5mg / ml nano-silver wire solution (10ml) on the surface of a layer of 10cm x 10cm PET substrate with a homogenizer. Heating for 5 minutes under the same conditions, a transparent and flexible current collector whose surface is covered with a network of metal nanowires is prepared, and the thickness of the coating is 100 nm.

[0042] (2) in the graphene of getting 25mg and 40ml mixed solution, (the composition of mixed solution is the concentrated sulfuric acid and the concentrated nitric acid, and the volume ratio is the concentrated sulfuric acid: concentrated nitric acid 3:1; The concentration of the concentrated sulfuric acid is mass fraction 98%, concentrated nitric acid The concentration is 65% of the mass fraction) and mixed, stirred at 70°C for 4h, then the mixed solution was suction filtered, and the solution after suction filtration was subjected to dialysis (that is, the above mixed liquid was poured into a dialysis bag, and then the dialysis bag...

Embodiment 3

[0047] (1) Spin-coat 0.5mg / ml nano-silver wire solution (10ml) on the surface of a layer of 10cmx10cm PET substrate with a homogenizer. After heating for 5 minutes, a transparent and flexible current collector whose surface is covered with a network of metal nanowires is prepared, and the thickness of the coating is 100 nm.

[0048] (2) in the graphene of getting 25mg and 40ml mixed solution, (the composition of mixed solution is the concentrated sulfuric acid and the concentrated nitric acid, and the volume ratio is the concentrated sulfuric acid: concentrated nitric acid 3:1; The concentration of the concentrated sulfuric acid is mass fraction 98%, concentrated nitric acid The concentration is 65% of the mass fraction) and mixed, stirred at 70°C for 4h, then the mixed solution was suction filtered, and the solution after suction filtration was subjected to dialysis (that is, the above mixed liquid was poured into a dialysis bag, and then the dialysis bag was immersed in deion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a transparent flexible supercapacitor. According to the method, with a metal nanowire solution as a raw material, preparation is carried out on the surface of a transparent flexible substrate material by a spin-coating method to obtain a transparent flexible collector with the surface covered with a metal nano wire network; on the basis of a deposition method, carbon-included materials like graphene are deposited on PET polar pieces in a light transmittance and uniformity controllable manner; and then the two polar pieces are rolled to obtain a double-electricity-layer transparent flexible super capacitor with a sandwich structure. The technical route is simple; the obtained active material has an open three-dimensional (multi-stage) structure; the internal resistance of the supercapacitor system is reduced; the high light transmittance is kept; and the energy and power density are optimized.

Description

technical field [0001] The invention relates to a method for preparing a transparent flexible supercapacitor, specifically belonging to the field of supercapacitors. Background technique [0002] "Transparent and flexible" is a promising direction of change for the development of future consumer electronics products, which can meet people's more requirements for multi-functionality and aesthetic appearance of electronic products. As an indispensable and important component, transparent and flexible electronic devices have potential commercial impact and huge market value, and have become one of the research hotspots in the fields of materials, electronics, and communication. However, due to the stages and limitations of technology development, it is still a great challenge to assemble a fully transparent and flexible electronic product. For example, the next generation of transparent and flexible smartphones, highly integrated smart glasses, etc., put forward high requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/84
CPCY02E60/13
Inventor 王恭凯钟禹翔张昕彭会芬
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com