Interior decoration coating for removing formaldehyde, and preparation method thereof

An interior decoration and formaldehyde technology, applied in the field of coatings, can solve the problems of poor water resistance, moisture absorption and stickiness of coatings, and achieve the effects of good scratch resistance, good physical isolation and waterproof, and good scratch resistance.

Inactive Publication Date: 2017-09-15
合肥市一片叶装饰工程有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the good hydrophilicity of the base material in water-based coatings, the coatings have poor water resistance. The coatings painted with such materials are often accompanied by moisture absorption and stickiness in the natural environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An indoor decorative paint for removing formaldehyde and a preparation method according to a preferred embodiment of the present invention;

[0030] The indoor decorative paint for removing formaldehyde is prepared from the following raw materials in parts by weight:

[0031] 35 parts of water-based polyurethane, 16 parts of water-based epoxy resin, 1.1 parts of graphene oxide, 15 parts of nano-silica, 12 parts of aluminum oxide, 13 parts of diatomaceous earth, 9 parts of activated carbon, 1.6 parts of oxidized formaldehyde catalyst, stabilizer 4 parts, 5 parts defoamer.

[0032] The oxidation formaldehyde catalyst is a titanium dioxide supported precious metal catalyst Pt / TiO 2 .

[0033] The loading amount of noble metal in the oxidation formaldehyde catalyst is 0.1% to 1.5%.

[0034] The stabilizer is a diethylene glycol solution of potassium 2-ethylhexanoate, wherein the mass concentration of potassium 2-ethylhexanoate is 15%.

[0035] The defoamer is dimethyl silicone oil.

...

Embodiment 2

[0045] An indoor decorative paint for removing formaldehyde and a preparation method according to a preferred embodiment of the present invention;

[0046] The indoor decorative paint for removing formaldehyde is prepared from the following raw materials in parts by weight:

[0047] 30 parts of water-based polyurethane, 12 parts of water-based epoxy resin, 0.2 parts of graphene oxide, 8 parts of nano-silica, 6 parts of aluminum oxide, 10 parts of diatomaceous earth, 5 parts of activated carbon, 0.5 parts of oxidized formaldehyde catalyst, stabilizer 2 parts, 3 parts defoamer.

[0048] The oxidation formaldehyde catalyst is a titanium dioxide supported precious metal catalyst Pd / TiO 2 .

[0049] The loading amount of noble metal in the oxidation formaldehyde catalyst is 0.1% to 1.5%.

[0050] The stabilizer is a diethylene glycol solution of potassium 2-ethylhexanoate, wherein the mass concentration of potassium 2-ethylhexanoate is 15%.

[0051] The defoamer is a polyether-siloxane copol...

Embodiment 3

[0061] An indoor decorative paint for removing formaldehyde and a preparation method according to a preferred embodiment of the present invention;

[0062] The indoor decorative paint for removing formaldehyde is prepared from the following raw materials in parts by weight:

[0063] 45 parts of water-based polyurethane, 18 parts of water-based epoxy resin, 1.5 parts of graphene oxide, 17 parts of nano-silica, 15 parts of aluminum oxide, 16 parts of diatomaceous earth, 12 parts of activated carbon, 2.2 parts of oxidized formaldehyde catalyst, stabilizer 6 parts, 8 parts defoamer.

[0064] The oxidizing formaldehyde catalyst is a titanium dioxide supported precious metal catalyst Au / TiO 2 .

[0065] The loading amount of noble metal in the oxidation formaldehyde catalyst is 0.1% to 1.5%.

[0066] The stabilizer is a diethylene glycol solution of potassium 2-ethylhexanoate, wherein the mass concentration of potassium 2-ethylhexanoate is 15%.

[0067] The defoamer is a polysiloxane defoamer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an interior decoration coating for removing formaldehyde, and a preparation method thereof. The coating comprises aqueous polyurethane, aqueous epoxy resin, graphene oxide, nano-silica, alumina, diatomite, active carbon, a formaldehyde oxidation catalyst, a stabilizer and an antifoaming agent. The preparation method comprises the following steps: carrying out a modifying reaction on the aqueous polyurethane, aqueous epoxy resin and graphene oxide; adding the diatomite, active carbon and the antifoaming agent, uniformly mixing and stirring above substances, adding the nano-silica and alumina, and carrying out shear dispersing for 10-20 min; and adding the formaldehyde oxidation catalyst and the stabilizer, and carrying out ultrasonic dispersing for 10-20 min to obtain the decoration coating. The coating has the advantages of good coating effect, excellent waterproof property, excellent scratch resistance and good formaldehyde removal performance, can be applied to interior decoration to provide a clean and safe living environment for people, and has good application values.

Description

Technical field [0001] The invention relates to the technical field of coatings, in particular to an indoor decorative coating for removing formaldehyde and a preparation method. Background technique [0002] With the improvement of living standards, indoor air pollution is gradually attracting people's attention. Studies have shown that volatile harmful gases such as formaldehyde, benzene, and toluene released by interior decoration and decoration materials are the main causes of air pollution. In order to meet the needs of the products for coagulation or hiding power or to enhance the hardness of the existing interior wall coatings, rubber, latex powder, varnish and other substances are often added to their raw materials, and these substances are the ones that produce harmful gases such as formaldehyde and benzene. Source of pollution. [0003] In the construction of interior wall paint, it is generally necessary to apply the base putty powder before applying the top paint. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D163/00C09D7/12
CPCC09D175/04C08K2003/2227C08K2003/2241C08K2201/011C08L2205/03C08L63/00C08L83/04C08K13/06C08K9/12C08K7/00C08K3/04C08K3/36C08K3/22C08K7/26C08K7/24
Inventor 郭建
Owner 合肥市一片叶装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com