A kind of cuprous oxide powder and preparation method thereof

A technology of cuprous oxide and powder, which is applied in the field of metal powder, can solve the problem of few cuprous oxide powders, and achieve the effect of efficient, convenient, fast, competitive and saving production steps

Active Publication Date: 2019-05-28
苏州昆腾威新材料科技有限公司
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many methods for preparing cuprous oxide, but it is rare to obtain cuprous oxide powder with uniform particle size and stable performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cuprous oxide powder and preparation method thereof
  • A kind of cuprous oxide powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] One aspect of the embodiments of the present invention provides a method for preparing cuprous oxide powder, which includes:

[0023] The pure copper is smelted to the molten state, and the molten copper is directly atomized in a mixed atmosphere of oxygen and nitrogen, so that the copper and oxygen undergo an oxidation reaction to obtain cuprous oxide powder.

[0024] As one of the preferred solutions, the volume ratio of oxygen and nitrogen in the mixed atmosphere of oxygen and nitrogen is 45:55˜50:50, especially preferably 50:50. If the proportion of nitrogen in the mixed gas is too low during the production process, a part of the cuprous oxide powder will continue to react with excess oxygen to form copper oxide powder, resulting in the impurity of the obtained cuprous oxide powder. If the proportion of nitrogen in the mixed gas is too high during the production process, some copper water cannot react with oxygen, and there will be a part of copper powder in the gen...

Embodiment 1

[0043] The method for preparing cuprous oxide powder of the present embodiment comprises the following steps:

[0044] A. Put the pure copper raw material into the gas atomization powder making equipment, first heat the pure copper to keep it warm, and then melt it to a molten state at 1100 ° C. The atomization powder making equipment can be obtained through commercial channels, etc., and will not be done here Too much detail.

[0045] B. Atomize the pure copper material in the molten state, introduce a mixed gas of oxygen and nitrogen, the volume ratio of oxygen and nitrogen is 45:55, and the gas pressure is 1MPa, and the cuprous oxide powder is obtained. The scanning electron microscope picture can be found in figure 2 , and its particle size is 35-45 microns.

Embodiment 2

[0047] The method for preparing cuprous oxide powder of the present embodiment comprises the following steps:

[0048] A. Put the pure copper raw material into the gas atomization powder making equipment, first heat the pure copper to keep it warm, and then smelt it to a molten state at 1200°C. The atomization powder making equipment can be obtained from the market, etc., and will not be done here Too much detail.

[0049] B. Atomize the pure copper material in the molten state, feed a mixed gas of oxygen and nitrogen, the volume ratio of oxygen and nitrogen is 48:52, and the gas pressure is 1.5MPa, and the cuprous oxide powder is obtained, and its scanning electron microscope picture can be refer to figure 2 , and its particle size is 20-30 microns.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses cuprous oxide powder and a preparation method thereof. The preparation method of the cuprous oxide powder is as follows: smelting pure copper to a molten state, directly atomizing the copper in the molten state in a nitrogen and oxygen mixed atmosphere for oxidation reaction of the copper and oxygen to obtain the cuprous oxide powder. During production of the cuprous oxide powder by the atomization method, the nitrogen and oxygen mixed atmosphere is introduced for high-temperature oxidation of the pure copper and the oxygen in the atomization process to prepare the cuprous oxide powder, meanwhile because of lack of oxygen, cuprous oxide cannot continue to react with the oxygen to form copper oxide. The preparation steps of the method are efficient, fast and convenient, production steps are saved, the production method of the cuprous oxide powder is broadened; and the cuprous oxide powder prepared by the preparation method has relatively concentrated and uniform particle size distribution and excellent physical properties, and is easy to use later.

Description

technical field [0001] The invention relates to a preparation method of cuprous oxide powder, in particular to a cuprous oxide powder and a preparation method thereof, belonging to the technical field of metal powder. Background technique [0002] The gas atomization method is a method of directly crushing liquid metal or alloy to obtain powder. It is widely used and its production scale is second only to the reduction method. It can produce metal powders such as lead, tin, aluminum, zinc, copper, iron, nickel, etc. , can also produce pre-alloyed powder. [0003] Cuprous oxide is an important inorganic chemical raw material, which is widely used in the fields of coatings, glass, ceramics, plastics, agriculture and industrial catalysis. In my country, the amount of cuprous oxide is increasing year by year, and the research on cuprous oxide is relatively active in recent years. At present, there are many methods for preparing cuprous oxide, but it is rare to obtain cuprous o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G3/02
CPCC01G3/02C01P2004/03C01P2004/61
Inventor 盛洪超邓斌阮海琼
Owner 苏州昆腾威新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com